High-wear-resistance steel plate and production method thereof

A technology with high wear resistance and production method, applied in the field of metal materials, can solve the problems of complex alloy, high cost, complex heat treatment process, etc., and achieve the effect of low alloy content, uniform cross-sectional hardness and good wear resistance

Inactive Publication Date: 2019-03-12
ANGANG STEEL CO LTD
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0014] 1. The alloy is complex and the cost is high;
[0015] 2. The heat treatment process is complicated, and offline or online quenching and tempering are required;
[0016] 3. Only thickness below 30 mm can be produced;

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-wear-resistance steel plate and production method thereof
  • High-wear-resistance steel plate and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0040] Below by embodiment the present invention will be further described.

[0041] In the embodiment of the present invention, according to the component ratio of the technical solution, smelting—continuous casting—heating and slow cooling—slab heating—controlled rolling—straightening is carried out.

[0042] (1) Smelting: Pretreatment of molten iron—converter smelting—refining—vacuum degassing, using converter smelting, refining treatment through top blowing or top-bottom composite blowing, and microalloying, strictly controlling molten steel [N]≤ 0.0040%, [O]≤0.0020%, [H]≤0.00015%, continuous casting adopts electromagnetic stirring or light pressing;

[0043] (2) Heating and slow cooling: After continuous casting, the slab needs to be heated and cooled slowly. The slow cooling time at 400-600°C is greater than or equal to 48 hours. When the slab temperature is 100-200°C, the slab should be cleaned with temperature. ;

[0044] (3) Slab heating: the heating temperature of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a high-wear-resistance steel plate and a production method of the high-wear-resistance steel plate. The high-wear-resistance steel plate comprises, by weight, 0.30%-0.35% of C,1.0%-1.5% of Si, 3.5%-5.0% of Mn, 0.02%-0.04% of Nb, 0.10%-0.20% of Ti, not larger than 0.012% of P, not larger than 0.003% of S, not larger than 0.0040% of [N], not larger than 0.00015% of [H], not larger than 0.0020% of [O] and the balance Fe and inevitable impurities. The production method of the high-wear-resistance steel plate comprises the steps of smelting, continuous casting, heating and slow cooling, plate blank heating, controlled rolling and straightening. According to the high-wear-resistance steel plate, chemical components are simple, the alloy content is relatively low, the surface hardness of the steel plate is larger than 500 HB, the wear resistance is good, the section hardness is uniform, the maximum thickness can reach 50 mm, and the high-wear-resistance steel plate canmeet the use demand for thick wear-proof steel plates and does not need heat treatment.

Description

technical field [0001] The invention belongs to the field of metal materials, and in particular relates to a HB500 grade high wear resistance steel plate and a production method thereof. Background technique [0002] High-strength wear-resistant steel plates are widely used in vehicles, ships, mining equipment, engineering machinery and cement equipment. As classic wear-resistant steels, high-carbon and high-manganese series wear-resistant steels have been widely used for more than a hundred years. In the past two decades, in order to meet the needs of the development of mining and transportation machinery and construction machinery, low- and medium-alloy wear-resistant steels have been obtained due to their good wear resistance and toughness, simple production process, and reasonable comprehensive economy. rapid development and application. [0003] Brinell hardness HB500 grade is a kind of low-alloy wear-resistant steel, which has high surface hardness and wear resistance...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22C38/02C22C38/04C22C38/12C22C38/14C21D8/02
CPCC21D8/0226C22C38/02C22C38/04C22C38/12C22C38/14
Inventor 张涛纪汶伯林田子侯华兴张哲杨颖
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap