Heat absorbent for solar water heaters and production method

A technology for a solar water heater and a production method, which is applied to the field of heat absorbing materials for solar water heaters, can solve the problems of unsatisfactory solar heat absorption effect, low heat absorption rate, and influence on popularization and application of solar water heaters, and achieves heat absorption effect. Ideal, high heat absorption rate, and the effect of improving the service life

Inactive Publication Date: 2019-03-22
SICHUAN JINMING NEW ENERGY TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the heat-absorbing materials of solar water heaters use dull paint, etc. Although these materials are low in cost and easy to operate, their heat-absorb

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0012] Embodiment 1, the solar water heater heat sink is prepared according to the following composition and weight ratio:

[0013] Carbon powder 25, zinc powder 5, titanium dioxide 20, aluminum silicate 12, calcium chloride 12, polyvinyl alcohol 7, calcium carbonate 10, sodium silicate 9.

[0014] After the materials are prepared and mixed according to the weight of each component, 8% of the prepared materials and 92% of water are diluted and stirred evenly to prepare a solar water heater heat absorbing agent.

Example Embodiment

[0015] Embodiment 2, the solar water heater heat sink is prepared according to the following composition and weight ratio:

[0016] Carbon powder 20, zinc powder 8, titanium dioxide 25, aluminum silicate 10, calcium chloride 10, polyvinyl alcohol 8, calcium carbonate 9, sodium silicate 10.

[0017] After the materials are prepared and mixed according to the weight of each component, 5% of the prepared materials and 95% of water are diluted and stirred evenly to prepare a solar water heater heat absorbing agent.

Example Embodiment

[0018] Embodiment 3, the solar water heater heat sink is prepared according to the following composition and weight ratio:

[0019] Carbon powder 30, zinc powder 4, titanium dioxide 18, aluminum silicate 15, calcium chloride 14, polyvinyl alcohol 5, calcium carbonate 7, sodium silicate 7.

[0020] The production method of the solar water heater absorber of the present invention is as follows: after preparing and mixing the materials according to the weight of each component, dilute and stir evenly according to 10% of the prepared material and 90% water to prepare the solar water heater absorber.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a heat absorbent for solar water heaters and a production method. The heat absorbent for the solar water heaters is prepared from the following raw material components according to a weight ratio: 20 to 30 of carbon powder, 2 to 8 of zinc powder, 15 to 25 of titanium dioxide, 10 to 15 of aluminium silicate, 7 to 14 of calcium chloride, 3 to 8 of polyvinyl alcohol, 5 to 10 of calcium carbonate and 5 to 10 of sodium silicate. After the materials are mixed according to the weight of each component, 5 to 10 of materials and 90 to 95 of water are uniformly stirred for dilution, so that the heat-absorbing material for the solar water heaters is produced. According to the invention, the heat absorption rate is high, and the heat absorption effect for sunlight is ideal. Theheat absorbent for the solar water heaters is durable, having a long service life which is prolonged by 30 percent or more. The application range is wide, and the invention is easy to popularize.

Description

technical field [0001] The invention relates to a heat-absorbing material, in particular to a heat-absorbing material for a solar water heater. Background technique [0002] At present, the heat-absorbing materials of solar water heaters use dull paint, etc. Although these materials are low in cost and easy to operate, their heat absorption effect on sunlight is not very ideal, and the heat absorption rate is not very high, which directly affects the performance of solar water heaters. Promote apps. Contents of the invention [0003] The purpose of the invention is to overcome the deficiencies of the prior art and provide a solar water heater heat absorbing agent with high heat absorption rate and long service life. [0004] The present invention is formulated from the following raw material components and weight ratios: carbon powder 20-30, zinc powder 2-8, titanium dioxide 15-25, aluminum silicate 10-15, calcium chloride 7-14, polyvinyl alcohol 3-8, calcium carbonate 5...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D129/04C09D5/32
CPCC09D129/04C08K3/04C08K3/34C08K2003/0893C08K2003/162C08K2003/2241C08K2003/265C08K2201/014C09D5/32
Inventor 魏铨举魏志明
Owner SICHUAN JINMING NEW ENERGY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap