Polymer wear-resistant PP composite material for eyeliner tube and preparation method thereof

A composite material and eyeliner technology, applied in the field of polymer composite materials, can solve the problems of poor wear resistance of eyeliner tube, loss of surface of eyeliner tube, and unsmooth luster.

Pending Publication Date: 2019-03-29
邵成杰
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the deficiencies of the prior art, the present invention provides a polymer wear-resistant PP composite material for eyeliner tubes and a preparation method thereof, which solves the problem that the existing eyeliner tubes have poor wear resistance and often appear eyeliner after long-term use. The surface of the tube is

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] S1. First weigh 70 parts of polypropylene powder, 6.5 parts of silicone rubber, 0.7 parts of tungsten carbide powder, 2 parts of nano-toughened aluminum oxide, 7 parts of sepiolite fiber and 2 parts of lubricating oil according to the weight ratio of the corresponding ingredients. Agent raw materials, then 70 parts of polypropylene powder, 6.5 parts of silicone rubber, 0.7 parts of tungsten carbide powder, 2 parts of nano-toughened aluminum oxide, 7 parts of sepiolite fiber and 2 parts of lubricant raw materials were added to the high-speed In the mixing mixer, stir at a high speed of 900r / min for 1.5h, so that the various raw material components are fully mixed, and the composite material mixture can be obtained;

[0024] S2, then add 0.7 parts of aluminum-based adhesives and 7 parts of compatibilizing and toughening agents to the composite material mixture obtained in S1 in sequence, and stir the high-speed mixing mixer at a speed of 700r / min for 40min to make the comp...

Embodiment 2

[0029]S1. First, weigh 85 parts of polypropylene powder, 5 parts of silicone rubber, 0.5 part of tungsten carbide powder, 1 part of nano-toughened aluminum oxide, 5.9 parts of sepiolite fiber and 1 part of lubricating oil according to the weight ratio of the corresponding ingredients. Then add 85 parts of polypropylene powder, 5 parts of silicone rubber, 0.5 part of tungsten carbide powder, 1 part of nano-toughened aluminum oxide, 5.9 parts of sepiolite fiber and 1 part of lubricant raw material to the high-speed In the mixing mixer, stir at a high speed of 800r / min for 1 hour, so that the various raw material components are fully mixed, and the composite material mixture can be obtained;

[0030] S2. After that, add 0.5 parts of aluminum-based adhesive and 5 parts of compatibilizing and toughening agent into the composite material mixture obtained in S1 in sequence, and stir the high-speed mixing mixer at a speed of 600r / min for 30min to make the composite material mixture Th...

Embodiment 3

[0035] S1. First, weigh 65 parts of polypropylene powder, 8 parts of silicone rubber, 1 part of tungsten carbide powder, 3 parts of nano-toughened aluminum oxide, 10 parts of sepiolite fiber and 3 parts of lubricating oil according to the weight ratio of the corresponding ingredients. agent raw materials, and then 65 parts of polypropylene powder, 8 parts of silicone rubber, 1 part of tungsten carbide powder, 3 parts of nano-toughened aluminum oxide, 10 parts of sepiolite fiber and 3 parts of lubricant raw materials were added to the high-speed In the mixing mixer, stir at a high speed of 1000r / min for 2 hours, so that the various raw material components are fully mixed, and the composite material mixture can be obtained;

[0036] S2, then add 0.8 parts of aluminum-based adhesive and 10 parts of compatibilizing and toughening agent to the composite material mixture obtained in S1 in sequence, and stir the high-speed mixing mixer at a speed of 800r / min for 50min to make the comp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a polymer wear-resistant PP composite material for an eyeliner tube. The polymer wear-resistant PP composite material comprises the following raw materials by weight: 65 to 85parts of polypropylene powder, 5 to 8 parts of silicone rubber, 0.5 to 1 part of tungsten carbide powder, 1 to 3 parts of nanometer toughened aluminum oxide, 0.5 to 0.8 part of an aluminum-based adhesive, 5 to 10 parts of sepiolite fiber, 5 to 10 parts of a compatibilizing and toughening agent, 1 to 3 parts of a lubricant and 0.1 to 0.7 part of an antioxidant. The invention relates to the technical field of polymer composite materials. The polymer wear-resistant PP composite material for the eyeliner tube and the preparation method thereof have the following advantages: improvement of the manufacturing materials of the eyeliner tube can be realized to increase the wear-resisting effect of the eyeliner tube; the wear resistance of the eyeliner tube can be greatly improved; the frequent situations of surface abrasion and edge peeling of the eyeliner tube after long-term use are avoided from occurrence; the glossiness and smoothness of the surface of the eyeliner tube are guaranteed; theinfluence on the appearance of the eyeliner tube is prevented; the purpose of prolonging the service life of the eyeliner tube is well achieved; and normal use of the eyeliner tube for people is guaranteed.

Description

technical field [0001] The invention relates to the technical field of polymer composite materials, in particular to a polymer wear-resistant PP composite material used for eyeliner tubes and a preparation method thereof. Background technique [0002] Eyeliner is a kind of makeup product, which is used to deepen and highlight the makeup effect of the eyes, making the eyes look big and energetic, similar to a pencil in shape, you can use a special pencil sharpener or a knife to remove the excess wood, and you can also improve There are two types of eyeliners: pencil type and automatic pencil type according to the thickness of the pen tip. They are used around the eyes. The texture is very soft. Some eyeliners with a slightly harder texture have a long-lasting makeup effect. The color is deep and can be used to elongate The end of the eye is often used in theater and stage makeup. Most eyeliners have a powdery makeup texture. Because the ingredients and texture are similar to ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L23/12C08L83/04C08L33/20C08K13/04C08K3/22C08K7/10C08K3/14
CPCC08K2003/2227C08K2201/011C08L23/12C08L2205/03C08L2205/035C08L2205/06C08L2205/08C08L83/04C08L33/20C08K13/04C08K3/22C08K7/10C08K3/14
Inventor 赵林烽
Owner 邵成杰
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap