Anti-impact anti-aging electric cable protection pipe material and preparation method thereof

An anti-aging cable and protection tube technology, applied in the field of cable protection tube materials, can solve the problems of low service life of the cable protection tube, easy rupture and damage, easy corrosion or aging, etc., so as to improve the unstable flow phenomenon and heat resistance. The effect of excellent and excellent impact resistance

Active Publication Date: 2019-04-16
广东威立瑞科技有限公司
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the harsh application environment of cable protection tubes, ordinary plastic tubes have poor compressive resistance and are prone to rupture and damage due to large extrusion and collisions, and ordinary plastic tubes are easy to corrode or age in various environments with different pH values. Therefore, when ordinary plastic tubes are used as cable protection tubes, the service life of the cable protection tubes is low, and the plastic tubes are easily damaged, causing leakage or short circuit accidents of internal wire leakage or wire disconnection.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-impact anti-aging electric cable protection pipe material and preparation method thereof
  • Anti-impact anti-aging electric cable protection pipe material and preparation method thereof
  • Anti-impact anti-aging electric cable protection pipe material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] An anti-shock and anti-aging cable protection tube material, comprising the following raw materials in parts by weight:

[0044]

[0045] Wherein, the anti-aging additive is a mixture of modified kaolin and HALS770 hindered amine light stabilizer in a weight ratio of 8:1.

[0046] The impact modifier is a mixture of chlorinated polyethylene, polystyrene, nano-calcium carbonate and wood flour in a weight ratio of 2:1:5:1, and the particle size of the wood flour is 200 μm.

[0047] Wherein, the preparation method of modified kaolin is:

[0048] (1) dispersing the kaolin of 70 parts by weight in water to obtain a suspension;

[0049] (2) Add 7 parts by weight of acrylamide cationic monomer, 5 parts by weight of polybutyl acrylate modifier, 1 part by weight of surfactant and 0.2 part by weight of ammonium persulfate initiator into water and mix uniformly to obtain a mixed solution ;

[0050] (3) Mix the suspension prepared in step (1) with the mixed solution prepared ...

Embodiment 2

[0057] An anti-shock and anti-aging cable protection tube material, comprising the following raw materials in parts by weight:

[0058]

[0059] Among them, the anti-aging additive is a mixture of modified kaolin and UV-326 light stabilizer with a weight ratio of 9:1.5; the impact modifier is chlorinated polyethylene, polystyrene, nano calcium carbonate and wood powder. The weight ratio of the mixture is 2.5:1:6:2, and the particle size of wood flour is 300μm.

[0060] Wherein, the preparation method of modified kaolin is:

[0061] (1) dispersing the kaolin of 77.5 parts by weight in water to obtain a suspension;

[0062] (2) 8.5 parts by weight of cationic monomer, 6.5 parts by weight of modifying agent, 2 parts by weight of surfactant and 0.25 parts by weight of initiator are added into water and mixed uniformly to prepare a mixed solution;

[0063] (3) Mix the suspension prepared in step (1) with the mixed solution prepared in step (2) evenly, react at 100°C for 1.5h, ...

Embodiment 3

[0070] An anti-shock and anti-aging cable protection tube material, comprising the following raw materials in parts by weight:

[0071]

[0072]

[0073] The anti-aging additive is a mixture of modified kaolin and light stabilizer in a weight ratio of 10:2; the impact modifier is chlorinated polyethylene, polystyrene, nano calcium carbonate and wood powder in a weight ratio of 3:1 :7:3 mixture, the particle size of wood flour is 400μm.

[0074] Wherein, the light stabilizer is a mixture of GW944 hindered amine light stabilizer and UVP-327 benzotriazole light stabilizer in parts by weight of 1.5:3.

[0075] Wherein, the preparation method of modified kaolin is:

[0076] (1) dispersing the kaolin of 85 parts by weight in water to obtain a suspension;

[0077] (2) 10 parts by weight of cationic monomers, 8 parts by weight of modifiers, 3 parts by weight of surfactants and 0.3 parts by weight of initiators are added into water and mixed uniformly to obtain a mixed solution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
impact strengthaaaaaaaaaa
heat deflection temperatureaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of electric cable protection pipe materials, particularly to an anti-impact anti-aging electric cable protection pipe material and a preparation method thereof, wherein the anti-impact anti-aging electric cable protection pipe material comprises the following raw materials by weight: 60-70 parts of a PVC resin, 30-45 parts of an XLPE resin, 10-15 partsof an LDPE resin, 12-16 parts of a TPU resin, 25-30 parts of an anti-impact modifier, 10-16 parts of an anti-aging aid, and 10-15 parts of a compatibilizer, wherein the anti-aging aid is a mixture comprising modified kaolin and a light stabilizer according to a weight ratio of 8-10:1-2, and the anti-impact modifier is a mixture of chlorinated polyethylene, polystyrene, nanometer calcium carbonateand wood powder. According to the present invention, the anti-impact anti-aging electric cable protection pipe material has excellent impact resistance and excellent aging resistance, has an impact strength of 19.8-26.0 KJ / m<2>, is not easily deformed after being heated, and has a heat distortion temperature of 85-97.6 DEG C.

Description

technical field [0001] The invention relates to the technical field of cable protection tube materials, in particular to an impact-resistant and anti-aging cable protection tube material and a preparation method thereof. Background technique [0002] Cable protection tube is also known as power cable protection tube, cement cable protection tube, power row tube, power cable protection tube, etc. The cable protection tube is mainly installed at the intersection of communication cables and power lines to prevent short-circuit accidents caused by disconnection of power lines, which may cause communication cables and wire ropes to be charged. The cable protection tube is used to protect cables, switches, and core boards, so that the whole machine will not be burned out, and it also plays a certain role in isolating the interference of the power line magnetic field. [0003] Due to the development of the times, composite protection tubes made of cement or other metal or non-meta...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/06C08L97/02C08L23/28C08L25/06C08L75/06C08L23/06C08K13/06C08K3/26C08K3/34
CPCC08K2003/265C08K2201/011C08L27/06C08L2201/02C08L2201/08C08L2203/20C08L2205/035C08L2205/16C08L2207/066C08L97/02C08L23/286C08L25/06C08L75/06C08L23/06C08K13/06C08K3/26C08K3/346
Inventor 袁伟李伟严世勇黄恭雍
Owner 广东威立瑞科技有限公司