A kind of modified epoxy resin and its preparation method and cathodic electrophoretic coating with high throwing power

A technology of epoxy resin and epoxy resin emulsion, used in electrophoretic coatings, anti-corrosion coatings, polyurea/polyurethane coatings, etc. The effect of permeability performance and process stability

Active Publication Date: 2020-10-30
KEDE CHEM IND SHUNDE +1
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The cathodic electrophoretic coating containing the polyurethane modified epoxy resin has excellent weather resistance, and has improved the fullness of the paint film, but its throwing power (four-box method) is 50-53%, which still cannot meet the requirements well. Uniform coating capability on all surfaces of complex substrates

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of modified epoxy resin and its preparation method and cathodic electrophoretic coating with high throwing power
  • A kind of modified epoxy resin and its preparation method and cathodic electrophoretic coating with high throwing power
  • A kind of modified epoxy resin and its preparation method and cathodic electrophoretic coating with high throwing power

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～3

[0040] Embodiment 1~3, modified epoxy resin of the present invention and preparation thereof

[0041] The formulations of the modified epoxy resins of Examples 1 to 3 of the present invention are shown in Table 1 below.

[0042] The formula of table 1 embodiment 1~3 modified epoxy resin

[0043]

[0044]

[0045] The epoxy resin is a bisphenol A type epoxy resin with an epoxy equivalent of 184-190 g / eq and a viscosity of 12000-15000 cps / 25°C. The specific model is epoxy resin 128E, which is a commercially available product.

[0046] The preparation method of embodiment 1~3 modified epoxy resin is as follows:

[0047] A1. Preparation of intermediate ketimine A: Add triethylenetetramine and methyl isobutyl ketone in the formula amount to the reactor, react at 160-180°C for reflux for 12 hours, keep at 160-180°C, and 80 ± 10) kPa negative pressure under reflux dehydration 24h, made the intermediate ketimine A;

[0048] A2. Preparation of the intermediate ketimine B: add ...

Embodiment 4～6

[0055] Embodiments 4-6, cathodic electrophoretic coating with high throwing power of the present invention and its preparation

[0056] The formulations of cathodic electrophoretic coatings with high throwing power in Examples 4 to 6 of the present invention are shown in Table 2 below.

[0057] The formula of table 2 embodiment 4~6 cathodic electrophoretic coating with high throwing power

[0058]

[0059] The preparation method of embodiment 4~6 cathodic electrophoretic paint with high throwing power is as follows:

[0060] S1. Preparation of modified epoxy resin emulsion: add the modified epoxy resin in the amount of formula into the reactor, and add the aminosulfonic acid and deionized water in the amount of formula in the stirring state at a temperature of 50-60°C, and keep warm After 4 hours, add deionized water for emulsification, lower the temperature to 45°C to 50°C, and extract the solvent for 5 hours under a negative pressure of -(80±10)kPa to prepare a modified ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy equivalentaaaaaaaaaa
water resistanceaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of environment-friendly water-based coatings, and in particular relates to a modified epoxy resin, a preparation method thereof, and a cathodic electrophoretic coating with high throwing power containing the modified epoxy resin. The raw materials for preparing the modified epoxy resin of the present invention include epoxy resin, bisphenol, polyethylene glycol, N,N-dimethylbenzylamine, 4-methyl-2-pentanone, intermediate ketimine A, Intermediate ketimine B, intermediate C, alcohol ether solvent, propylene glycol methyl ether acetate and polyether amine, use the modified epoxy resin to prepare corresponding emulsion and color paste, and then make the emulsion and color paste according to Proportional mixing to prepare cathodic electrophoretic coatings. Compared with the existing cathodic electrophoretic coating, the cathodic electrophoretic coating of the present invention has significantly improved throwing power, and can well satisfy the surface electrophoretic coating of workpieces with complex surface structures, so that the surface of the coated workpiece, the depth of the recess, the gap and The shielded part obtains a uniform thickness of the coating film layer, thereby effectively improving the overall corrosion resistance of the workpiece, and has a wide range of applications.

Description

technical field [0001] The invention belongs to the technical field of environment-friendly water-based coatings, and in particular relates to a modified epoxy resin, a preparation method thereof, and a cathodic electrophoretic coating with high throwing power containing the modified epoxy resin. Background technique [0002] Cathodic electrophoretic coating has technical advantages such as excellent anti-corrosion performance, high automatic coating efficiency, and water-based environmental protection. It has been widely used in electrical appliances, building materials, automobiles and other industries. Throwing power refers to the ability of the paint to coat the inner surface, recesses and back of the object to be coated during electrophoretic painting, and also refers to the ability to coat a uniform paint film on all surfaces of the complex object to be coated. Threshing power performance is a key performance of electrophoretic coating performance. With excellent throw...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/04C09D5/44C09D5/08C09D7/61C09D7/63
CPCC08G18/58C08G18/584C08G18/724C08G18/758C08G18/7671C08G59/1477C08G59/62C09D5/08C09D5/4465C09D5/4492
Inventor 李文庄杨波高睿邓仲明
Owner KEDE CHEM IND SHUNDE
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com