Sulfuric acid dew point corrosion-resistant steel
A technology that resists sulfuric acid and corrodes steel, applied in furnaces, heat treatment equipment, manufacturing tools, etc., can solve the problems of easy segregation, reduced productivity, and increased cost, and achieves excellent resistance to sulfuric acid dew point corrosion, as well as manufacturability and fatigue resistance. excellent effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0138] Example
[0139] The steel (the balance being Fe and inevitable impurities) having the composition shown in Table 1 was smelted in a converter, and a billet with a thickness of 200 mm was produced by a continuous casting method. After cooling the steel slab, it was heated to 1200°C and hot rolled to produce a hot rolled steel sheet having a thickness of 4.5 mm.
[0140] It should be noted that in hot rolling, the reduction ratio is set to 97.75%, the finishing temperature of finishing rolling is set to 850°C, the coiling temperature is set to 560°C, and the average cooling from 800°C to 650°C The speed is set as shown in Table 2.
[0141] For the hot-rolled steel sheet thus obtained, the area ratio and Vickers hardness of each phase in the steel structure were measured by the method shown below, as well as sulfuric acid dew point corrosion resistance, manufacturability, bendability, and fatigue resistance. Evaluation. These results are shown in Table 2.
PUM
Property | Measurement | Unit |
---|---|---|
Fatigue strength | aaaaa | aaaaa |
Fatigue strength | aaaaa | aaaaa |
Fatigue strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap