High-wear-resistant cold-resistant rubber for snow removal vehicles

A high wear resistance, snow removal vehicle technology, applied in the field of rubber processing, can solve the problems of poor cold resistance, short service life, easy cracking and other problems of rubber, and achieve the effect of good corrosion resistance, long service life and avoid low temperature cracking

Inactive Publication Date: 2019-04-23
沈阳慧超科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing rubber has poor cold resistance, is easy to crack during use, affects the use effect, has poor corrosion resistance, short service life, and needs to be replaced frequently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] The technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the embodiments of the present invention. Apparently, the described embodiments are only some of the embodiments of the present invention, not all of them.

[0008] A high abrasion-resistant cold-resistant rubber used on a snow removal vehicle is made of the following raw materials in parts by weight:

[0009] 40-65 parts of polyurethane rubber, 1-2 parts of tris(2,4-di-tert-butyl base) phosphite, 1-4 parts of zinc diethyldithiocarbamate, 1-5 parts of aromatic oil, polyurethane rubber 20-60 parts, 6-10 parts of coumarone, 1-10 parts of pottery clay, 3-5 parts of zinc isooctanoate, 11-15 parts of aluminum phosphate, 2-12 parts of silicon carbide, 1-2 parts of thiol imidazoline , 1-5 parts of anti-aging agent, 4-12 parts of softener, 2-10 parts of sulfur.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-wear-resistant cold-resistant rubber for snow removal vehicles, wherein the high-wear-resistant cold-resistant rubber is prepared from the following raw materials by weight: 40-65 parts of a polyurethane rubber, 1-2 parts of tris(2,4-ditert-butylphenyl)phosphite, 1-4 parts of zinc diethyl dithiocarbamate, 1-5 parts of aromatic hydrocarbon oil, 20-60 parts of a polyurethane rubber, 6-10 parts of coumarone, 1-10 parts of clay, 3-5 parts of zinc octoate, 11-15 parts of aluminum phosphate, 2-12 parts of silicon carbide, 1-2 parts of thiol imidazoline, 1-5 parts of ananti-aging agent, 4-12 parts of a softening agent, and 2-10 parts of sulfur. According to the present invention, the produced high-wear-resistant cold-resistant rubber can provide cold resistance effect, can avoid the low-temperature cracking of rubber products, and further has advantages of good wear resistance and long service life.

Description

technical field [0001] The invention relates to the technical field of rubber processing, in particular to a high abrasion-resistant cold-resistant rubber used on snow removal vehicles. Background technique [0002] The existing rubber has poor cold resistance, is easy to crack during use, affects the use effect, has poor corrosion resistance, short service life, and needs to be replaced frequently. Contents of the invention [0003] The purpose of the present invention is to solve the shortcomings in the prior art, and propose a high wear resistance cold-resistant rubber used on snow removal vehicles. [0004] In order to achieve the above object, the present invention adopts the following technical solutions: [0005] A high abrasion-resistant cold-resistant rubber used on snow removal vehicles, made of the following raw materials in parts by weight: 40-65 parts of polyurethane rubber, 1- 2 parts, 1-4 parts of zinc diethyldithiocarbamate, 1-5 parts of aromatic oil, 20-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L75/04C08L91/00C08L45/02C08K13/02C08K5/526C08K3/34C08K5/098C08K3/32
CPCC08L75/04C08K2003/327C08L2205/025C08L2205/035C08L91/00C08L45/02C08K13/02C08K5/526C08K3/346C08K5/098C08K3/32C08K3/34
Inventor 潘洪吉
Owner 沈阳慧超科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com