Self-luminous water permeable brick and preparation method thereof

A technology of permeable bricks and self-illumination, applied in ceramic products, other household appliances, applications, etc., can solve the problems of reducing the permeable effect of permeable bricks, not being able to store energy, self-illumination, and slow water permeability, so as to achieve good use effects and bending resistance High strength and hardness, and the effect of improving water retention

Active Publication Date: 2019-04-26
林瑞云
View PDF8 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The luminescent permeable bricks prepared by this method are easy to block a large number of pores of the permeable bricks when applying cement and curing agent, reducing the permeable effect of the permeable bricks, and the water permeable speed is slow, and the passivated glass needs light source irradiation to refract or reflect light. , can not self-storage self-illumination, provide road signs for vehicles or pedestrians at night without light sources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-luminous water permeable brick and preparation method thereof
  • Self-luminous water permeable brick and preparation method thereof
  • Self-luminous water permeable brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] According to the above-mentioned preparation method of a self-luminous permeable brick, it is made according to the following steps:

[0034]Put 58 parts of nickel tailings fine aggregate (parts by weight, the same below), 7 parts of diatomite, 5 parts of bentonite, 11 parts of cement, 6 parts of nickel tailings powder and 13 parts of granite sawing mud with a particle size of 1.2 mm. Put it into a mixer and stir evenly to obtain a fine aggregate mixture, then add 27 parts of water to the fine aggregate mixture and stir evenly to obtain a fine aggregate mortar, and the granite sawing mud is powdery granite particles; the particle size is 3.8mm 62 parts of nickel tailings coarse aggregate, 7 parts of diatomite, 4 parts of bentonite, 9 parts of cement, 9 parts of nickel tailings powder and 11 parts of granite sawing mud are put into a mixer and stirred evenly to obtain a coarse aggregate mixture, and then Add 31 parts of water to the coarse aggregate mixture and stir to o...

Embodiment 2

[0036] Put 58 parts of nickel tailings fine aggregate with a particle size of 1.2 mm, 7 parts of diatomite, 5 parts of bentonite, 11 parts of cement, 6 parts of nickel tailings powder and 13 parts of granite sawing mud into a mixer and stir evenly to obtain Fine aggregate mixture, then add 27 parts of water to the fine aggregate mixture and stir evenly to obtain fine aggregate mortar; 62 parts of nickel tailings coarse aggregate with a particle size of 3.8mm, 7 parts of diatomite, 4 parts of bentonite, Put 9 parts of cement, 9 parts of nickel tailings powder and 11 parts of granite sawing mud into a mixer and stir evenly to obtain a coarse aggregate mixture, then add 31 parts of water to the coarse aggregate mixture and stir to obtain coarse aggregate mortar; Lay fine aggregate mortar, coarse aggregate mortar and fine aggregate mortar sequentially from bottom to top according to the thickness ratio of 1:3:1 to obtain a rough permeable brick with a lower permeable layer, a coars...

Embodiment 3

[0038] Put 58 parts of nickel tailings fine aggregate with a particle size of 1.2 mm, 7 parts of diatomite, 5 parts of bentonite, 11 parts of cement, 6 parts of nickel tailings powder and 13 parts of granite sawing mud into a mixer and stir evenly to obtain Fine aggregate mixture, then add 27 parts of water to the fine aggregate mixture and stir evenly to obtain fine aggregate mortar; 62 parts of nickel tailings coarse aggregate with a particle size of 3.8mm, 7 parts of diatomite, 4 parts of bentonite, Put 9 parts of cement, 9 parts of nickel tailings powder and 11 parts of granite sawing mud into a mixer and stir evenly to obtain a coarse aggregate mixture, then add 31 parts of water to the coarse aggregate mixture and stir to obtain coarse aggregate mortar; Lay fine aggregate mortar, coarse aggregate mortar and fine aggregate mortar sequentially from bottom to top according to the thickness ratio of 1:3:1 to obtain a rough permeable brick with a lower permeable layer, a coars...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a self-luminous water permeable brick and a preparation method thereof. The self-luminous water permeable brick comprises a water permeable brick base material and a luminous layer laid on the surface of the water permeable brick base material, wherein the luminous layer is prepared from the following raw materials in parts by weight: 35-60 parts of nickel tailing sand, 8-25 parts of quartz sand, 4-9 parts of diatomite, 6-15 parts of self-luminous materials, 7-22 parts of granite saw mud, 12-35 parts of a binding agent and 8-14 parts of a curing agent. Through repeatedtests, the invention provides the self-luminous water permeable brick; meanwhile, an existing preparation method of a water permeable brick is improved; nickel tailings with good abrasion resistance,high bending strength and high hardness are turned into wealth, the water permeable brick base material with high strength and good water permeability is prepared by fully utilizing the nickel tailings, and the light storing type self-luminous materials are laid on the surface of the water permeable brick base material, so that the self-luminous water permeable brick with light weight and high strength is prepared.

Description

technical field [0001] The invention belongs to the technical field of permeable bricks, in particular to a self-luminous permeable brick and a preparation method thereof. Background technique [0002] With the continuous development of cities, impermeable concrete floors are now laid on roads or squares in many cities, especially for cities with rainy weather in the south. When heavy rainfall occurs in a short period of time, the rainwater cannot be discharged in time. Prolonged rainstorms often lead to flooding on the roads and even urban floods. The deep rainwater makes it impossible for vehicles and pedestrians to pass normally in rainy days, causing traffic congestion or even paralysis. Some shops and buildings on the ground floor are in danger of flooding People bring a lot of economic loss. When traveling at night, many roads have no street lights or are in the blind spots of street lights. Without landmarks, it is easy to cause vehicles or pedestrians to go in the w...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B26/14C04B26/06C04B38/00E01C11/22C04B111/20C04B111/80
CPCC04B26/06C04B26/14C04B28/00C04B2111/00284C04B2111/00612C04B2111/2038C04B2111/807C04B2201/52E01C11/225C04B18/12C04B14/08C04B14/104C04B14/048C04B38/0041C04B14/06C04B14/36C04B2103/0068
Inventor 林瑞云
Owner 林瑞云
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap