Environment-friendly slowly-cured TPU hot melt glue film for insole and production method of environment-friendly slowly-cured TPU hot melt glue film

A technology of hot-melt adhesive film and production method, which is applied in the direction of adhesive, adhesive type, film/sheet without carrier, etc., can solve problems such as low lamination quality and glue hazards, so as to improve lamination quality and avoid Harmful, environmentally friendly effect

Inactive Publication Date: 2019-04-26
江苏和和新材料股份有限公司
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In the prior art, insoles are generally composed of an elastic bottom layer and a cloth surface layer. During production, the elastic bottom layer is first made, and then glue is applied on the surface of the elastic bottom layer to fit the cloth layer, and finally cut and trimmed. Finished products, this proces

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly slowly-cured TPU hot melt glue film for insole and production method of environment-friendly slowly-cured TPU hot melt glue film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] The hot melt adhesive film is prepared according to the following weight percentages and requirements of each component.

[0017] TPU particles: 60%, tackifying resin: 35%, functional additives: 5%. Among them, the hardness of TPU particles is 60-90A, the melting point is 50-100°C, and the melting index is 10-60g / 10min@150°C; the tackifying resin is C5 resin, and the softening point of the tackifying resin is 80-100°C, 160 The viscosity at ℃ is 1000-6000CPS; the functional auxiliary agent is antioxidant and ultraviolet absorber, and the weight percentage of antioxidant is 2%, and the weight percentage of ultraviolet absorber is 3%.

Embodiment 2

[0019] The hot melt adhesive film is prepared according to the following weight percentages and requirements of each component.

[0020] TPU particles: 70%, tackifying resin: 20%, functional additives: 7%. Among them, the hardness of TPU particles is 60-90A, the melting point is 50-100°C, and the melting index is 10-60g / 10min@150°C; the tackifying resin is C5 resin, and the softening point of the tackifying resin is 80-100°C, 160 The viscosity at ℃ is 1000-6000CPS; the functional auxiliary agent is an antioxidant and an ultraviolet absorber, and the weight percentage of the antioxidant is 3%, and the weight percentage of the ultraviolet absorber is 4%.

Embodiment 3

[0022] The hot melt adhesive film is prepared according to the following weight percentages and requirements of each component.

[0023] TPU particles: 80%, tackifying resin: 11%, functional additives: 9%. Among them, the hardness of TPU particles is 60-90A, the melting point is 50-100°C, and the melting index is 10-60g / 10min@150°C; the tackifying resin is C5 resin, and the softening point of the tackifying resin is 80-100°C, 160 The viscosity at ℃ is 1000-6000CPS; the functional auxiliary agent is an antioxidant and an ultraviolet absorber, and the weight percentage of the antioxidant is 4%, and the weight percentage of the ultraviolet absorber is 5%.

[0024] The production process of Example 1-3: first put the raw materials of each component into the extruder according to the weight percentage, and after extruding from the extruder, coat it on the release paper, and wind it up to make TPU hot melt film. Among them, the temperature settings of the extruder are as follows: ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Melt fingeraaaaaaaaaa
Viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to an environment-friendly slowly-cured TPU hot melt glue film for an insole and a production method of the environment-friendly slowly-cured TPU hot melt glue film, and belongsto the field of TPU new materials. The TPU hot melt glue film is prepared from the following components in percentage by weight: 50%-90% of TPU particles, 10%-40% of tackifying resin, and 4%-10% of afunctional additive, wherein the hardness of the TPU particles is 60-90 A, the melting point of the TPU particles is 50-100 DEG C, and the melt flow index of the TPU particles is 10-60 g/10min@150 DEGC; the tackifying resin is C5 resin or C9 resin, the softening point of the tackifying resin is 80-100 DEG C, and the viscosity of the tackifying resin at 160 DEG C is 1000-6000 CPS; the functional additive is an antioxidant and an ultraviolet absorber; and all the components of the TPU hot melt glue film are placed in an extruder proportionally, and extruded by the extruder and then release paper is coated with all the components , rolling-up is conducted, and thus the TPU hot melt glue film can be prepared. The environment-friendly slowly-cured TPU hot melt glue film for the insole adopts environment-friendly TPU materials and is environmentally friendly, harm of white glue and yellow glue to the body of workers is avoided, the curing speed is low while the cost is saved, and thus the attaching quality between all layers of the insole is improved.

Description

technical field [0001] The invention relates to the field of new TPU materials, in particular to an environment-friendly slow-curing TPU hot-melt adhesive film for insoles and a production method thereof. Background technique [0002] The name of TPU is thermoplastic polyurethane elastomer. It is mainly divided into polyester type and polyether type. It has a wide range of hardness, wear resistance, oil resistance, transparency and good elasticity. It is widely used in daily necessities, sporting goods, toys, decorative materials and other fields. TPU film has the characteristics of good toughness, high strength, odorless, non-toxic, and heat-sealing processing. [0003] In the prior art, insoles are generally composed of an elastic bottom layer and a cloth surface layer. During production, the elastic bottom layer is first made, and then glue is applied on the surface of the elastic bottom layer to fit the cloth layer, and finally cut and trimmed. Finished products, this p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J175/04C09J11/08C09J7/10
CPCC09J11/08C09J175/04C09J7/10C08L57/02
Inventor 叶书怀苟明明
Owner 江苏和和新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap