A kind of anti-seepage bonding material of expanded perlite external wall insulation board and preparation method thereof

A technology of external wall insulation board and expanded perlite, which is applied in the field of building insulation materials, can solve the problems of peeling off the surface of the insulation board, water seepage and water leakage of the insulation board, and achieve good anti-seepage, high structural strength, and excellent waterproof effects

Active Publication Date: 2021-07-30
谢思松
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, after the insulation board is exposed to wind, sun and rain, the salt ions in the water glass will be separated from the insulation board, and the surface of the insulation board will be severely peeled off and damaged, resulting in water seepage and leakage of the insulation board.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of anti-seepage bonding material of expanded perlite external wall insulation board and preparation method thereof
  • A kind of anti-seepage bonding material of expanded perlite external wall insulation board and preparation method thereof
  • A kind of anti-seepage bonding material of expanded perlite external wall insulation board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A preparation method of an anti-seepage water bonding material for expanded perlite external wall insulation boards, comprising the steps of:

[0042] (1) Weigh 75g of deionized water, 5g of silica gel binder, 5g of sodium methyl siliconate, and 1g of anti-seepage agent;

[0043] (2) Put the ingredients in step (1) into the disperser, adjust the speed to 180r / min, and stir for 30 minutes.

[0044] Wherein, the preparation method of silica gel adhesive comprises the steps:

[0045] (1) Ingredients: Weigh 70g of acrylic emulsion, 8g of nano-silica, 5g of pine wax resin and 1g of alkylphenoxyethylene ether;

[0046] (2) Put 70g of acrylic emulsion into the disperser, adjust the rotation speed to 800r / min, and stir evenly;

[0047] (3) Add 8g of nano-silica, 5g of pine wax resin and 1g of alkylphenol oxyethylene ether in sequence, and continue stirring for 15 minutes.

[0048] The preparation method of anti-seepage agent comprises the steps:

[0049] (1) Weigh 50g of ce...

Embodiment 2

[0055] A preparation method of an anti-seepage water bonding material for expanded perlite external wall insulation boards, comprising the steps of:

[0056] (1) Weigh 78g of deionized water, 8g of silica gel binder, 6g of sodium methyl siliconate, and 1g of anti-seepage agent;

[0057] (2) Put the ingredients in step (1) into the disperser, adjust the speed to 180r / min, and stir for 30 minutes.

[0058] Wherein, the preparation method of silica gel adhesive comprises the steps:

[0059] (1) Ingredients: Weigh 72g of acrylic emulsion, 9g of nano-silica, 8g of pine wax resin and 1g of alkylphenoxyethylene ether;

[0060] (2) Put 72g of acrylic emulsion into the disperser, adjust the rotation speed to 800r / min, and stir evenly;

[0061] (3) Add 9g of nano-silica, 8g of pine wax resin and 1g of alkylphenol oxyethylene ether in sequence, and continue stirring for 15 minutes.

[0062] The preparation method of anti-seepage agent comprises the steps:

[0063] (1) Weigh 53g of ce...

Embodiment 3

[0069] A preparation method of an anti-seepage water bonding material for expanded perlite external wall insulation boards, comprising the steps of:

[0070] (1) Weigh 80g of deionized water, 10g of silica gel binder, 8g of sodium methyl siliconate, and 2g of anti-seepage agent;

[0071] (2) Put the ingredients in step (1) into the disperser, adjust the speed to 180r / min, and stir for 30 minutes.

[0072] Wherein, the preparation method of silica gel adhesive comprises the steps:

[0073] (1) Ingredients: Weigh 75g of acrylic emulsion, 10g of nano-silica, 8g of pine wax resin and 2g of alkylphenoxyethylene ether;

[0074] (2) Put 75g of acrylic emulsion into the disperser, adjust the rotation speed to 800r / min, and stir evenly;

[0075] (3) Add 10g of nano-silica, 8g of pine wax resin and 2g of alkylphenol oxyethylene ether in sequence, and continue stirring for 15 minutes.

[0076] The preparation method of anti-seepage agent comprises the steps:

[0077] (1) Weigh 55g of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an anti-seepage bonding material for an expanded perlite external wall insulation board and a preparation method thereof. The key points of the technical scheme include the following components in parts by weight: 75-85 parts of deionized water, silica gel adhesive 5 to 15 parts, 5 to 10 parts of sodium methyl siliconate, 1 to 3 parts of anti-seepage agent, mix deionized water, silica gel binder, sodium methyl siliconate and anti-seepage agent together to form the anti-seepage agent of the present invention. Water-permeable bonding material with excellent waterproof, anti-seepage, anti-aging, anti-freezing and thawing and thermal insulation properties.

Description

technical field [0001] The invention relates to a building thermal insulation material, in particular to an anti-seepage bonding material for an expanded perlite external wall thermal insulation board and a preparation method thereof. Background technique [0002] Building energy conservation is an industry supported by the national industrial policy. At present, building energy-saving materials are mainly divided into inorganic thermal insulation lightweight aggregate and organic thermal insulation lightweight aggregate. However, due to the characteristics of the chemical properties of materials, no matter whether it is an inorganic system or an organic system, it is impossible to simultaneously meet the requirements of heat preservation, energy saving and fire safety. In terms of thermal insulation performance, organic materials are superior to inorganic materials; in terms of fire safety performance, inorganic thermal insulation materials are slightly better. In recent ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/26C04B24/42C04B103/65
CPCC04B40/0039C04B40/0042C04B2103/65C04B24/2641C04B22/06C04B24/36C04B24/32C04B24/42C04B22/00C04B22/148C04B24/04C04B2103/0068
Inventor 谢思松
Owner 谢思松
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com