Diamond resin grinding slice material and preparation method thereof

A technology of resin grinding discs and diamonds, applied in chemical instruments and methods, and other chemical processes, can solve the problems of easy breakage, short life, poor toughness and bending resistance of grinding blocks, etc., and achieve increased roughness, durability Effects of enhanced friction performance and improved alkali corrosion resistance

Pending Publication Date: 2019-05-10
厦门家和兴钻石工具有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the above-mentioned patents, only resin is used as a binder, and no toughness-enhancing components are added. The toughness and bending resistanc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diamond resin grinding slice material and preparation method thereof
  • Diamond resin grinding slice material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0052] Example 1: A diamond resin grinding plate material, the raw material of which includes the following components by weight percentage:

[0053] Diamond 3%;

[0054] Cashew nut oil modified phenolic resin 10%;

[0055] Stainless steel powder 5%;

[0056] Copper fiber 5%;

[0057] Auxiliary abrasive 10%;

[0058] The melamine formaldehyde resin molding powder makes up to 100%. Both cashew nut oil modified phenolic resin and melamine formaldehyde resin molding powder can be obtained commercially.

[0059] A method for preparing diamond resin grinding sheet material includes the following steps:

[0060] Step 1: Mixing diamond, cashew nut oil modified phenolic resin, stainless steel powder, copper fiber, auxiliary abrasive, and melamine formaldehyde resin molding powder uniformly to obtain mixed powder;

[0061] Step two, put the lower mold into the hollow forming mold, spread the hook and loop fastener on the upper surface of the lower mold, with the hair side of the hook and loop facin...

Example Embodiment

[0065] Embodiment 2: A diamond resin grinding plate material, which is different from Embodiment 1 in that the raw material includes the following components by weight percentage:

[0066] Diamond 5%;

[0067] Cashew nut oil modified phenolic resin 12%;

[0068] Stainless steel powder 8%;

[0069] Copper fiber 10%;

[0070] Auxiliary abrasive 8%;

[0071] The melamine formaldehyde resin molding powder makes up to 100%.

Example Embodiment

[0072] Embodiment 3: A diamond resin grinding plate material, which is different from Embodiment 1 in that the raw material includes the following components by weight percentage:

[0073] Diamond 8%;

[0074] 15% cashew nut oil modified phenolic resin;

[0075] Stainless steel powder 12%;

[0076] 15% copper fiber;

[0077] Auxiliary abrasive 5%;

[0078] The melamine formaldehyde resin molding powder makes up to 100%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a diamond resin grinding slice material and a preparation method thereof, and relates to the technical field of grinding materials. The technical scheme includes that the diamond resin grinding slice material comprises, in weight percent, 3-8% of diamond, 10-15% of cashew nut oil modified phenolic resin, 5-12% of stainless steel powder, 5-15% of copper fibers, 5-10% of auxiliary abrasive and the balance melamine formaldehyde resin molding powder, and the total weight percent is 100%. According to the material, the cashew nut oil modified phenolic resin and the melamineformaldehyde resin molding powder are matched to serve as an adhesive of a grinding block, the toughness of the grinding block can be improved, friction resistance is enhanced, and bending strength and abrasion resistance are further enhanced after the copper fibers are added.

Description

technical field [0001] The invention relates to the technical field of abrasive materials, more specifically, it relates to a diamond resin abrasive material and a preparation method thereof. Background technique [0002] The diamond resin abrasive block is made of resin as the binder and diamond as the abrasive grain. Compared with the traditional abrasive block, the diamond resin abrasive block has the advantages of good sharpness, high processing efficiency and long service life. There is no need for frequent shutdowns, and the labor intensity of production employees is low. [0003] In the Chinese invention patent whose publication number is CN106956226A, a composite grinding block and its preparation method are disclosed. The composite grinding block includes a deck and a grinding head, and the grinding head is made of resin abrasives and magnesite abrasives. Composition, the magnesite abrasive is arranged on the periphery of the corresponding resin abrasive. The resi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L61/28C08L61/14C08L33/20C08K3/04C08K3/08C08K7/06C08K13/04C08J5/06C09K3/14
Inventor 廖美全
Owner 厦门家和兴钻石工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap