PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy with scratch resistance and preparation method thereof

A technology of scratch resistance and alloy, which is applied in the field of PC/ABS alloy with scratch resistance and its preparation, can solve the problems of low hardness, scratches by hard objects, limited improvement of scratch behavior, etc., and achieve easy Migration, good scratch resistance

Active Publication Date: 2019-05-31
SHANGHAI KUMHOSUNNY JINSHAN PLASTICS CO LTD
View PDF11 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] Although there are many reports on scratch-resistant materials, there is still no good report on the scratch resistance of PC/ABS.
Such as CN105623233A, the introduction of calcium carbonate will lead to the decline of mechanical properties, and at the same time, the improvement of scratching behavior is limited; although CN107674396A can improve the hardness by introducing PMMA,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy with scratch resistance and preparation method thereof
  • PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy with scratch resistance and preparation method thereof
  • PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy with scratch resistance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0083] This embodiment provides a method for preparing a PC / ABS alloy with scratch resistance, comprising the following preparation steps:

[0084] (1) Weigh each component by weight: PVDF is 90 parts, fluorinated graphite is 10 parts, antioxidant 245 is 0.1Kg, and antioxidant 168 is 0.1Kg.

[0085] (2) Put the other components of the prepared material in a mixer, and mix for 5-30 minutes to obtain a mixed material.

[0086] (3) Put the mixed material into a twin-screw extruder, control the screw speed to 500rpm, melt and extrude, and granulate to obtain polyvinylidene fluoride masterbatch.

[0087] The twin-screw extruder includes 10 temperature control zones, the temperature of temperature control zones 1 to 2 is 130 to 220°C, the temperature of temperature control zones 3 to 4 is 130 to 220°C, and the temperature of temperature control zones 5 to 6 is The temperature is 130-220°C, the temperature in temperature control zone 7-8 is 130-220°C, and the temperature in temperat...

Embodiment 2

[0095] This embodiment provides a method for preparing a PC / ABS alloy with scratch resistance, comprising the following preparation steps:

[0096] (1) Weigh each component by weight: PVDF is 90 parts, fluorinated graphite is 10 parts, antioxidant 245 is 0.1Kg, and antioxidant 168 is 0.1Kg.

[0097] (2) Put the other components of the prepared material in a mixer, and mix for 5-30 minutes to obtain a mixed material.

[0098] (3) Put the mixed material into a twin-screw extruder, control the screw speed to 500rpm, melt and extrude, and granulate to obtain polyvinylidene fluoride masterbatch.

[0099] The twin-screw extruder includes 10 temperature control zones, the temperature of temperature control zones 1 to 2 is 130 to 220°C, the temperature of temperature control zones 3 to 4 is 130 to 220°C, and the temperature of temperature control zones 5 to 6 is The temperature is 130-220°C, the temperature in temperature control zone 7-8 is 130-220°C, and the temperature in temperat...

Embodiment 3

[0107] This embodiment provides a method for preparing a PC / ABS alloy with scratch resistance, comprising the following preparation steps:

[0108] (1) Weigh each component by weight: PVDF is 40 parts, fluorinated graphite is 60 parts, antioxidant 245 is 0.1Kg, and antioxidant 168 is 0.1Kg.

[0109] (2) Put the other components of the prepared material in a mixer, and mix for 5-30 minutes to obtain a mixed material.

[0110] (3) Put the mixed material into a twin-screw extruder, control the screw speed to 500rpm, melt and extrude, and granulate to obtain polyvinylidene fluoride masterbatch.

[0111] The twin-screw extruder includes 10 temperature control zones, the temperature of temperature control zones 1 to 2 is 130 to 220°C, the temperature of temperature control zones 3 to 4 is 130 to 220°C, and the temperature of temperature control zones 5 to 6 is The temperature is 130-220°C, the temperature in temperature control zone 7-8 is 130-220°C, and the temperature in temperat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a PC/ABS (polycarbonate/acrylonitrile-butadiene-styrene) alloy with scratch resistance and a preparation method thereof. The PC/ABS alloy comprises, by weight, 30-80 parts of PC, 15-60 parts of ABS, 1-20 parts of polyvinylidene fluoride masterbatch, 0.5-5 parts of a compatibilizer, 2-15 pats of a toughener, 0.1-1 part of an antioxidant, and 0.1-1 part of a lubricant. The preparation method comprises preparing the materials by weight, adding the materials into a medium-speed mixer except for the polyvinylidene fluoride masterbatch, mixing for 5-30 min to obtain a mixture,adding the mixture into a twin-screw extruder under controlled speed of 180-600 rpm, feeding the polyvinylidene fluoride masterbatch from the lateral side, melting and extruding, and granulating to obtain the finished PC/ABS alloy. Compared with the prior art, the PC/ABS alloy with scratch resistance provided herein has high processibility and high scratch resistance.

Description

technical field [0001] The invention relates to the field of polymer materials, in particular to a PC / ABS alloy with scratch resistance and a preparation method thereof. Background technique [0002] PC / ABS alloy is a common engineering plastic alloy product. Due to its high heat resistance and excellent mechanical properties, it is widely used in automobiles, electronics, home appliances and other fields. However, as PC / ABS is more and more used in surface decoration parts, the requirements for aesthetics are getting higher and higher. At the same time, because decorative parts are often touched or touched, the scratch resistance of the material is also paid more and more attention. . [0003] Currently, there are many scratch-resistant patents. [0004] For example, Hu Senchuan et al. described in the CN105623233A patent that the wear resistance and scratch resistance of PC / ABS alloys can be improved by modifying calcium carbonate. [0005] Jiantian Maoxing described in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L69/00C08L55/02C08L27/16C08L51/00C08L53/00C08L33/12C08L51/04C08L83/04C08K13/02C08K3/04C08K5/134C08K5/526C08K5/20C08J3/22
Inventor 高磊李强辛敏琦
Owner SHANGHAI KUMHOSUNNY JINSHAN PLASTICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka