Compound curing agent used for polyester-type powder paint and production method and application thereof

A composite curing agent, powder coating technology, applied in powder coatings, polyester coatings, coatings, etc., can solve the problems of human germ cell mutation, hereditary, thick coating pinholes, etc., to achieve high epoxy equivalent, comprehensive Excellent performance, less irritating effect

Active Publication Date: 2019-06-07
安徽泰达新材料股份有限公司
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in recent years, it has been found that TGIC curing agent has potential sensitization and will cause mutations in human germ cells and is hereditary. Most countries in the European Union have banned the use of TGIC as a curing agent
However, powder coatings with HAA as curing agent always have defects such as thick coating pinholes and easy yellowing.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compound curing agent used for polyester-type powder paint and production method and application thereof
  • Compound curing agent used for polyester-type powder paint and production method and application thereof
  • Compound curing agent used for polyester-type powder paint and production method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Composite curing agent for polyester resin powder coatings described in the present embodiment, its preparation raw material comprises following components:

[0023]

[0024] The preparation method of composite curing agent for polyester type resin powder coating described in the present embodiment comprises the steps:

[0025] (1) Add the organic solvent, triglycidyl trimellitate, and hydroxyl polyester resin in the recipe amount into the reaction kettle, heat up to 80°C and mix thoroughly, keep warm for 3 hours until completely dissolved into one phase; then add the recipe amount Diglycidyl terephthalate, crystalline epoxy resin, heat preservation reaction at 90°C for 4 hours, then add dicyclopentadiene dioxide for reaction, heat up to 110°C and heat preservation reaction for 6 hours, until all become homogeneous , lower the temperature to 70°C, add the prescribed amount of trimesic acid triglycidyl, continue to keep warm at 70°C for 1 hour, and stop the reaction a...

Embodiment 2

[0029] Composite curing agent for polyester resin powder coatings described in the present embodiment, its preparation raw material comprises following components:

[0030]

[0031]

[0032] The preparation method of composite curing agent for polyester type resin powder coating described in the present embodiment comprises the steps:

[0033] (1) Add the organic solvent, triglycidyl trimellitate, and hydroxyl polyester resin in the recipe amount into the reaction kettle, heat up to 90°C and mix thoroughly, keep warm for 1 hour until completely dissolved into one phase; then add the recipe amount Diglycidyl terephthalate, crystalline epoxy resin, heat preservation reaction at 95°C for 2 hours, then add dicyclopentadiene dioxide for reaction, heat up to 120°C and heat preservation reaction for 2 hours, until all become homogeneous , lower the temperature to 70°C, add the amount of trimesic acid triglycidyl tricarboxylate, continue the heat preservation reaction at 70°C fo...

Embodiment 3

[0037] Composite curing agent for polyester resin powder coatings described in the present embodiment, its preparation raw material comprises following components:

[0038]

[0039]

[0040] The preparation method of composite curing agent for polyester type resin powder coating described in the present embodiment comprises the steps:

[0041] (1) Add the organic solvent, triglycidyl trimellitate, and hydroxyl polyester resin in the recipe amount into the reaction kettle, heat up to 85°C and mix thoroughly, keep warm for 2 hours until completely dissolved into one phase; then add the recipe amount Diglycidyl terephthalate, crystalline epoxy resin, heat preservation reaction at 92°C for 3 hours, then add dicyclopentadiene dioxide for reaction, raise the temperature to 115°C and heat preservation reaction for 4 hours, until all become homogeneous , lower the temperature to 70°C, add the amount of trimesic acid triglycidyl, continue to keep warm at 70°C for 2 hours, and sto...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of powder paint, particularly relates to a compound curing agent used for polyester-type powder paint, and further discloses a production method and application of the compound curing agent used for the polyester-type powder paint. The compound curing agent used for the polyester-type powder paint is mainly produced by using trimesic acid,tris(2,3-epoxypropy)ester and diglycidyl terephthalate as main raw materials and selectively adding 1,2,4-benzenetricarboxylic acid,tris(2,3-epoxypropy)ester, hydroxy polyester resin, bicyclopentadiene dioxide and / or crystalline epoxy resin for mixing reaction. The compound curing agent used for the polyester-type powder paint has a good curing effect, the mechanical performance of a produced coating is stable,and meanwhile, the coating has good boiling-resistant performance; and when the compound curing agent used for the polyester-type powder paint and polyester resin are cured, the performance of a product of the compound curing agent used for the polyester-type powder paint and the polyester resin totally reaches curing effects of current TGIC and HAA curing agents, and the compound curing agent used for the polyester-type powder paint and an existing TGIC or HAA product can be mixed for use, so that the comprehensive performance is more excellent.

Description

technical field [0001] The invention belongs to the technical field of powder coatings, in particular to a composite curing agent for polyester powder coatings, and further discloses its preparation method and application. Background technique [0002] Powder coating is a 100% solid powder that does not contain organic solvents. It is different from oil-based paints and water-based paints. It does not use solvent or water as a dispersion medium when coating, but uses air as a dispersion medium to evenly coat the workpiece. The surface is a new type of environmentally friendly paint that forms a special-purpose coating film after heating. Powder coating has the advantages of no VOC, environmental protection, energy saving, high construction efficiency and wide application range. With its advantages of economy, environmental protection, high efficiency and excellent performance, it is gradually replacing organic solvent-based coatings and has become an important development di...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/63C09D7/65C09D5/03C09D167/00
Inventor 柯伯成柯伯留汪永辉罗建立柯美松徐小买周晔
Owner 安徽泰达新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com