Preparation method and applications of photocatalysis material prepared through adding of graphene

A photocatalytic material, graphene technology, applied in the direction of chemical instruments and methods, botanical equipment and methods, applications, etc., can solve the problem of insufficient sewage treatment effect, achieve enhanced performance, expand the scope of use, and high light conversion rate Effect

Pending Publication Date: 2019-07-02
湖南天一长新材料科技有限责任公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage is that ultraviolet light irradiation is required, and the antibacterial rate is generally only 95%-96%. After drying with zeolite, it is used as a sewage treatment agent, and the sewage treatment effect is not strong enough.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and applications of photocatalysis material prepared through adding of graphene
  • Preparation method and applications of photocatalysis material prepared through adding of graphene

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] Embodiment one, the preparation method of the photocatalytic material that adds graphene, comprises the following steps, 1) at first indium and ruthenium are processed into nitric acid solution, and the nitric acid of 200 milliliters dissolves 4 grams of indium and 2 grams of ruthenium;

[0031] 2) Weigh 2 kg of butyl titanate and 2 kg of isopropanol respectively, first place the isopropanol in the container, then add butyl titanate, and stir for 5 minutes;

[0032] 3) Add 10 kg of deionized water to the reaction kettle, take 50 milliliters of indium nitrate and ruthenium nitrate solutions, put them in the deionized water in the reaction kettle, turn on the stirrer, and stir for 5 minutes;

[0033] 4) Weigh 5 grams of graphene aqueous solution and add it to the above reaction kettle. The graphene aqueous solution is a commercially available product with a graphene purity>99wt%, and the manufacturer is Suzhou Carbonfeng Graphene Technology Co., Ltd.;

[0034] 5) Add the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method and applications of a photocatalysis material prepared through adding of graphene. The preparation method comprises following steps: 1, indium and bismuthare dissolved in a nitric acid solution to obtain a mixed nitrate solution; 2, butyl titanate and isopropanol are mixed and stirred to obtain a mixed solution of butyl titanate and isopropyl; 3, a graphene aqueous solution, the mixed nitrate solution obtained in step 1, and deionized water are mixed and stirred to obtain a graphene mixed solution; 4, the graphene mixed solution prepared in the step 3 is mixed with the mixed solution of butyl titanate and isopropyl, and an obtained product is stirred, and is subjected to 2h of hydrolysis reaction at a reaction temperature of 60 to 70 DEG C; 5,the temperature is increased through heating to 95 to 100 DEG C, stirring is carried out, and reaction is carried out for 4h to form a viscous liquid; and 6, deionized water and isopropyl are added tothe viscous liquid, stirring is carried out, and when it is detected that the pH value becomes 7, stirring is stopped so ast o obtain a stock solution. The preparation method is simple and easy to operate, no ultraviolet light irradiation is needed, the antibacterial rate is high, and the organic matter decomposition performance is excellent.

Description

technical field [0001] The invention belongs to the field of new materials, and in particular relates to a preparation method and application of a graphene-added photocatalytic material. Background technique [0002] The current photocatalytic materials are compounds based on nano-titanium ions and nano-indium ions, which can effectively convert light into electric charges. Through their photosynthesis, electron transitions allow oxygen atoms in water to form hydrogen peroxide to kill microorganisms. or decompose organic matter. Photocatalytic materials have strong substance decomposition ability and superhydrophilic effect. Using this function, photocatalytic materials can be used for air purification, water purification, decomposition of organic substances, anti-fogging and anti-fouling coatings. For example, the Chinese patent number is 201610013744.6, and the patent name is a material and its preparation method for ultraviolet photocatalytic removal of bromate in water....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/62C02F1/30A01N59/00A01N55/02A01P1/00A01P3/00
CPCB01J23/62B01J23/002C02F1/30B01D53/8628B01D53/8603A01N59/00A01N55/02B01D2255/802B01D2258/06B01J2523/00B01J35/39B01J2523/33B01J2523/47B01J2523/821
Inventor 龙艳飞龙建新
Owner 湖南天一长新材料科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com