A kind of polyolefin elastomer adhesive film with low water vapor transmission rate and preparation method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A low water vapor, polyolefin technology, applied in the field of polyolefin elastomer film and preparation, can solve the problems of not fully guaranteeing reliability, losing water blocking effect, limited effect of improving water blocking performance of film, etc., to improve cross-linking Density, improve water resistance, improve the effect of cross-linking
Active Publication Date: 2020-12-01
HANGZHOU FIRST APPLIED MATERIAL CO LTD
View PDF6 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
This method has a limited effect on improving the water-blocking performance of the film, and when the water-absorbing agent is saturated or completely reacts with water, the water-blocking effect will be lost, and the reliability of the long-term use of the module cannot be fully guaranteed.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0024]Components comprising the following parts by mass: 80 parts of polyolefin elastomer with a melt index of 5g / 10min, brand C5070D (SABIC Innovative Plastics), 20 parts of ethylene octene copolymer modified resin containing 2.5% amino groups, 0.26 parts of ethylene glycol acid, 0.65 parts tert-butyl peroxyisopropyl carbonate, 0.6 parts triallyl isocyanurate, 0.5 parts vinyltriethoxysilane, 0.04 parts 3,5-di-tert-butyl-4-hydroxy - cetyl benzoate, 0.2 part molecular sieve, designated as S-1.
Embodiment 2
[0026] Components comprising the following parts by mass: 65 parts of polyolefin elastomers with a melt index of 15g / 10min, trade mark C13060D (SABIC Innovative Plastics), 35 parts of ethylene and pentene copolymer modified resins containing 1.0% carboxyl groups, 0.20 parts of 1 , 4-Butanediamine, 0.40 tert-Butyl 3,3,5 Trimethylhexanoate peroxide, 0.35 Triallyl Isocyanurate B, 0.5 Part Vinyltrimethoxysilane, 0.08 Part 4-Hydroxy - 2,2,6,6-tetramethyl-1-piperidinol, 0.25 parts of silica, denoted as S-2.
Embodiment 3
[0028] Components comprising the following parts by mass: 80 parts of polyolefin elastomers with a melt index of 30g / 10min, grade C30070D (SABIC Innovative Plastics), 20 parts of ethylene-butylene copolymer modified resins containing 2.0% isocyanate groups, 0.22 parts of 1 , 3-propanediol, 0.65 parts of 1,1-bis(tert-butylperoxy)-3,3,5-trimethylcyclohexane, 0.6 parts of triallyl isocyanurate, 0.5 parts of vinyltri Ethoxysilane, 0.02 part of 4-hydroxy-2,2,6,6-tetramethyl-1-piperidinol, 0.2 part of magnesium sulfate, denoted as S-3.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
thickness
aaaaa
aaaaa
melt flow index
aaaaa
aaaaa
melt flow index
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses a low water vapor transmission rate polyolefin elastomer adhesive film and a preparation method, which comprises 50-100 parts by mass of matrix resin, 0-40 parts by mass of modified resin, and 0.001-2 parts by mass of active agent , 0.1 to 3 parts by mass of organic peroxides, 0.02 to 5 parts by mass of co-crosslinking agents, 0.02 to 2 parts by mass of silane coupling agents, 0.005 to 2 parts by mass of light stabilizers, 0 to 20 parts by mass of Water blocking filler. The present invention improves the cross-linking degree and cross-linking density of the adhesive film by adding the modified resin and activator with active groups, and reduces the water vapor transmission rate; adding water-blocking fillers further improves the water-blocking performance of the adhesive film, ensuring Component reliability, extending component life.
Description
technical field [0001] The invention belongs to the field of photovoltaic encapsulation materials, and relates to a polyolefin elastomer adhesive film with low water vapor transmission rate used for encapsulation of electronic devices and a preparation method. Background technique [0002] Today, with energy shortages and environmental problems becoming more and more prominent, it has become an inevitable trend to find renewable and environmentally friendly green energy. Photovoltaic power generation is the process of converting solar energy into electrical energy. It has three advantages of permanence, cleanliness and flexibility. Compared with traditional thermal power generation, hydropower generation and nuclear power generation, its preparation process is simple and reproducible. Therefore, Has a very good development prospects. [0003] At present, the packaging material of photovoltaic modules mainly adopts ethylene vinyl acetate copolymer (EVA). However, the molecu...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More