High-temperature-resisting and easy-to-process semi-aromatic polyamide and preparation method thereof

A semi-aromatic polyamide, an easy-to-process technology, applied in the field of high-temperature-resistant and easy-to-process semi-aromatic polyamide and its preparation, can solve the problems of high melting point, poor dimensional stability, poor performance retention, and poor toughness, and achieve good toughness , Improve dimensional stability and performance retention, and lower the melting point

Inactive Publication Date: 2019-07-23
DONGGUAN HUAYING NEW MATERIAL CO LTD
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a semi-aromatic polyamide with high temperature resistance and easy processing and its preparation method, which solves the problems of high melting point, poor toughness, poor dimensional stability and performance retention rate of existing semi-aromatic polyamide products in humid environment. good technical questions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-temperature-resisting and easy-to-process semi-aromatic polyamide and preparation method thereof
  • High-temperature-resisting and easy-to-process semi-aromatic polyamide and preparation method thereof
  • High-temperature-resisting and easy-to-process semi-aromatic polyamide and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] A preparation method of a 10T type high temperature resistant and easy-to-process semi-aromatic polyamide (abbreviated as 10T / OADP):

[0053] Step 1: Preparation of dimer acid salt, weigh unhydrogenated dimer acid 2824.50g (about 5mol), pentamethylenediamine 1132.21g (about 5.05mol) and 4000g deionized water, mix well and pour it into 20L stainless steel reactor. Turn on the stirring device and set the rotation speed to 60r / min, and pass in nitrogen to replace the air in the reaction kettle. The temperature was raised to 80° C. for a salt-forming reaction, and the reaction was stopped after 3 hours of normal pressure reaction. The reactant was separated by suction filtration, the filter cake was washed with absolute ethanol and deionized water, and then the product was dried under vacuum at 80° C. for 12 hours to obtain a white dimer salt powder, which was ready for use.

[0054] Step 2: precondensation reaction, 1231.69g (about 7.41mol) of terephthalic acid, 1281.93g...

Embodiment 2

[0060] The preparation method of a kind of 10T high-temperature-resistant and easy-processing semi-aromatic polyamide (abbreviated as 10T / OADP) is as follows:

[0061] Step 1: the preparation of the dimer salt is the same as in Example 1. This example directly uses the dimer salt prepared in Example 1.

[0062] Step 2: precondensation reaction: 1231.69g (about 7.41mol) of terephthalic acid, 1281.93g (about 7.41mol) of decyl diamine, 267.94g of dimer salt (about 2.5% of the total molar ratio of diacid / diamine) %), sodium phosphite 8.00g, benzoic acid 45.25g and 1200g deionized water drop into the stainless steel reactor, and pass into the air in the nitrogen replacement reactor three times. Set the speed at 250r / min, raise the temperature to 160°C, and the pressure to 0.6MPa, and react for 1.5 hours; continue to raise the temperature to 235°C, keep the pressure at 2.5MPa, and react for 5 hours to ensure that terephthalic acid, decanediamine and The full reaction of the dimer ...

Embodiment 3

[0065] The preparation method of 9T high-temperature-resistant and easy-processing semi-aromatic polyamide (referred to as 9T / OADP) is as follows:

[0066] Step 1: Preparation of dimer salt: same as in Example 1. The diamine uses nonanediamine, and dimer acid is used to make dimer salt.

[0067] Step 2: precondensation reaction, 1231.69g (about 7.41mol) of terephthalic acid, 1178.19g (about 7.41mol) of nonanediamine, 428.70g of dimer salt (about 4% of the total molar ratio of diacid / diamine) %), sodium phosphite 8.00g, benzoic acid 45.25g and 1200g deionized water drop in the stainless steel reactor, airtight reactor, vacuumize, then pass into nitrogen, then vacuumize the air in the nitrogen replacement reactor three times. Set the speed at 200r / min, raise the temperature to 150°C, and the pressure to 0.5MPa, and react for 2 hours; continue to raise the temperature to 230°C, keep the pressure at 2.5MPa, and react for 4 hours to ensure that terephthalic acid, nonanediamine and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
melting pointaaaaaaaaaa
Login to view more

Abstract

The invention provides high-temperature-resisting and easy-to-process semi-aromatic polyamide and a preparation method thereof. A preparation process of the high-temperature-resisting and easy-to-process semi-aromatic polyamide mainly comprises three steps including preparation of dimer acid salt, a pre-polycondensation reaction and a solid-phase polymerization reaction. According to the high-temperature-resisting and easy-to-process semi-aromatic polyamide, dimer acid with a long flexible chain is introduced into semi-aromatic polyamide, so that the melting temperature is reduced, a processing temperature range is widened, and meanwhile, the toughness of the semi-aromatic polyamide is greatly increased; the size stability and performance retention rate of the semi-aromatic polyamide undera humid environment are improved and the semi-aromatic polyamide has a wide application prospect.

Description

technical field [0001] The invention belongs to the synthesis technology of semi-aromatic polyamide, in particular to a semi-aromatic polyamide with high temperature resistance and easy processing and a preparation method thereof. Background technique [0002] High temperature resistant polyamide has high temperature resistance due to its molecular structure containing benzene ring or other aromatic ring structure. It is usually formed by polycondensation of aromatic diamine or diacid and aliphatic diacid or diamine. Semi-aromatic polyamide has both the excellent physical and mechanical properties of aromatic polyamide and the incomparable processing performance of aliphatic polyamide, so it has become the main product of high temperature resistant polyamide. Representative products include DuPont's HTN series (PA6T / 66), Mitsubishi Gas's MXD6, DMS's PA46, etc. [0003] Most of the products in the prior art have relatively high melting points, generally above 300°C. Although...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G69/26C08G69/28
CPCC08G69/26C08G69/28
Inventor 贺鹏勇蔡绪福张小林袁丹丹
Owner DONGGUAN HUAYING NEW MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap