A kind of wetting agent and its preparation method and application

A technology of sizing agent and coupling agent, which is applied in the field of sizing agent for direct yarns used in high-quality surface pultrusion profiles, to achieve the effects of less hairiness, improved compatibility, and strong clustering

Active Publication Date: 2022-02-01
JUSHI GRP CO
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] With the wide application of pultrusion technology, the quality requirements for pultrusion profiles are getting higher and higher, especially for customers in the high-end field, the demand for high-quality surface profiles is increasing. Direct yarn sizing developed for profile surface quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of wetting agent and its preparation method and application
  • A kind of wetting agent and its preparation method and application
  • A kind of wetting agent and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0070] The preparation method of this sizing agent comprises the following steps:

[0071] Dilution of 1S film former, surfactant A and surfactant B:

[0072] Dilute the film-forming agent with 1 to 3 times its mass of water; dilute surfactant A with 4 to 6 times its mass of water, and the water temperature is 80 to 95°C; dilute surfactant B with 4 to 6 times its mass diluted with water, the water temperature is 80-95°C;

[0073] Preparation of 2S coupling agent:

[0074] Add water with a total water content of 30% of the wetting agent into the container, sequentially add a pH regulator and a coupling agent, and stir to obtain a dispersion solution of the coupling agent;

[0075] Preparation of 3S sizing agent:

[0076] Add the diluted film-forming agent, surfactant A, and surfactant B obtained in step 1S to the coupling agent dispersion solution obtained in step 2S, supplement the water in the wetting agent formula, and stir evenly to obtain the product.

Embodiment 1

[0080] Weigh each component by mass percentage, and prepare the sizing agent according to the following steps:

[0081] 1S Dilution of film-forming agent, surfactant A and surfactant B: dilute the dimer acid modified epoxy resin emulsion with water 1 to 3 times its mass; dilute the acetylenic diol Germini nonionic surfactant with its Dilute with 4-6 times the mass of water, and the water temperature is 80-95°C; dilute the disemicarbazide polymer cationic surfactant with 4-6 times the mass of water, and the water temperature is 80-95°C;

[0082] Preparation of 2S coupling agent: add water with a total water content of 30% of the wetting agent into the container, add glacial acetic acid and A-151 in sequence, and stir to obtain a coupling agent dispersion solution;

[0083] Preparation of 3S sizing agent: add the diluted dimer acid-modified epoxy resin emulsion, acetylene glycol Germini nonionic surfactant, and diaminocarbamide polymer cationic surfactant prepared in step 1S to ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
bending strengthaaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention provides a wetting agent, the total mass of the non-water part of the wetting agent accounts for 5% to 7% of the total mass of the wetting agent, and the balance is water; the mass of the non-water part of each component in the wetting agent accounts for The percentage of the total mass of the non-water part is expressed as follows: 5% to 17% of coupling agent; 45% to 65% of film forming agent; 8% to 22% of surfactant A; 8% to 22% of surfactant B; Agent 1% ~ 7%. The direct yarn made by using the sizing has excellent raw filament bundling property, no fiber splitting, and less wool yarn fluff; the prepared non-alkali glass fiber direct yarn reinforced composite material has better bending strength and surface quality of the pultrusion profile.

Description

technical field [0001] The invention relates to the field of glass fiber sizing agents, in particular to a sizing agent for direct yarns for high-quality surface pultrusion profiles. Background technique [0002] Pultrusion molding technology is a continuous automatic production process for manufacturing composite materials with high glass fiber content, high performance and low cost. , After continuous mold release, the profile products are obtained by cutting to length or certain post-processing. In addition to the corrosion resistance, aging resistance, and insulation properties of traditional FRP materials, materials manufactured by pultrusion technology also have the characteristics of stable product size, good appearance quality, and high production efficiency. Based on the unique properties of the materials manufactured by the pultrusion process, its products can replace traditional materials such as metal, plastic, wood, ceramics, etc., and are widely used in chemic...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C25/465C03C25/12
CPCC03C25/465C03C25/12
Inventor 张志坚章建忠费其锋周贤旺李明宋长久杨洋
Owner JUSHI GRP CO
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com