Preparation method of anti-cutting flame-resistant thermal-radiation-resistant camouflage fabric

A cutting-resistant and heat-radiation-resistant technology, applied in chemical instruments and methods, layered products, metal layered products, etc., can solve problems such as lack of cross-system integration capabilities, single functional design, and lack of composite fabrics to achieve good cut resistance effect, excellent thermal radiation resistance, good camouflage stealth and anti-reconnaissance performance

Active Publication Date: 2019-09-03
二向箔苏州微波介质材料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The old-fashioned concept of traditional material application, the singleness of functional design, and the lack of cross-system integration capabilities have resulted in the lack of similar composite fabrics in the market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0013] The equipment that present embodiment weaving method adopts is:

[0014] Model RSDT-S three-position computerized double-sided jacquard machine

[0015] Machine No. 3- 36 needles / 25.4mm

[0016] Barrel diameter 30-34 inches

[0017] Road number 20-96F

[0018] A preparation method of cut-resistant, flame-retardant, heat-resistant radiation camouflage fabric, the method comprising the steps of:

[0019] (1) First, the colored heterocyclic aromatic fiber and ultra-high molecular weight polyethylene fiber are blended on a double-sided large circular knitting machine.

[0020] (2) On the computer double-sided jacquard machine, enter the required camouflage pattern into the process package through the scanner, and the computer will automatically assign the needle arrangement process. Then input the color of the corresponding camouflage pattern and the cycle value of the color block into the process package, and the loom automatically adjusts the process module according ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of an anti-cutting flame-resistant thermal-radiation-resistant camouflage fabric. According to the preparation method, colored heterocyclic aromatic fiberand ultrahigh molecular weight polyethylene fiber are subjected to blending, and jacquard technology is adopted in preparation using a double surface jacquard machine so as to obtain a flame-resistanthigh-strength anti-cutting fabric, and single surface adhesion of nanometer silver ion film with a nanometer silver content of 15 to 40% of the flame-resistant high-strength anti-cutting fabric is carried out so as to obtain a finished product. The technology is simple; the colored heterocyclic aromatic fiber and the ultrahigh molecular weight polyethylene fiber are subjected to blending, weavingis carried out using a computerized jacquard machine, and the flame-resistant high-strength anti-cutting fabric and the nanometer silver ion film are subjected to combination, so that the anti-cutting flame-resistant thermal-radiation-resistant camouflage fabric excellent in performance is obtained, and industrialized production condition requirements are satisfied.

Description

technical field [0001] The invention relates to the technical field of functional fabric production, in particular to a preparation method of a cut-resistant, flame-retardant and heat-resistant radiation-resistant camouflage fabric. Background technique [0002] On April 1, 2019, a forest fire broke out in Liangshan, Sichuan Province, causing 30 fire fighters to die on duty. When the accident happened, the fire scene reached hundreds of degrees of high temperature. In addition to the direct burn of the flame, there was also the penetration caused by the high temperature. Sexual heat radiation brings huge harm to human body especially. The cause of the accident is enough to highlight the lack of function of our professional protective equipment. The firefighting clothing worn by general firefighters every day has only a certain degree of flame retardancy, does not have the performance of heat radiation protection, and does not have good durability against cutting. [0003] ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/00B32B9/04B32B15/085B32B15/14B32B27/02B32B27/32B32B7/12D04B1/16D04B1/12
CPCB32B5/02B32B5/08B32B7/12B32B15/085B32B2262/0253B32B2307/3065B32B2307/581B32B2307/71D04B1/126D04B1/16D10B2321/0211D10B2331/14
Inventor 蔡正波
Owner 二向箔苏州微波介质材料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com