Method for preparing magnesium hydroxide two-dimensional nano-sheets through rapid precipitation
A magnesium hydroxide and two-dimensional nanotechnology, which is applied in the field of rapid precipitation to prepare two-dimensional magnesium hydroxide nanosheets, achieves the effects of stable quality, simple operation and novel product morphology.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0018] The invention provides a method for rapidly precipitating two-dimensional nanosheets of magnesium hydroxide. This method uses Mg(NO 3 ) 2 and NaHCO 3 As a raw material, the liquid phase precipitation method is used to synthesize, and it is realized by the following technical side:
[0019] At 65°C, 520 g of 0.19% Mg(NO 3 ) 2 ·6H 2 O and 480 g of 0.42% NaHCO 3 Dissolve in water, continue to stir 10 minutes with 300r / min; Gained mixed material is with 5000r / min, centrifugation 5 minutes with high-speed centrifuge; Gained light white precipitate is cleaned 3 times with 96% ethanol; Gained material is in 60 °C for 12 hours to obtain magnesium hydroxide two-dimensional nanosheets.
[0020] XRD results such as figure 1 The product structure is magnesium hydroxide, and the appearance is as follows figure 2 As shown, it is a nano-scale sheet structure, and the width of the nano-sheet is about 500 nm.
Embodiment 2
[0022] The invention provides a method for rapidly precipitating two-dimensional nanosheets of magnesium hydroxide. This method uses Mg(NO 3 ) 2 and NaHCO 3 As a raw material, the liquid phase precipitation method is used to synthesize, and it is realized by the following technical side:
[0023] At 65°C, 540 g of 0.38% Mg(NO 3 ) 2 ·6H 2 O and 460 g of 0.50% NaHCO 3 Dissolve in water, continue to stir 10 minutes with 300r / min; Gained mixed material is with 5000r / min, centrifugation 5 minutes with high-speed centrifuge; Gained light white precipitate is cleaned 3 times with 96% ethanol; Gained material is in 60 °C for 12 hours to obtain magnesium hydroxide two-dimensional nanosheets.
Embodiment 3
[0025] The invention provides a method for rapidly precipitating two-dimensional nanosheets of magnesium hydroxide. This method uses Mg(NO 3 ) 2 and NaHCO 3 As a raw material, the liquid phase precipitation method is used to synthesize, and it is realized by the following technical side:
[0026] At 65°C, 580 g of 0.58% Mg(NO 3 ) 2 ·6H 2 O and 420 g of 0.59% NaHCO 3 Dissolve in water, continue to stir 10 minutes with 300r / min; Gained mixed material is with 5000r / min, centrifugation 5 minutes with high-speed centrifuge; Gained light white precipitate is cleaned 3 times with 96% ethanol; Gained material is in 60 °C for 12 hours to obtain magnesium hydroxide two-dimensional nanosheets.
PUM
Property | Measurement | Unit |
---|---|---|
width | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap