Preparation method of electric vehicle grade lithium carbonate

A technology for electric vehicles and lithium carbonate, applied in the direction of lithium carbonate;/acid carbonate, etc., to achieve high product yield, increase capacity, and low loss

Active Publication Date: 2022-01-25
TIANQI LITHIUM CORP
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] As can be seen from Table 1, the purity, impurity content and magnetic substance content requirements of EV grade lithium carbonate products are all higher than those of battery grades, and the existing lithium salt production methods can only obtain battery grade lithium carbonate products in large-scale production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of electric vehicle grade lithium carbonate
  • Preparation method of electric vehicle grade lithium carbonate
  • Preparation method of electric vehicle grade lithium carbonate

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The preparation method of electric vehicle grade lithium carbonate of the present invention, comprises the steps:

[0037] A. Slurry treatment: After filtering the lithium sulfate slurry, add calcium carbonate to the filtrate, and separate the solid and liquid to obtain calcium sulfate dihydrate solid and slightly acidic liquid, wherein the lithium sulfate slurry is obtained by leaching after acidification and roasting of lithium ore The leaching slurry, the pH value of the lithium sulfate slurry is 1-2, the specific gravity is 1.2-1.4, and the concentration is Li 2 The O content is calculated as 30-32g / L;

[0038] B. Twice neutralization and purification: adjust the pH of the slightly acidic liquid in step A to 6.5 to 7.5, react for 30 to 40 minutes, and filter to obtain a neutral liquid; then add sodium carbonate to the neutral liquid and adjust the pH to 11 to 7.5 12. React for 30-40 minutes, filter to obtain a primary purification solution;

[0039] C. Decalcifica...

Embodiment 1

[0082] Such as figure 1 Shown, adopt following steps to produce and obtain EV grade lithium carbonate:

[0083] A. Slurry treatment: After filtering the lithium sulfate slurry, add 12kg / m3 to the filtrate 3 calcium carbonate, solid-liquid separation to obtain calcium sulfate dihydrate solid and slightly acidic liquid, wherein, the lithium sulfate slurry is the leaching slurry obtained by leaching lithium ore after acidification and roasting, the pH value of the lithium sulfate slurry is 1, and the specific gravity is 1.2 , the concentration is Li 2 The O content was calculated as 30 g / L.

[0084] B. Twice neutralization and purification: adjust the pH of the slightly acidic solution in step A to 6.5, react for 30 minutes, and filter to obtain a neutral solution; then add a concentration of 300 ± 10g / L sodium carbonate solution 1.5 liters / Prepare a neutral solution, adjust the pH to 11, react for 30 minutes, and filter to obtain a primary purification solution.

[0085] C....

Embodiment 2

[0095] Such as figure 1 Shown, adopt following steps to produce and obtain EV grade lithium carbonate:

[0096] A. Slurry treatment: After filtering the lithium sulfate slurry, add 16kg / m3 to the filtrate 3 calcium carbonate, solid-liquid separation to obtain calcium sulfate dihydrate solid and slightly acidic liquid, wherein, the lithium sulfate slurry is the leaching slurry obtained by leaching lithium ore after acidification and roasting, the pH value of the lithium sulfate slurry is 2, and the specific gravity is 1.4 , the concentration is Li 2 The O content was calculated as 32 g / L.

[0097] B. Twice neutralization and purification: adjust the pH of the slightly acidic solution in step A to 7.5, react for 40 minutes, filter to obtain a neutral solution; then add a concentration of 300 ± 10g / L sodium carbonate solution 2 liters / Prepare a neutral solution, adjust the pH to 12, react for 40 minutes, and filter to obtain a primary purification solution.

[0098] C. Decal...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
magnetic flux densityaaaaaaaaaa
magnetic flux densityaaaaaaaaaa
magnetic flux densityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method of electric vehicle-grade lithium carbonate, belonging to the technical field of lithium batteries. The technical problem that the present invention solves is to provide a kind of preparation method of electric vehicle grade lithium carbonate. In the method, a concentrate is obtained through slurry treatment, two neutralization purifications, calcium removal, demagnetization and organic matter removal, and concentration, and the concentrate is refined four times to obtain EV grade lithium carbonate. The method of the present invention can successfully prepare EV-grade lithium carbonate that is not currently on the market, and realize the industrialized production of EV-grade lithium carbonate products. The product quality obtained is EV-grade products, and compared with battery-grade products, its chemical index is higher Excellent, lower magnetic substances, less likely to agglomerate, and excellent product consistency, laying a solid foundation for improving the capacity, battery life and safety performance of lithium power batteries.

Description

technical field [0001] The invention relates to a preparation method of electric vehicle-grade lithium carbonate, belonging to the technical field of lithium batteries. Background technique [0002] Under the background of energy constraints and environmental pollution, the world will regard the development of new energy as an important measure to improve the environment and save costs. Among them, new energy vehicles (electric vehicles) have become the development direction of the future automobile industry due to their incomparable advantages such as low cost of use, easy maintenance, low manufacturing difficulty, stable driving, strong power, low carbon and environmental protection. According to the data released by the China Association of Automobile Manufacturers, from January to November 2017, the production and sales of pure electric vehicles were 526,000 and 502,000, a year-on-year increase of 56.5% and 60.9%. 34,420 vehicles, a year-on-year increase of 119.19% and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01D15/08
CPCC01D15/08C01P2006/80
Inventor 涂明江李隆君夏光友邓玉松刘长春陈福怀刘卫东曹乃珍李超邓红云徐川高宜宝
Owner TIANQI LITHIUM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com