A stainless steel wire, large deformation technology, applied in the direction of manufacturing tools, furnaces, heat treatment equipment, etc., to achieve the effect of no defects in appearance, good corrosion resistance, and bright surface

Active Publication Date: 2021-05-07
江阴祥瑞不锈钢精线有限公司 +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem to be solved by the present invention is to provide a production process of stainless steel wire for riveting shells with large deformation. The characteristics of large deformation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Production Process of Stainless Steel Wire for Riveting Shells with Large Deformation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] In order to make the technical problems, technical solutions and advantages to be solved by the present invention clearer, the following will describe in detail in conjunction with specific embodiments.

[0026] The invention provides a production process of stainless steel wire for riveting shells with large deformation.

[0027] The process includes steps as follows:

[0028] (1) 304HC stainless steel wire coil with a diameter of Φ5.5mm is used as the raw material;

[0029] (2) Draw the raw material once, and draw it into stainless steel wires with diameters of Φ3.79mm and Φ4.59mm;

[0030] (3) pickling the stainless steel wire made in step (2) with sulfuric acid electrolyte;

[0031] (4) washing the stainless steel wire after pickling;

[0032] (5) carry out drying treatment to stainless steel wire with preheating furnace;

[0033] (6) the stainless steel wire after drying is annealed through the annealing furnace;

[0034] (7) film treatment is carried out to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention provides a production process of stainless steel wire for riveting shells with large deformation, and belongs to the technical field of stainless steel wire production. The process uses 304HC stainless steel wire with a diameter of Φ5.5mm as the raw material; draws once to make stainless steel wires with diameters of Φ3.79mm and Φ4.59mm; then pickles the stainless steel wire with sulfuric acid electrolyte , and then washed with water; then the stainless steel wire is dried in a preheating furnace; the dried stainless steel wire is annealed in an annealing furnace; the annealed stainless steel wire is treated with a film; finally the processed stainless steel wire is coiled and packaged finished product. The stainless steel wire produced by this process has a bright surface, no defects in appearance, excellent mechanical properties, good corrosion resistance, and can achieve large deformation. The mechanical properties of Φ3.79mm stainless steel wire are: tensile strength 530‑550MPa, yield strength 240‑250MPa, elongation 40‑50%, hardness HV: 160‑180; mechanical properties of Φ4.59mm stainless steel wire are: tensile strength 540‑570MPa, yield strength 230‑250MPa, elongation 45‑55%, hardness HV: 160‑190.

Description

technical field [0001] The invention relates to the technical field of stainless steel production, in particular to a production process of stainless steel wire for riveting shells with large deformation. Background technique [0002] At present, 304HC stainless steel wire has been widely used in various fields, especially as large deformation stainless steel wire, which is characterized by 3.48-3.62% Cu. In austenitic stainless steel, the role of copper as an alloying element is to significantly reduce the austenite The cold hardening tendency of stainless steel improves the cold forming performance, and the presence of copper can significantly improve the corrosion resistance of austenitic stainless steel to reducing media, such as sulfuric acid, phosphoric acid, etc., and when molybdenum and copper are compounded and alloyed, the effect is even greater prominently, the addition of copper promotes the dissolution of molybdenum to form MoO 4 2- , strongly promote the pass...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/42C22C38/44C21D9/52C21D1/26C21D1/74C25F1/06
CPCC21D1/26C21D1/74C21D9/525C21D2211/001C22C38/001C22C38/02C22C38/04C22C38/42C22C38/44C25F1/06
Inventor 胡建祥宋仁伯全书仪王天一苏阳怀烨明王红霞
Owner 江阴祥瑞不锈钢精线有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More