Faceted Crystal Glass Polishing Method
A crystal glass, faceted technology, applied in glass forming, glass manufacturing equipment, spherical grinder, etc., can solve the problems of uneven facet size, time-consuming and laborious quality, and can not be guaranteed, and achieves the reduction of labor and labor. time, the effect of reducing the processing cost
Active Publication Date: 2020-06-09
浦江馨妍水晶工艺品有限公司
View PDF5 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] Existing crystal glass ball facets, faceting on the finished crystal ball is a time-consuming and poor quality work. In the prior art, most of the facets are manually faceted, and there are uneven facets and uneven facet sizes. After the facet is completed, it needs to be transferred to the polishing process for polishing, which is time-consuming and laborious and the quality cannot be guaranteed
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0025] In order to enable those skilled in the art to better understand the solutions of the present invention, the technical solutions in the embodiments of the present invention will be clearly and completely described below in conjunction with the drawings in the embodiments of the present invention. Obviously, the described embodiments are only It is a part of embodiments of the present invention, but not all embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts shall fall within the protection scope of the present invention.
[0026] The research and development of faceted crystal glass polishing process includes the following steps:
[0027] a. Ingredients: According to the requirements of the crystal glass formula, put each raw material into the mixer and mix them evenly to obtain the ingredients according to the parts by mass;
[0028] b, heating: put the p...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses faceted crystal glass polishing technology research and development. The faceted crystal glass polishing technology research and development comprises the following steps batching is conducted, specifically, according to the crystal glass formula requirement, all raw materials are put into a blender mixer by mass portion to be uniformly mixed, and a prepared material is obtained; heating is conducted, specifically, the obtained prepared material is put into a crystal glass furnace to be melted, and molten crystal glass is obtained; cooling is conducted, specifically, the molten crystal glass is cooled to a certain temperature through a temperature control system; forming is conducted, specifically, the cooled molten crystal glass is poured into ball making equipmentfor forming processing, crystal glass ball blanks are obtained, and the obtained crystal glass ball blanks are subjected to annealing treatment; faceting is conducted, specifically, the crystal glassball blanks are subjected to faceting treatment through a faceting machine, and finished multi-faceted crystal glass ball products are obtained; and polishing is conducted, specifically, the facetedcrystal glass ball are subjected to polishing treatment through polishing equipment, and finished faceted crystal glass ball products are obtained. According to faceted crystal glass polishing technology research and development, automatic faceting and polishing of the crystal glass balls are achieved, the quality is improved, the machining time is shortened, and the labor force of manpower is reduced.
Description
technical field [0001] The invention relates to the technical field of crystal glass processing, in particular to the research and development of a faceted crystal glass polishing process. Background technique [0002] Existing crystal glass ball facets, faceting on the finished crystal ball is a time-consuming and poor quality work. In the prior art, most of the faceting is done by hand, and there are uneven facets and uneven facet sizes. After the facet is completed, it needs to be transferred to the polishing process for polishing, which is time-consuming and laborious, and the quality cannot be guaranteed. Contents of the invention [0003] In order to overcome the deficiencies of the prior art, the present invention provides the research and development of the faceted crystal glass lapping and polishing process. [0004] In order to achieve the above object, the present invention adopts the following technical solutions: the research and development of faceted crysta...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Patents(China)
IPC IPC(8): B24B1/00B24B11/02B24B41/06C03B19/02C03B25/00
CPCB24B1/00B24B11/02B24B41/06C03B19/02C03B25/00
Inventor 张宝清
Owner 浦江馨妍水晶工艺品有限公司