High-strength heat-insulating fiber composite spraying material and preparation method thereof

A fiber composite and spray material technology, applied in the field of spray material, can solve the problems of large waste, affect normal production, fast heat loss, etc., and achieve the effects of low thermal conductivity, long service life, and improved adhesion.

Pending Publication Date: 2019-11-29
河南恒耐尔耐火材料有限公司
View PDF15 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The blast furnace or hot blast stove is partially damaged during use, and the heat is lost quickly, which affects normal production and wastes a lot

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-strength heat-insulating fiber composite spraying material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The proportion by weight of the components is: mullite light material 52%, spherical fiber fleece 25%, Guangxi white mud 5%, guar beans 2%, aluminum dihydrogen phosphate liquid 8%, pure calcium aluminate 70 cement 5%, silica powder 3%.

Embodiment 2

[0027] The proportion by weight of the components is: mullite light material 52%, spherical fiber fleece 15%, Guangxi white mud 5%, guar beans 1%, aluminum dihydrogen phosphate liquid 8%, pure calcium aluminate 70 cement 5%, silica powder 3%.

Embodiment 3

[0029] The proportion by weight of the components is: mullite light material 52%, spherical fiber fleece 20%, Guangxi white mud 5%, guar beans 0.8%, aluminum dihydrogen phosphate liquid 8%, pure calcium aluminate 70 cement 5%, silica powder 3%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of spraying materials, and particularly relates to a high-strength heat- insulation fiber composite spraying material capable of quickly repairing heat damaged parts, prolonging service life and saving cost and a preparation method thereof. The high-strength heat- insulation fiber composite spraying material comprises the following components in percentage by weight: 50-54% of a mullite light material, 23-27% of spherical fiber wool, 4-6% of Guangxi white mud, 1.5-3% of guar gum, 6-9% of aluminum dihydrogen phosphate liquid, 4-6% of pure calcium aluminate 70 cement and 4-6% of silica micropowder. The invention aims to provide the high-strength heat- insulation fiber composite spraying material which can effectively solve the repair of heat damaged parts, prolong the service life and save cost and a preparation method thereof with simple process and low cost.

Description

technical field [0001] The invention belongs to the technical field of injection materials, and in particular relates to a high-strength heat-insulating fiber composite injection material capable of quickly repairing heat-damaged parts of a blast furnace or a hot blast stove and a preparation method thereof. Background technique [0002] The spray material is a bulk refractory material constructed by spraying, which is composed of refractory aggregate and powder with a certain particle size, binder and admixture. The jet power is usually compressed air. The main material is selected according to the maximum temperature that may be reached in the kiln, the range of temperature fluctuations, and the nature of the slag. The gunning material also needs to consider the material of the lining itself. The injection material is mainly used to form an integral inner guard and repair other furnace linings. The blast furnace or hot blast stove is partially damaged during use, and th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/185C04B35/63C04B35/636C04B35/66C04B35/80
CPCC04B35/66C04B35/185C04B35/636C04B35/6309C04B35/6303C04B2235/5252C04B2235/349C04B2235/3418C04B2235/96C04B2235/9607
Inventor 马骥姜丽霞
Owner 河南恒耐尔耐火材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com