Production method for reducing temperature drop of hot-rolled intermediate blank

A production method and temperature drop technology, applied in the direction of temperature control, etc., can solve problems such as high temperature of slab out of the furnace, increase of gas consumption, and prolongation of furnace time, so as to improve rolling stability, reduce rolling time, reduce The effect of edge temperature drop

Inactive Publication Date: 2019-12-20
ANGANG STEEL CO LTD
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the temperature drop in the rough rolling area of ​​Anshan Iron and Steel's 1580 production line is relatively large, which directly causes the slab to be released from the furnace at a higher temperature, prolongs the time in the furnace, increases gas consumption, and increases costs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0021] 1. The rough rolling area of ​​the hot rolling line is composed of the fixed width mill, R1 and R2 rolling mills. Before the first and second passes of the R1 rolling mill, it is not judged whether the rolling of the R2 rolling mill is completed. The R1 rolling mill is used for rolling in advance. The time is 1 to 3 seconds, and the rolling speed of R1 and R2 is increased, and each pass is increased by 0.3 to 0.8 m / s on the basis of the rolling speed set by the original second-level digital model; (for example: the rolling speed of R1 three passes Respectively: 1.0 m / s, 1.44 m / s, 1.76 m / s, respectively increased to 1.5 m / s, 1.8 m / s, 2.0 m / s; R2 three-pass rolling speed: 2.7 m / s second, 3.2 m / s, 4.0 m / s, respectively increased to 3.3 m / s, 4.0 m / s, 4.5 m / s).

[0022] 2. The water pressure and water volume of the cooling water of the roll body in summer are controlled at 0.8-1.0MPa; the water pressure and volume of the cooling water of the roll body in winter are 0.6-0.8MP...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a production method for reducing the temperature drop of a hot-rolled intermediate blank. Whether an R2 rolling mill finishes rolling or not is not checked before a first passand a second pass of steel feeding of an R1 rolling mill, the R1 rolling mill rolls in advance, and the time gap of the R1 rolling mill is 1-3 seconds; the pressure of roller body cooling water in arough rolling area is controlled to be 0.8-1.0 MPa in summer and 0.6-0.8 MPa in winter; in the rough rolling process, the temperature difference between the middle and the edge of the plate blank is controlled to be 20-30 DEG C; water spray on the inlet side and the outlet side of the rolling mill is changed to air spray, and the temperature difference of the cross section is controlled to be within 20 DEG C; and the abrasive width of a resin strip of a water cutting plate of the rolling mill does not exceed 20 mm. The production method has advantages that the plate blank discharging temperature is reduced, the energy consumption is saved, the cost is reduced, and the rolling stability of a machine frame and the next process is improved.

Description

technical field [0001] The invention belongs to the field of hot-rolling technology, and in particular relates to a production method for reducing the temperature drop of a hot-rolled intermediate slab. Background technique [0002] At present, the temperature drop in the rough rolling area of ​​Anshan Iron and Steel's 1580 production line is relatively large, which directly causes the slab to be released from the furnace at a higher temperature, prolongs the time in the furnace, increases gas consumption, and increases costs. The large temperature drop in the rough rolling area is mainly caused by the long rolling time, the large amount of side spray water and cooling water, and the serious water leakage in the frame. The main factor for the normal production of the line. Therefore, in order to reduce the temperature drop in the rough rolling area, reduce energy consumption, and improve the rolling stability of the finish rolling, it is of great significance to develop a p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21B37/74
CPCB21B37/74
Inventor 王存刘旺臣贺亮李江委王杰于斌马振伟
Owner ANGANG STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products