Rubber sole with oil resistance, slip resistance and antistatic effect and processing method thereof
A technology of rubber soles and processing methods, which can be applied to shoe soles, footwear, household appliances, etc., can solve problems such as poor anti-slip effect, poor oil resistance, and unsatisfactory anti-static effect, and achieve both anti-slip effect and anti-static effect Excellent, good oil resistance, scientific processing technology
Inactive Publication Date: 2019-12-24
福建省莆田市联盛鞋业有限公司
View PDF7 Cites 0 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0002] The soles of existing sports shoes generally have the problems of poor oil resistance, poor anti-slip effect, and unsatisfactory antistatic effect
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0027] A rubber sole with oil-resistant, anti-slip and antistatic functions is characterized in that the raw materials of the sole include: 35kg of nitrile rubber 220s, 5kg of butadiene rubber, 5kg of nitrile rubber 4155, 15kg of nitrile rubber N41, 15kg Silica, 1.5kg of polyethylene glycol, 8kg of antistatic agent, 5kg of lubricant, 3kg of antioxidant, 3kg of ultraviolet absorber, 2kg of polyisobutylene, 1.5kg of accelerator, 0.6kg of Stearic acid, 1.5kg of anti-wear agent, 6kg of zinc oxide, 1kg of antiozonant, 0.87kg~1.09kg of sulfur.
[0028] Such as figure 1 Shown, a kind of processing method of oil-resistant anti-slip antistatic rubber sole, this processing method specifically comprises the following steps:
[0029] Step 1. Weigh NBR 220s, cis-butadiene rubber, NBR 4155, and N41 respectively according to their weight, then mix them to form the main rubber and pour them into the internal mixer for mixing. The internal mixer must first pour Mix the main rubber, add half ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
| Property | Measurement | Unit |
|---|---|---|
| thickness | aaaaa | aaaaa |
| length | aaaaa | aaaaa |
| width | aaaaa | aaaaa |
Login to View More
Abstract
The invention relates to a rubber sole with oil resistance, slip resistance and antistatic effect and a processing method thereof. The processing method comprises the following steps: respectively weighing nitrile butadiene rubber 220s, butadiene rubber, nitrile butadiene rubber 4155 and nitrile butadiene rubber N41 by weight, mixing the components to form main rubber, and pouring the main rubberinto an internal mixer for stirring treatment for 2 minutes and then adding half of white carbon black; then adding a lubricating agent and polyethylene glycol, and continuously performing stirring treatment for 2 minutes; heating the materials to 110 DEG C, pouring the other half of the white carbon black, the antioxidant, the ultraviolet absorber, the polyisobutene, the accelerant, the stearic acid, the wear-resistant agent, the zinc oxide and the anti-ozone agent, continuously stirring the materials, heating the materials to 130 DEG C, finally adding the antistatic agent, continuously stirring the materials, and heating the materials to 135 DEG C; and after the materials are stirred well, the mixture is subjected to open milling twice through an open mill, finally outputting rubber sheets. The processing method has the characteristics that the processing technology is more scientific, and the processed rubber shoe sole is good in oil-resistant effect and excellent in anti-slip effect and antistatic effect.
Description
technical field [0001] The invention relates to a rubber sole with oil-resistant, anti-slip and antistatic functions and a processing method thereof. Background technique [0002] The soles of existing sports shoes generally have the problems of poor oil resistance, poor anti-slip effect and unsatisfactory antistatic effect. Contents of the invention [0003] In order to solve the above problems, the present invention provides a rubber sole with oil-resistant, anti-slip and anti-static functions and its processing method, which has more scientific processing technology, and the processed rubber sole has good oil-resistant effect, excellent anti-slip effect and anti-static effect. specialty. [0004] In order to achieve the above object, the present invention provides the following specific technical measures: a rubber sole with oil-resistant, anti-slip and antistatic functions, characterized in that, [0005] The raw materials of the sole include: 35kg of nitrile rubber ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/02C08L9/00C08K13/02C08K3/36C08K5/09C08K3/22C08K3/06B29C35/02A43B13/04B29L31/50
CPCA43B13/04B29C35/02B29L2031/504C08K2003/2296C08L9/02C08L2201/04C08L2205/02C08L2205/025C08L2205/035C08L9/00C08K13/02C08K3/36C08K5/09C08K3/22C08K3/06
Inventor 陈文彪林挺
Owner 福建省莆田市联盛鞋业有限公司