Method for preparing titanium-rich material for boiling chlorination with high-calcium-magnesium and low-grade titanium slag

A low-grade titanium and boiling chlorination technology, which is applied in the field of low-grade titanium slag to prepare titanium-rich materials for boiling chlorination, high calcium and magnesium, can solve the problems of industrial scale-up difficulty, upgrade difficulty, and upgradeability, and achieve improved Restore dynamics, solve upgrade difficulty or can't upgrade, high recovery rate effect

Active Publication Date: 2021-11-09
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to electric furnace smelting, only TiO can be obtained 2 High-calcium-magnesium and low-grade titanium slag products with a grade of 74% to 78% and (CaO+MgO) content as high as 6% to 10% have a dense structure and are difficult or impossible to upgrade
In the existing research, there are additives or supplementary special heating means, etc., the industrial scale-up is difficult and the energy consumption is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing titanium-rich material for boiling chlorination with high-calcium-magnesium and low-grade titanium slag
  • Method for preparing titanium-rich material for boiling chlorination with high-calcium-magnesium and low-grade titanium slag

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Weigh 200g of 40-200 mesh typical Panxi titanium slag, put it into a quartz reactor, and oxidize it at an oxidation temperature of 950°C, an oxygen concentration of 6vol.%, and an oxygen flow rate of 150L / h for 1h. After reaching the oxidation time, purge with nitrogen , then feed coke oven gas, reduce at 800°C for 1.5h, gas velocity is 130-150L / h, after the set time, feed nitrogen to cool to room temperature, then reduce titanium slag and hydrochloric acid in the digestion tank Mix evenly for acid leaching treatment, the concentration of hydrochloric acid is 20%, the liquid-solid ratio (ml:g)=2:1, the acid leaching temperature is 135°C, the acid leaching time is 6h, and the rotation speed of the digestion tank is 20r / min.

[0046] After the acid leaching treatment, the liquid-solid separation is carried out, and the washing water is washed with pure water until the washing water is clear, and finally dried in an oven at 105 ° C for 2 hours to obtain TiO 2 Grade is abou...

Embodiment 2

[0048] Weigh 200g of typical Panxi titanium slag of 40-200 mesh, put it into a quartz reactor, and oxidize it at an oxidation temperature of 1000°C, an oxygen concentration of 6vol.%, and an oxygen flow rate of 150L / h for 1.5h. After reaching the oxidation time, blow it with nitrogen. Scanning, the microscopic morphology of the oxidation product is as follows figure 1 As shown, then pass in coke oven gas, reduce at 850°C for 1.5h, the gas velocity is 130-150L / h, after the set time, pass in nitrogen to cool to room temperature, and then reduce the titanium slag in the digestion tank Mix with hydrochloric acid evenly for acid leaching treatment, the concentration of hydrochloric acid is 20%, the liquid-solid ratio (ml:g) = 2:1, the acid leaching temperature is 145°C, the acid leaching time is 6h, and the speed of the digestion tank is 20r / min.

[0049] After the acid leaching treatment, the liquid-solid separation is carried out, and the washing water is washed with pure water u...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of metallurgy and chemical industry, and in particular relates to a method for preparing titanium-rich material for boiling chlorination from high-calcium-magnesium and low-grade titanium slag. The method for preparing titanium-rich material for boiling chlorination with high-calcium-magnesium and low-grade titanium slag of the present invention comprises the following steps: (1) drying and screening the titanium slag; (2) drying the titanium concentrate at 950-1000°C Carry out high-temperature strong oxidation reaction; (3) then carry out weak reduction reaction at 800-850 °C; (4) add hydrochloric acid, pressurize leaching under heating and rotating conditions; (5) separate solid and liquid, wash and dry to obtain rich Finished titanium. The invention can successfully process high-calcium-magnesium and low-grade titanium slag similar to Panzhihua, and upgrade it to prepare high-quality titanium-rich raw materials that meet the needs of boiling chlorination, which is of great significance for the utilization of Panxi's complex titanium resources and the development of chlorinated titanium white .

Description

technical field [0001] The invention belongs to the field of metallurgy and chemical industry, and in particular relates to a method for preparing titanium-rich material for boiling chlorination from high-calcium-magnesium and low-grade titanium slag. Background technique [0002] my country's Panxi ilmenite concentrate belongs to low-grade ilmenite ore with high calcium and magnesium content. The ways to prepare titanium-rich materials can be summarized into two categories. The fine-grained grade of the concentrate accounts for a relatively large proportion, and the obtained artificial rutile product has a finer particle size, which does not meet the requirements of boiling chlorination raw materials. The second category is to smelt titanium slag in an electric furnace with titanium concentrate, crush the titanium slag to a suitable particle size, and then upgrade the process route to prepare PUS slag, successfully solving the problem of fine titanium concentrate raw materia...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B34/12C22B7/04C22B1/00
CPCC22B1/005C22B7/007C22B7/04C22B34/1209C22B34/1245Y02P10/20
Inventor 刘娟叶恩东肖军李凯茂
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com