Processing technology of antibacterial aerated brick

A processing technology and technology of aerated bricks, used in applications, household appliances, ceramic products, etc., can solve the problem that aerated bricks do not have antibacterial functions, and achieve good bacteriostatic effect, increase compressive strength, and inhibit mold.

Inactive Publication Date: 2020-01-17
贵州彬腾越新型建材有限公司
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention intends to provide an antibacterial aerated brick to solve the problem that the aerated bricks in the prior art do not have antibacterial function

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing technology of antibacterial aerated brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1, a kind of processing technology of antibacterial aerated brick, comprises the following steps:

[0021] 1) Weigh 70 parts of fly ash, 15 parts of quicklime, 10 parts of cement, 10 parts of gypsum, 9 parts of aluminum powder paste, 8 parts of montmorillonite powder, 6-8 parts of traditional Chinese medicine slag, and 5 parts by weight of steel fiber 12 parts by weight of copper-containing aluminum phosphate, wherein Chinese medicinal dregs contain Coptidis Rhizome, Scutellaria baicalensis and clove, the content of these three Chinese medicinal ingredients in medicinal dregs is more than 30%, and the diameter of steel fibers is 0.08-0.2mm;

[0022] 2) Mix coal ash, quicklime, cement, gypsum, montmorillonite powder, and steel fiber, then add water, mix evenly, add aluminum powder paste to obtain slurry,

[0023] 3) Inject the stirred slurry into the mould, then put it into the resting room and seal it at 55-60°C for heat preservation, resting for 1.8-2 hours,...

Embodiment 2

[0026] Embodiment 2, a kind of processing technique of antibacterial aerated brick, comprises the following steps:

[0027] 1) Weigh 60 parts of fly ash, 10 parts of quicklime, 10 parts of cement, 5 parts of gypsum, 8 parts of aluminum powder paste, 5 parts of montmorillonite powder, 6-8 parts of traditional Chinese medicine slag, and 3 parts by weight of steel fiber 10 parts by weight of copper-containing aluminum phosphate, wherein the traditional Chinese medicine residue contains star anise and rhubarb, the content of these two traditional Chinese medicine ingredients in the medicinal residue is more than 40%, and the diameter of the steel fiber is 0.08-0.2mm;

[0028] 2) Mix coal ash, quicklime, cement, gypsum, montmorillonite powder, and steel fiber, then add water, mix evenly, add aluminum powder paste to obtain slurry,

[0029] 3) Inject the stirred slurry into the mould, then put it into the resting room and seal it at 55-60°C for heat preservation, resting for 1.8-2 h...

Embodiment 3

[0032] Embodiment 3, a kind of processing technology of antibacterial aerated brick, comprises the following steps:

[0033] 1) Weigh 80 parts of fly ash, 15 parts of quicklime, 15 parts of cement, 12 parts of gypsum, 9 parts of aluminum powder paste, 8 parts of montmorillonite powder, 6-8 parts of traditional Chinese medicine slag, and 6 parts by weight of steel fiber 12 parts by weight of copper-containing aluminum phosphate, wherein the dregs of traditional Chinese medicines contain Coptis chinensis, Scutellaria baicalensis and rhubarb, the content of these three traditional Chinese medicine ingredients in the dregs of Chinese medicines is more than 30%, and the diameter of the steel fibers is 0.08-0.2mm;

[0034] 2) Mix coal ash, quicklime, cement, gypsum, montmorillonite powder, and steel fiber, then add water, mix evenly, add aluminum powder paste to obtain slurry,

[0035] 3) Inject the stirred slurry into the mould, then put it into the resting room and seal it at 55-6...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a processing technology of an antibacterial aerated brick in the technical field of production of novel environment-friendly building materials. and parts by weight of the rawmaterials are as follows. The concrete is prepared from the following raw materials by weight: 60-90 parts of fly ash, 10-20 parts of quick lime, 10-15 parts of cement, 5-15 parts of gypsum, 8-10 parts of aluminum powder paste, 5-10 parts of montmorillonite powder and 6-8 parts of traditional Chinese medicine residues, wherein the traditional Chinese medicine residues are residues containing one or more of coptis chinensis, scutellaria baicalensis, clove, anise or rheum officinale, the content of the traditional Chinese medicines is greater than 30%, and the water-to-material ratio is 0.6-0.7.The montmorillonite powder and the traditional Chinese medicine residues are arranged in the aerated brick, copper-containing aluminum phosphate and silicon dioxide colloid form a coating which is attached to the outer part of the aerated brick, namely the inner part and the outer part, and due to the montmorillonite powder and the traditional Chinese medicine residues arranged in the aerated brick and the coating attached to the outer part of the aerated brick, the antibacterial effect is better.

Description

technical field [0001] The invention relates to the technical field of production of environmentally friendly new building materials, in particular to a processing technology of an antibacterial aerated brick. Background technique [0002] Aerated brick is a new type of environmentally friendly building material that is lightweight, porous, thermally insulated, good in fire resistance, can be nailed, sawed, planed, and has a certain earthquake resistance; it is widely used, mainly in mechanical workshops and civil buildings Wall materials, infill walls, load-bearing wall materials such as floor and roof slabs, as well as non-load-bearing materials and surrounding infill enclosures. With the national ban on clay solid bricks, aerated bricks have become the leading product in the building materials industry. But the aerated bricks of the prior art do not just have the antibacterial function. Contents of the invention [0003] The present invention intends to provide an ant...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B38/02C04B28/00C04B40/02
CPCC04B28/00C04B40/024C04B2111/20C04B2111/40C04B2201/50C04B18/08C04B22/064C04B22/143C04B18/24C04B14/104C04B22/04C04B22/16C04B14/48C04B38/02
Inventor 张波严伟
Owner 贵州彬腾越新型建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com