Porcelain firing process combining celadon and Jianzhan

A celadon and craft technology, applied in the production of clay products, drinking utensils, ceramic materials, etc., can solve problems such as difficult to combine, no porcelain is found, and achieve stable color, good flammability, and shiny and full oil droplets. Effect

Active Publication Date: 2022-02-11
南平市建阳区兰亭叙建盏陶瓷有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Porcelain is extremely difficult to combine due to the limitation of blank, glaze composition and firing process. At present, there is no porcelain made by combining celadon and Jianzhan process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Porcelain firing process combining celadon and Jianzhan
  • Porcelain firing process combining celadon and Jianzhan
  • Porcelain firing process combining celadon and Jianzhan

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] The porcelain firing process combining celadon and Jianzhan includes the following steps:

[0041] (1) Prepare green body raw materials, Jianzhan glaze slurry, celadon glaze slurry, wherein,

[0042] The green body raw material is prepared by the following method: mixing 7 parts by weight of kaolin, 1 part by weight of field mud and 3 parts by weight of red mud, crushing, elutriating, grinding, passing through a 90-mesh sieve, press filtration, mud refining, After aging for one year, the raw material of the green body is obtained;

[0043] The Jianzhan glaze slurry is prepared by the following method: mix 5 parts by weight of glaze ore, 3 parts by weight of plant ash, 2 parts by weight of field mud, and 0.3 parts by weight of iron red, add 3.5 times by weight of water and put it into a ball mill Grind and pass through a 90-mesh sieve to obtain Jianzhan glaze slurry;

[0044] The celadon glaze slurry is prepared by the following method: take 65 parts by weight of ridge...

Embodiment 2

[0062] The porcelain firing process combining celadon and Jianzhan includes the following steps:

[0063] (1) Prepare green body raw materials, Jianzhan glaze slurry, celadon glaze slurry, wherein,

[0064] The green body raw material is prepared by the following method: mixing 6 parts by weight of kaolin, 2 parts by weight of field mud and 4 parts by weight of red mud, crushing, elutriating, grinding, passing through a 80-mesh sieve, press filtration, mud refining, After aging for one year, the raw material of the green body is obtained;

[0065] The Jianzhan glaze slurry is prepared by the following method: mix 4 parts by weight of glaze ore, 3 parts by weight of plant ash, 2 parts by weight of field mud, and 0.3 parts by weight of iron red, add 3 times the weight of water and put it into a ball mill Grind and pass through an 80-mesh sieve to obtain Jianzhan glaze slurry;

[0066] The celadon glaze slurry is prepared by the following method: take 70 parts by weight of ridg...

Embodiment 3

[0082] The porcelain firing process combining celadon and Jianzhan includes the following steps:

[0083] (1) Prepare green body raw materials, Jianzhan glaze slurry, celadon glaze slurry, wherein,

[0084] The green body raw material is prepared by the following method: mixing 8 parts by weight of kaolin, 1 part by weight of field mud and 2 parts by weight of red mud, crushing, elutriating, grinding, passing through a 100-mesh sieve, pressure filtration, mud refining, After aging for one year, the raw material of the green body is obtained;

[0085] The Jianzhan glaze slurry is prepared by the following method: mix 6 parts by weight of glaze ore, 3.5 parts by weight of plant ash, 3 parts by weight of field mud, and 0.2 parts by weight of iron red, add 3 times by weight of water and put it into a ball mill Grind and pass through a 100-mesh sieve to obtain Jianzhan glaze slurry;

[0086] The celadon glaze slurry is prepared by the following method: take 60 parts by weight of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a porcelain firing process combining celadon and Jianzhan, which comprises the following steps: preparing body raw materials, Jianzhan glaze slurry, and celadon glaze slurry; drawing the body raw materials into a cup shape, repairing the blank, and engraving patterns on the outside of the cup , biscuit firing, and cooling to obtain the green body; glaze; put the glazed and dried green body into the electric kiln for roasting, stop the furnace, cool down naturally, and leave the kiln. The present invention combines Longquan celadon with Jianzhan technology, and the inside of the cup and the rim of the prepared porcelain cup are Jianzhan glaze, and the outside of the cup is celadon glaze with engraved patterns. The combination of celadon and Jianzhan breaks through the traditional porcelain Restricted by species, it has a strong sense of visual impact and artistic beauty, and is a milestone in the field of porcelain.

Description

technical field [0001] The invention relates to the technical field of porcelain, in particular to a porcelain firing process combining celadon and Jianzhan. Background technique [0002] Jianzhan is a representative of black porcelain, one of the eight famous porcelains in the Song Dynasty in China, and was used by the royal family in the Song Dynasty. In the middle and late Yuan Dynasty, with the chaos of war and changes in social fashion, Jianyao Jianzhan tended to decline, and in the following hundreds of years, the firing skills of Jianyao Jianzhan were on the verge of being lost. After the reform and opening up, the 800-year-old Jianzhan firing technique has been restored and developed. [0003] Celadon is a traditional porcelain treasure of the Han nationality in China, among which Longquan celadon is well-known. People describe Longquan celadon as "quality like jade, bright as mirror, and sound like chime". Longquan celadon has the advantages of fine and tough text...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/24C04B33/04C04B33/132C04B33/34C03C8/00A47G19/22
CPCC04B33/04C04B33/1321C04B33/1322C04B33/24C04B33/34C03C8/00A47G19/2205Y02P40/60
Inventor 李光熙
Owner 南平市建阳区兰亭叙建盏陶瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com