Optical glass

A kind of optical glass and optical technology, applied in the direction of glass production, etc., can solve the problems of poor chemical durability, surface corrosion of glass parts, unfavorable processing, etc.

Active Publication Date: 2020-02-28
CDGM OPTICAL GLASS
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Optical glass for precision stamping usually has the disadvantage of poor chemical durability, which is not conducive to subsequent processing and even affects the quality of the glass
For optical glass with poor chemical durability, in the subsequent polishing and cleaning process, measures such as protective coating need to be taken, and the yield rate is low, which increases the process and cost
If the weather resistance level of the glass is low, the surface of the polished glass is easily corroded by water vapor in the air and scrapped during cleaning, drying, transportation, etc.
[0004] For example, patent CN200610021577.6 provides an environmentally friendly optical glass. By adjusting the component distribution ratio, an optical glass with ideal optical constants can be obtained without introducing elements such as Pb, As, and Cd that are harmful to the environment. However, Little contribution to the chemical resistance and durability of optical glass, especially the weather resistance
[0005] For example, patent CN108975687A provides an optical glass with high SiO 2 Content (50% ~ 65%) optical glass formula, so the meltability is poor, and in order to ensure good meltability, it is necessary to increase the melting temperature, which is not conducive to improving the light transmittance of the glass

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Optical glass
  • Optical glass
  • Optical glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0047] The composition range of each component of the optical glass of the present invention will be described below with reference to the examples. In this specification, unless otherwise specified, the content of each component is expressed in weight percent (wt %) relative to the total amount of glass substances converted into oxides. Here, the "composition in terms of oxides" refers to the case where oxides, composite salts, hydroxides, etc. used as raw materials for the optical glass composition of the present invention are decomposed and converted into oxides during melting , and the total amount of the oxide was taken as 100%.

[0048] Unless otherwise indicated in a specific instance, the numerical ranges set forth herein include the upper and lower values, "above" and "below" include the endpoints, all integers and fractions within the range, and are not intended to be limiting when the range is defined specific values ​​listed. The term "and / or" herein is inclusive...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Transition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses optical glass which comprises the following components in percentage by weight: 28%-42% of SiO2, 5%-18% of ZnO, 26%-48% of RO, 0-10% of TiO2, and 0-10% of ZrO2, wherein RO is one or more selected from MgO, CaO, SrO and BaO. According to the invention, the formula and the proportioning relationship are optimized, without adding other expensive metals, the content of SiO2 isremarkably reduced, the proportioning relationship of all the components is optimized, the moisture resistance stability, weather resistance and acid resistance of the optical glass are remarkably improved, and particularly, the moisture resistance stability and weather resistance of the optical glass can reach first-class standards; meanwhile, the optical glass also has a good optical constant.

Description

technical field [0001] The invention relates to the technical field of environmental protection optical glass, in particular, the invention relates to optical glass and optical preforms, optical elements and optical instruments made of the optical glass. Background technique [0002] The lenses that make up the optical system usually have spherical lenses and aspheric lenses. A spherical lens has a constant curvature from the center to the edge of the lens, while an aspheric lens has a curvature that changes continuously from the center to the edge; as in a photographic lens , in order to ensure optical performance, numerous "aberrations" must be corrected. If only spherical lenses are used for correction, the corresponding lens technology requires many lens combinations. Aspherical lenses can improve optical quality, reduce optical components, and reduce design costs. Compared with spherical lenses, aspheric lenses have unique advantages, so they are widely used in optical ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C3/062C03C3/078
CPCC03C3/062C03C3/078Y02P40/57
Inventor 匡波孙伟
Owner CDGM OPTICAL GLASS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products