A foam rubber and a manufacturing method technology, applied in the foam rubber manufacturing field, can solve the problems of poor elasticity and durability of the puff, and achieve the effect of excellent elasticity and durability

Active Publication Date: 2020-03-24
ZEON CORP
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in the technique of this patent document 1, the puff obtained may be poor in elasticity and durability against moisture such as water-based cosmetics.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing foam rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0109] Manufacture of polymer latex

[0110] Add 200 parts of water, 1.5 parts of potassium oleate, 38 parts of acrylonitrile, 0.5 parts of tert-dodecyl mercaptan, 0.03 parts of sodium formaldehyde sulfoxylate, 0.003 parts of ferrous sulfate, 0.008 parts of ethylene glycol in a pressure-resistant reaction vessel Sodium amine tetraacetate was fully degassed, and 45 parts of 1,3-butadiene and 17 parts of isoprene were added.

[0111] Next, 0.05 part of cumene hydroperoxide was added as a polymerization initiator to initiate emulsion polymerization at a reaction temperature of 5°C. When the polymerization conversion rate reached 95%, a polymerization terminator solution containing 0.25 parts of diethylhydroxylamine and 5 parts of water was added to terminate the polymerization reaction to obtain an emulsion.

[0112]Then, after removing unreacted monomers from the obtained emulsion, 0.02 part of modified hydrocarbon oil based on mineral oil (trade name "DF714S", manufactured b...

Embodiment 2

[0119] The usage amount of the antifoaming agent was changed from 0.02 part to 0.1 part, and the conditions of the particle size increasing treatment were changed to a rotation speed of 900 rpm and a stirring time of 4.5 hours, except that, it was carried out in the same manner as in Example 1 to produce a polymer latex The polymer latex and the foam rubber were evaluated in the same manner as the foam rubber. In addition, in Example 2, the solid content concentration of the polymer latex after the concentration treatment was 66.0% by weight. The results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

Provided is a method for manufacturing a foam rubber by foaming a polymer latex, wherein the method for manufacturing a foam rubber uses, as said polymer latex, a polymer latex in which the concentration of solid content is 60.0 wt% or more; the content of an antifoaming agent is 0.001-1.0 parts by weight with respect to 100 parts by weight of a polymer in said polymer latex; and the viscosity ata temperature of 25 DEG C is 370 cps or less when the concentration of solid content is adjusted to 66.0 wt%.

Description

technical field [0001] The present invention relates to a method for producing foam rubber capable of appropriately controlling foaming and excellent in elasticity and durability. Background technique [0002] Foam rubber (rubber foam) produced using polymer latex is used in various applications such as mattresses, powder puffs (cosmetic sponges), rollers, and shock absorbers. In the use of such foam rubber, particularly as foam rubber for puffs, it is required to have a good foam state, a uniform foam structure, and an excellent balance of elasticity and texture. [0003] For example, Patent Document 1 discloses a method of producing a puff using a copolymer latex whose solid content concentration, gel content, and Mooney viscosity are controlled within specific ranges. However, according to the technique of this patent document 1, the obtained puff may have poor elasticity and durability against moisture such as water-based cosmetics. [0004] prior art literature [00...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08J9/228
CPCC08J2309/04C08J2201/026C08J9/30C08J9/228
Inventor 谷山友哉羽根田英和
Owner ZEON CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap