Carbon fiber sizing agent and preparation methods thereof

A carbon fiber and carbon fiber tow technology, which is applied in the field of carbon fiber sizing agent and its preparation, can solve the problems of high molding cost of carbon fiber composite materials, low molding efficiency of carbon fiber composite materials, etc., so as to reduce investment in fixed assets, realize manufacturability, and reduce molding. effect of time

Active Publication Date: 2020-04-14
北京鸿羽腾风材料科技有限公司 +1
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The invention solves the problem of low molding efficiency of carbon fiber composite materials
The invention solves the problem of high molding cost of carbon fiber composite materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Carbon fiber sizing agent and preparation methods thereof
  • Carbon fiber sizing agent and preparation methods thereof
  • Carbon fiber sizing agent and preparation methods thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0044] In the following, the present invention will be further described in conjunction with the embodiments. However, the scope of the present invention is not limited to the following examples. Those skilled in the art can understand that various changes and modifications can be made to the present invention without departing from the spirit and scope of the present invention.

[0045] The present invention provides a general and / or specific description of the materials and test methods used in the test. Although many materials and operating methods used to achieve the purpose of the present invention are well known in the art, the present invention is still described here in as much detail as possible.

[0046] The instruments, reagents, materials, etc. involved in the following embodiments, unless otherwise specified, are all conventional instruments, reagents, materials, etc. that exist in the prior art and can be obtained through formal commercial channels. The experimental...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a carbon fiber sizing agent. The carbon fiber sizing agent is prepared from the following raw materials, a water-based bisphenol A epoxy resin, polyether alcohol, unsaturated acid and water, wherein the weight ratio of the water-based bisphenol A epoxy resin to the polyether alcohol to the unsaturated acid is 1: 0.5 to 5: 0.4 to 5. The polyether alcohol is selected from dimethyl trimer dimethanol; and the unsaturated acid is selected from acrylic acid. The invention also discloses three preparation methods of the carbon fiber sizing agent. The invention also discloses application of the carbon fiber sizing agent in preparation of carbon fibers and carbon fiber composite materials, and the prepared carbon fibers and carbon fiber composite materials. The carbon fibertreated by the sizing agent can be soaked by the polyester resin, so that the carbon fiber can obtain manufacturability similar to glass fiber, and the forming time of the carbon fiber composite material can be greatly reduced, the fixed asset investment of carbon fiber composite material forming equipment is reduced, and the low-cost and quick forming of the carbon fiber composite material are realized.

Description

Technical field [0001] The invention relates to a carbon fiber sizing agent and a preparation method thereof, belonging to the field of carbon fiber and carbon fiber composite materials. Background technique [0002] Resin-based composite materials are fiber-reinforced materials based on organic polymers, and fiber-reinforced materials such as glass fiber, carbon fiber, basalt fiber, or aramid are usually used. Resin-based composite materials are widely used in aviation, automotive, and marine industries. The commonly used resins for fiber-reinforced resin-based composites are epoxy resin and unsaturated polyester resin. The commonly used resins are thermosetting resins, thermoplastic resins, and various modified or blended matrixes. The molding process of the fiber-reinforced resin-based composite material is as follows: the resin first infiltrates the fiber, after the fiber is infiltrated, the resin undergoes cross-linking reaction and solidifies, and the composite material is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/55D06M13/224C08J5/06D06M101/40
CPCC08J5/06D06M13/2246D06M15/55D06M2101/40
Inventor 靳普陈宗良
Owner 北京鸿羽腾风材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap