Sharp type diamond drill bit for dry-drilling of granite
A diamond drill and granite technology, applied in the field of powder metallurgy, can solve the problems of slow cutting speed and affecting processing efficiency, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0015] A diamond drill bit, which uses ultrafine tungsten-copper alloy powder, copper-tin alloy powder, ultrafine iron powder, carbonyl nickel powder, phosphor copper powder, silver powder, and diamond as raw materials,
[0016] Among them, the superfine tungsten-copper alloy powder contains 70% tungsten and 30% copper by mass fraction, and the Fischer grain size is less than 2.5 μm; the copper-tin alloy powder contains 80% copper by mass fraction, contains 20% tin, and the Fischer grain size is less than 30 μm. The weight percentage of phosphorus in the phosphor bronze powder is 20%, and the Fischer particle size is less than 40 μm;
[0017] The weight percent composition of above raw material is:
[0018] Ultra-fine tungsten-copper alloy powder 30%-45%, copper-tin pre-alloy powder 25%-45%, ultra-fine iron powder 10%-20%, carbonyl nickel powder 5%-15%, phosphor copper powder 5%-10% , silver powder 1%-5%, the concentration of diamond is 15%-50% (according to 400%), and the pa...
Embodiment 2
[0034] Take 3kg of ultra-fine tungsten-copper alloy powder, 4kg of copper-tin alloy powder, 1kg of ultra-fine iron powder, 1kg of carbonyl nickel powder, 0.8kg of phosphor copper powder, and 0.2kg of silver powder, put them into the mixing tank, and mix them for 3 hours , then add 300g of 350-450μm diamond and continue mixing for 3 hours. Then add the mixed powder into granulating agent to make granules, and carry out drying treatment. Weigh a certain weight of the mixed powder and put it into the assembled compression mold cavity equipped with a cold compression mold. Pressing to obtain a cold-pressed blank, the pressing pressure is 50-150MPa. Then put the blank into a graphite mold and put it in a hot-press sintering furnace for sintering. At a sintering temperature of 880°C and a pressure of 35MP for a holding time of 8 minutes, after cooling and demoulding, a diamond cutter tooth is produced. The hardness of the cutter head is HRB95-100, and then ground arc treatment, and...
PUM
Property | Measurement | Unit |
---|---|---|
Fisherman's particle size | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Granularity | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap