Blue glaze and preparation method thereof

A technology of Qilan glaze and glaze, which is applied in the field of Qilan glaze and its preparation, can solve the problems that are not involved in the production of Jilan glaze and the research on process restoration, and the preparation process of unseen Chenghua Jilan glaze, etc., and achieve smoothness and heat Good stability, wide range of firing, uniform thickness

Inactive Publication Date: 2020-06-12
景德镇市乐陶陶瓷原料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, it does not involve research on the production and process restoration of Jilan glaze
In addition, there is no relevant report on the preparation process of Chenghua Jilan glaze

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A Qilan glaze is composed of the following raw materials: 44.9% albite, 22.6% quartz powder, 9.1% kaolin, and 23.4% wollastonite.

Embodiment 2

[0027] A Qilan glaze is composed of the following raw materials: 47.8% albite, 21.3% quartz powder, 8.8% kaolin, and 22.1% wollastonite.

Embodiment 3

[0029] A Qilan glaze is composed of the following raw materials: 42.8% albite, 23.2% quartz powder, 11.1% kaolin, and 22.9% wollastonite.

[0030] The present invention also provides a preparation method for preparing the above-mentioned Qilan glaze, comprising the following steps:

[0031] S1, weigh raw materials according to the above ratio;

[0032] S2. Pour the raw materials weighed in step S1 into a ball mill tank for ball milling;

[0033] S3, filtering, filtering the ball-milled raw materials through an ultrafine screen, and mixing the filtered raw materials;

[0034] S4. Add water and mix thoroughly according to the component requirements.

[0035] In this embodiment, in the step S2, each raw material needs to be finely ground for 18-21 hours during the ball milling treatment.

[0036] In this embodiment, in the step S2, during the ball milling process, the ball:material=2:1.

[0037] In this embodiment, in the step S3, the mesh of the ultrafine screen used in the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a blue glaze and a preparation method thereof. The blue glaze is prepared from, by weight, 40-48% of albite, 18-25% of quartz powder, 8-12% of kaolin and 21-25% of wollastonite. The glaze enables a porcelain fired by the glaze to be dark in color and luster, uniform in concentration, stable in color generation, non-flowing and non-cracking in glaze surface, smooth in hand feeling, durable, wear-resistant, good in smoothness and thermal stability, wide in firing range, suitable for medium-temperature oxidizing atmosphere and high-temperature reducing atmosphere and suitable for wide popularization.

Description

technical field [0001] The invention relates to the technical field of glazes, in particular to a Qilan glaze and a preparation method thereof. Background technique [0002] Treasures of traditional Chinese porcelain making crafts. Also known as "accumulating blue glaze", "sacrificing blue glaze" and "ji blue glaze". Both Ming and Qing blue glazes are called "Ji blue", a kind of high temperature lime alkali glaze. The green body is glazed and fired at high temperature for the first time. The color is deep, the glaze does not flow or crack, the color tone is uniform, and the color is relatively stable. Its glaze color is as blue as the deep sea, the glaze surface is even and stable, and later generations call it "Jiqing". Because of its stable and bright color like gemstones, it is also regarded as juxtaposed with white glaze and red glaze. The three "top grades" of Xuande color glaze porcelain. The craftsmanship inherits the tradition of the Yuan Dynasty, and the firing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86
Inventor 黄伟友
Owner 景德镇市乐陶陶瓷原料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com