Full-automatic galvanizing process for neodymium iron boron

A kind of NdFeB, fully automatic technology, applied in the cleaning method of using tools, chemical instruments and methods, cleaning methods and utensils, etc., can solve the problems that employees cannot adapt, increase labor costs, and inconvenient management, so as to prevent contact with acid opportunities, increase production automation, and reduce possible effects of acid allergies

Inactive Publication Date: 2020-06-23
SINO MAGNETICS TECH
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, electro-galvanizing is all manual operation, and the randomness of manual operation in the production process is relatively large, resulting in large fluctuations in product quality consistency; there are many operators, and management is difficult; there are many operators, and the labor cost of the workshop increases; the manual operation site is chaotic, Inconvenient management
The electroplating process uses chemical products, and many employees cannot adapt to it, and even cause severe allergies

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Full-automatic galvanizing process for neodymium iron boron
  • Full-automatic galvanizing process for neodymium iron boron

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0020] The specific embodiments of the present invention will be described in detail below with reference to the accompanying drawings, but it should be understood that the protection scope of the present invention is not limited by the specific embodiments.

[0021] Unless otherwise expressly stated otherwise, throughout the specification and claims, the term "comprising" or its transformations such as "including" or "including" will be understood to include the stated elements or components, and not Other elements or other components are not excluded.

[0022] Such as figure 1 As shown, the NdFeB automatic galvanizing process according to the preferred embodiment of the present invention includes the following steps: Step 101: Loading materials to be galvanized NdFeB products, and giving a signal when the materials are loaded, the automatic galvanizing process Start; Step 102: Use 2% HNO3 solution for automatic pickling; Step 103: Perform ash removal treatment on the product afte...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a full-automatic galvanizing process for neodymium iron boron. The process comprises the following steps of: feeding a galvanized neodymium iron boron product, and starting anautomatic galvanizing process when a material is loaded and a signal is given; and carrying out automatic pickling for 30s by 2%HNO3 solution; carrying out ash removal to the product after automatic pickling, wherein the ash removal is carried out by roller ash removal; first secondary backflow washing is carried out to the product after ash removal; a first secondary backflow washing product is electrogalvanized, and the electroplating zinc uses potassium chloride electroplating solution to obtain the galvanized neodymium iron boron product; the galvanized neodymium iron boron product is polished; automatic passivation treatment is carried out to the polished neodymium iron boron product; and a second secondary backflow washing is carried out to a passivation product.

Description

Technical field [0001] The invention relates to the technical field of electro-galvanization, in particular to a neodymium-iron-boron automatic galvanizing process. Background technique [0002] Neodymium iron boron magnets are tetragonal crystals formed by neodymium, iron and boron. Neodymium iron boron magnets are permanent magnets with magnetic properties second only to absolute zero holmium magnets, and they are also the most commonly used rare earth magnets. NdFeB magnets are widely used in electronic products, such as hard drives, mobile phones, earphones, and battery-powered tools. NdFeB electroplating adopts different electroplating processes according to the use environment of the product. The surface coating is also divided into two categories, one is galvanized, used for conventional products; the other is nickel-plated, used for higher requirements The product. There are also a few products that require other plating types, such as alloy plating, silver plating, et...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C25D7/00C25D5/52C25D5/48C25D5/34C25D3/22C23G1/02B08B3/10B08B3/04B08B1/04
CPCC25D7/001C25D3/22C25D5/34C25D5/52C25D5/48C23G1/02B08B3/041B08B3/10B08B1/32
Inventor 邵江龙马江
Owner SINO MAGNETICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com