Metal wiredrawing composite steel plate and preparation method thereof

A clad steel plate and metal wire drawing technology, applied in the field of metal clad steel plates, can solve the problems of complex lamination process and high production cost, and achieve the effects of low production cost, convenient operation and good application prospect.

Inactive Publication Date: 2012-05-09
SUZHOU HESHENG NEW MATERIALS
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] At present, the imitation stainless steel wire drawing sheets used for home appliance panels include PET/Al/PVC composite steel sheets, PET printed wire drawing composite steel sheets and PET real wire drawing composite steel sheet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Metal wiredrawing composite steel plate and preparation method thereof
  • Metal wiredrawing composite steel plate and preparation method thereof
  • Metal wiredrawing composite steel plate and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] The base material is hot-dip galvanized steel plate with a thickness of 0.4mm;

[0028] The front side of the base material is processed by the metal surface wire drawing machine. The metal surface wire drawing machine is equipped with two sets of differential rollers rotating in the same direction. The upper roller is a fast-rotating grinding roller, and the lower roller is a slow-speed transfer rubber Roller, the substrate is conveyed through two sets of rollers, and the fine straight grain drawing is processed on the front of the substrate by mechanical friction;

[0029] Degrease and clean the substrate treated by the wire drawing process to remove surface oil stains and dry it at 50°C;

[0030] After degreasing and cleaning, the surface passivation treatment is carried out by spraying. The passivation agent used in the passivation treatment is Aldoine 5200, a chromium-free passivation agent from Henkel, to form a colorless paint-based passivation film on the front ...

Embodiment 2

[0035] The base material is hot-dip galvanized steel plate with a thickness of 0.4mm;

[0036] The front side of the base material is processed by the metal surface wire drawing machine. The metal surface wire drawing machine is equipped with two sets of differential rollers rotating in the same direction. The upper roller is a fast-rotating grinding roller, and the lower roller is a slow-speed transfer rubber Roller, the substrate is conveyed through two sets of rollers, and the fine straight grain drawing is processed on the front of the substrate by mechanical friction;

[0037] Degrease and clean the substrate treated by the wire drawing process to remove surface oil stains and dry at 60°C;

[0038] After degreasing and cleaning, the surface passivation treatment is carried out by spraying. The passivation agent used in the passivation treatment is Aldoine 5200, a chromium-free passivation agent from Henkel, to form a colorless paint-based passivation film on the front and...

Embodiment 3

[0043] The base material is hot-dip galvanized steel plate with a thickness of 0.5mm;

[0044] The front side of the base material is processed by the metal surface wire drawing machine. The metal surface wire drawing machine is equipped with two sets of differential rollers rotating in the same direction. The upper roller is a fast-rotating grinding roller, and the lower roller is a slow-speed transfer rubber Roller, the substrate is conveyed through two sets of rollers, and the fine straight grain drawing is processed on the front of the substrate by mechanical friction;

[0045] Degrease and clean the substrate treated by the wire drawing process, remove surface oil stains, and dry at 50°C;

[0046] After degreasing and cleaning, the surface passivation treatment is carried out by spraying. The passivation agent used in the passivation treatment is Aldoine 5200, a chromium-free passivation agent from Henkel, to form a colorless paint-based passivation film on the front and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a metal wiredrawing composite steel plate and a preparation method thereof. A base material of the metal wiredrawing composite steel plate is a hot galvanizing steel plate or an electro-galvanizing steel plate, a straight grain wiredrawing structure is formed on the front side of the base material through wiredrawing by using a metal surface wiredrawing machine, and a transparent fingerprint-resistant paint layer is formed on the straight grain wiredrawing structure through roller coating. During manufacturing, the method comprises the following steps of: performing wiredrawing process treatment on the front side of the base material by using the metal surface wiredrawing machine; performing degreasing cleaning on the base material subjected to the wiredrawing process treatment to remove oil stains on the surface; performing surface passivation in a sprinkling mode after the degreasing cleaning to form colorless paint bottom passive films on the front side and the back side of the base material, and drying in a drying oven; painting a back paint on the back side of the base material through roller coating at normal temperature after the passivation, and drying in the drying oven; painting a transparent fingerprint-resistant paint on the front side of the base material which is subjected to wiredrawing, degreasing cleaning and passivation; and coating a protective film on the surface of the transparent fingerprint-resistant paint layer. By directly treating the hot galvanizing steel plate or electro-galvanizing steel plate by using a wiredrawing process, and coating a transparent paint layer on the hot galvanizing steel plate or electro-galvanizing steel plate, an appearance effect of imitation stainless steel is achieved.

Description

technical field [0001] The invention relates to a metal composite steel plate, in particular to a metal wire drawing composite steel plate and a preparation method thereof. Background technique [0002] Steel plates are widely used in industry and life, such as automobiles, refrigerators, washing machines, high-end furniture, cabinet equipment, industrial and civil buildings and other fields. The general steel plate can only be used as a final product after being coated with a protective layer or a decorative layer on its surface, mostly after it is made into a product or a semi-finished product, so it brings a lot of inconvenience to the manufacturer and manufacturer. [0003] PET / PVC composite steel plate is a newly developed product in the mid-1990s, which has good properties such as moisture resistance, corrosion resistance, and durability. The color laminated steel plate composited with PET / PVC composite film and steel plate has beautiful appearance, surface decoration...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B44C5/04B44F9/10B32B15/04B32B33/00B23P9/02
Inventor 汪倩文赵东明
Owner SUZHOU HESHENG NEW MATERIALS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap