Polycarbonate styrene resin alloy and preparation method thereof

A technology of styrenic resin and polycarbonate resin, which is applied in the field of polycarbonate styrenic resin alloy and its preparation, can solve the problems of small size, reduced gloss, and limited number of cross-linked products, and achieves excellent results. , The degree of gloss reduction is large, and the effect of solving the insufficient degree of extinction

Active Publication Date: 2020-06-30
SHANGHAI KUMHO SUNNY PLASTICS
View PDF9 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the number of cross-linked products generated by this method of directly adding a cross-linking agent is limited and the size is small, so the range of reducing gloss is limited, and the gloss that can only be achieved is 2.9-7.6

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polycarbonate styrene resin alloy and preparation method thereof
  • Polycarbonate styrene resin alloy and preparation method thereof
  • Polycarbonate styrene resin alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0043] The preparation method of above-mentioned ultra-low luster polycarbonate styrenic resin alloy comprises the following steps:

[0044] (1) prepare materials according to the components and content;

[0045] (2) Premix the materials prepared in step (1) in a high-speed mixer for 3-10 minutes;

[0046] (3) Pass the premixed material obtained in step (2) through a twin-screw extruder, perform melt extrusion at 230-280°C, cool and granulate, and obtain an ultra-low gloss polycarbonate styrene resin alloy.

[0047] Further test and evaluation of the prepared ultra-low gloss polycarbonate styrene resin alloy, the mechanical properties and gloss test methods are as follows:

[0048] Carry out physical and mechanical performance test and glossiness test to the prepared polycarbonate styrenic resin alloy:

[0049] Tensile test: according to the ISO 527 standard, the tensile speed is 50mm / min;

[0050] IZOD notched impact strength: tested according to ISO 180 standard;

[0051...

Embodiment 1

[0066] An ultra-low gloss polycarbonate styrenic resin alloy, comprising the following raw material components in parts by weight:

[0067]

Embodiment 2

[0069] An ultra-low gloss polycarbonate styrenic resin alloy, comprising the following raw material components in parts by weight:

[0070]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a polycarbonate styrene resin alloy and a preparation method thereof. The polycarbonate styrene resin alloy comprises the following raw material components in parts by weight:30-60 parts of polycarbonate resin, 25-60 parts of styrene resin, 5-30 parts of branched polycarbonate, 5-15 parts of assistant crosslinking resin and 0.5-1.0 part of a processing aid. The preparation method comprises the following steps: premixing the raw materials in a high-speed mixer for 3-10 min, and carrying out extrusion granulation on the premix through a double-screw extruder at the temperature of 230-280 DEG C to obtain the ultralow-gloss polycarbonate styrene resin alloy. Compared with the prior art, the polycarbonate styrene resin alloy with ultralow gloss is directly prepared bya one-step method without preparing low gloss master batch, the preparation method and the technological process are simple, the problems of insufficient gloss, uneven gloss distribution, deterioration of physical and mechanical properties, complex process, high cost and the like are solved, and the resin alloy is particularly suitable for the field of automotive interiors.

Description

technical field [0001] The invention relates to the technical field of polymer material processing, in particular to a polycarbonate styrene resin alloy and a preparation method thereof. Background technique [0002] Polycarbonate styrene-based resin alloys have been widely used, and low-gloss surface effects are expected in some fields such as electronic appliances and automotive interior parts, such as computer casings, keyboards, mice, and instruments in automotive interior parts. panels, sun visors, navigator frames, etc. Especially in the field of automotive interiors, in order to avoid the visual disturbance caused by the reflection of sunlight on the driver and reduce the driver's visual fatigue, so as to achieve the purpose of safe and comfortable driving, matting or matte treatment is generally carried out to reduce the interior as much as possible. surface gloss of the piece. Generally, there are mainly the following methods to reduce the surface gloss of interio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L55/02C08L69/00C08L33/20C08L51/00C08L51/04C08L51/06
CPCC08L55/02C08L69/00C08L33/20C08L2205/035C08L2205/025C08L51/003C08L51/04C08L51/06
Inventor 查超周霆辛敏琦
Owner SHANGHAI KUMHO SUNNY PLASTICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap