Foam breathable film composite multifunctional fabric

A breathable film and multi-functional technology, which is applied in the field of composite functional fabrics and foamed breathable film composite multi-functional fabrics, can solve the problems affecting the performance of laminated fabrics such as waterproof and hydrostatic pressure resistance

Active Publication Date: 2021-10-01
浙江东进新材料有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

If the porosity of the film is increased and the pore size is increased, although the moisture permeability and air permeability can be improved, it will affect the waterproof and hydrostatic pressure resistance of the laminated fabric.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Foam breathable film composite multifunctional fabric
  • Foam breathable film composite multifunctional fabric
  • Foam breathable film composite multifunctional fabric

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0047] A waterproofing agent, which is made by polymerization reaction of 28 parts of organosilicon monomer, 13 parts of organic fluorine monomer, 13 parts of modified nano-silica sol, 8 parts of emulsifier, 0.8 parts of initiator and 163 parts of water. The preparation method as follows:

[0048] Add 140 parts of water, 13 parts of modified nano-silica sol and 8 parts of emulsifier into the reaction kettle, dissolve and stir to disperse evenly, then add 12 parts of organosilicon monomer (as shown in the above formula 2), stir and emulsify for 0.5h ;When the temperature reaches 78°C, add a solution of 0.3 parts of initiator and 8 parts of water, and keep warm for 0.5h; add dropwise a solution of 0.5 parts of initiator and 15 parts of water, 16 parts of organic silicon monomer, 13 parts of organic fluorine monomer After 2 hours of dripping, the temperature was raised to 85°C, and the reaction was continued for 1 hour, and then the temperature was lowered to below 50°C to obtain...

Embodiment 2

[0063] A composite multi-functional fabric with a foaming breathable film, which includes a surface fabric, an adhesive layer, a foamed film, an adhesive layer, and an inner fabric from top to bottom. Composite by adhesive layer;

[0064] The method for preparing foamed breathable film composite multifunctional fabric is as follows:

[0065] ① Prepare the waterproofing agent and water to form a 30g / L waterproofing agent finishing solution,

[0066] ②The surface fabric is dipped and rolled with waterproofing agent finishing liquid, two dipping and two rolling, the rolling rate is 80%

[0067] ③Dry at 100°C for 2 minutes, bake at 160°C for 1 minute,

[0068] ④According to 150g / m 2 The amount of the adhesive is coated on the surface fabric and the inner fabric, and compounded with the foam film.

[0069] ⑤Dry at 100°C for 3 minutes and bake at 170°C for 2 minutes to obtain a composite multifunctional fabric with a foamed breathable film.

[0070] The adhesive is composed of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
porosityaaaaaaaaaa
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a composite multifunctional fabric with a foaming breathable film, which comprises a surface fabric, an adhesive layer, a foamed film, an adhesive layer, and an inner fabric from top to bottom, and the fabric and the film are combined through the adhesive layer. The surface of the surface fabric is also provided with a waterproof agent; the steps of preparing the foamed breathable film composite multi-functional fabric are as follows: ① configure the waterproof agent and water into a waterproof agent finishing solution, ② pad the surface fabric with the waterproof agent finishing solution, ③ dry, bake Baking, ④ surface fabric, inner layer fabric coated with adhesive, compound with foam film, ⑤ drying, baking.

Description

technical field [0001] The invention relates to a composite functional fabric, in particular to a foamed breathable membrane composite multifunctional fabric, which belongs to the field of functional textiles. Background technique [0002] Waterproof and moisture-permeable fabric is usually also called waterproof and breathable fabric, which is a fabric that can not only prevent rain and wind, but also wick away sweat and breathe. During the wearing process, water cannot penetrate the fabric under a certain pressure, but the sweat emitted by the human body can be transmitted to the outside world through the fabric in the form of water vapor, without condensation and accumulation between the human body surface and the fabric, keeping the wearer dry and warm. Most of the waterproof and moisture-permeable functional fabrics are high-density fabrics, coated fabrics, and laminated fabrics. In terms of processing convenience and performance, laminated fabrics account for the majo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B32B27/02B32B27/12B32B27/36B32B27/40D03D15/56D06M11/79D06M15/356D06M15/277D06M101/32
CPCB32B5/02B32B5/245B32B5/18D06M11/79D06M15/3568D06M15/277B32B2262/0284B32B2266/0278D06M2101/32D03D15/56
Inventor 陈明贤孙立新董洪波
Owner 浙江东进新材料有限公司