Nickel paste for electronic cigarette atomizing core and preparing method thereof

A technology of electronic smog and atomizing core, which is applied in metal processing equipment, printing, transportation and packaging, etc. It can solve the problems of high sintering process requirements, small amount of mist generation, poor thixotropy, etc., and achieve continuous suction mist generation Large, low metallization sintering temperature, low sintering process requirements

Active Publication Date: 2020-07-31
湖南省国银新材料有限公司
View PDF25 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Now other similar atomizing core nickel paste products mainly use nickel-chromium alloy powder as the main conductive material. This nickel-chromium alloy powder contains chromium, and it is easy to produce peculiar smell with a lot of e-liquid under high temperature heating state, resulting in poor taste, and electronic smoke The metal sintering temperature of the chemical core is relatively high, which requires high sintering process for large-scale industrial production
The width of the circuit line diameter after printing and sintering of this kind of paste is basically 0.3-0.5 mm, and the thixotropy is poor during the printing process, and the height is only 80-100 microns, and it is prone to problems such as virtual printing and disconnection. Small volume of suction mist

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nickel paste for electronic cigarette atomizing core and preparing method thereof
  • Nickel paste for electronic cigarette atomizing core and preparing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A preparation method of nickel paste for electronic smog chemical core:

[0026] (1) by mass percentage, take by weighing 2% ethyl cellulose STD-300, 8% polymethacrylic resin, 10% alcohol ester twelve, 60% diethylene glycol butyl ether acetate, 10 % oleic acid, 6% lecithin, 4% polyether silicone oil, heated and stirred at 50-100°C to obtain an organic vehicle;

[0027] (2) Take by weighing 15g of the organic carrier prepared in step (1), 60g of nickel powder, 10g of flaky titanium hydride powder, and 15g of glass powder of Bi-Si-B system; wherein, the average particle diameter of the nickel powder is 6.5 μm , the tap density is 3.6g / cm 3 , the average particle size of the titanium hydride powder is 2.5 μm, the average particle size of the glass powder is 2.0 μm, and the softening point is 600-700° C.;

[0028] (3) Stir and mix the above-mentioned materials, and then add them into a three-roll rolling mill for grinding and dispersing to obtain the nickel paste for elec...

Embodiment 2

[0030] (1) by mass percentage, take by weighing 2% rosin resin, 4% phenolic resin, 15% diethylene glycol butyl ether, 65% diethylene glycol butyl ether acetate, 10% terpineol, 2% lecithin, 2% polyether silicone oil, heating and stirring at 50-100°C to obtain an organic vehicle;

[0031] (2) Take by weighing 20g of the organic carrier prepared in step (1), 70g of nickel powder, 5g of flaky titanium hydride powder, and 5g of glass powder of Bi-Si-B system; wherein, the average particle diameter of the nickel powder is 3.0 μm , the tap density is 4.5g / cm 3 , the average particle size of the titanium hydride powder is 1.8 μm, the average particle size of the glass powder is 1.0 μm, and the softening point is 600-700° C.;

[0032] (3) Stir and mix the above-mentioned materials, and then add them into a three-roll rolling mill for grinding and dispersing to obtain the nickel paste for electronic smog cores after stirring evenly.

Embodiment 3

[0034] (1) by mass percentage, take by weighing 4% ethyl cellulose STD-300, 6% rosin resin, 15% alcohol ester twelve, 50% diethylene glycol butyl ether acetate, 15% lemon tributyl ester, 10% polyether silicone oil, heating and stirring at 50-100°C to obtain an organic vehicle;

[0035](2) Take by weighing 9g of organic carrier prepared in step (1), 80g of nickel powder, 1g of flaky titanium hydride powder, and 10g of glass powder of Bi-Si-B system; wherein, the average particle diameter of the nickel powder is 1.5 μm , the tap density is 6.5g / cm 3 , the average particle size of the titanium hydride powder is 1.0 μm, the average particle size of the glass powder is 3.0 μm, and the softening point is 600-700° C.;

[0036] (3) Stir and mix the above-mentioned materials, and then add them into a three-roll rolling mill for grinding and dispersing to obtain the nickel paste for electronic smog cores after stirring evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
densityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses nickel paste for an electronic cigarette atomizing core and a preparing method thereof. The paste is suitable for various porous ceramic atomizing cores, and is particularly suitable for porous silicon oxide ceramics. The paste comprises, by mass percent, 60 to 80% of nickel powder, 1 to 10% of hydrogenated titanium powder, 3 to 16% of glass powder and 8 to 30% of an organic carrier. Compared with an existing atomizing core nickel paste technology, the electronic cigarette atomizing core nickel paste has the ideal thixotropy, a fine line with the quite good high-width ratio can be continuously printed, virtual printing, line breaking and other problems cannot appear, low metallization sintering temperature is achieved, no lead or chromium or other poisonous metal iscontained in a component, the need for a large-scale industrial production sintering process is low, after cigarette loading, continuous suction atomization amount is large, the paste can be matchedwith various tobacco tar, the reduction degree of tobacco tar essence is high, in the atomizing process, no peculiar smell is generated, and taste is good.

Description

technical field [0001] The invention relates to the technical field of electronic smog cores, in particular to a nickel paste for electronic smog cores and a preparation method thereof. Background technique [0002] With the development of the electronic cigarette industry, the design of various electronic cigarette components is also approaching maturity. Among them, the technology of the electronic cigarette atomizing sheet of the metallized porous ceramic atomizing core is also becoming more and more advanced with the development requirements of the industry. It's getting finer. The heating condition of the matching of the atomizing core and the e-liquid, and the reduction of the essence of the matching of the atomizing core and the e-liquid are getting higher and higher. A metal circuit with a better line aspect ratio and good continuity has become one of the new technical development requirements. Now other similar atomizing core nickel paste products mainly use nicke...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F1/00B22F9/02B22F3/10B41M1/12B41M1/34
CPCB22F9/02B22F3/1007B41M1/12B41M1/34B22F2999/00B22F1/052B22F1/108B22F1/10B22F2201/00
Inventor 刘宵杨华荣严红革王翔肖新明闫仁泉陈吉华
Owner 湖南省国银新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com