Austenite vermicular graphite cast iron material

A technology of vermicular graphite cast iron and austenite, which is applied in the field of austenitic vermicular graphite iron materials, can solve the problems of inability to meet requirements, limited heat resistance, limited tensile strength, and increased installed failure rate, so as to improve wear resistance. , The effect of tensile strength and elongation improvement, creep rate and elongation rate

Inactive Publication Date: 2020-09-18
FEILONG AUTO COMPONENTS CO LTD
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the implementation of the National Sixth Standard, the temperature resistance and pressure resistance of the existing aluminum pistons have been significantly improved. Due to the limited heat resistance and tensile strength of the currently used nickel-based austenitic gray cast iron inserts, the failure rate of the installed machine has been greatly increased. fulfil requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Austenite vermicular graphite cast iron material
  • Austenite vermicular graphite cast iron material
  • Austenite vermicular graphite cast iron material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0022] The present invention will be further described below in conjunction with embodiment. Apparently, the described embodiments are some, but not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0023] The invention provides an austenitic vermicular graphite cast iron material, the austenitic vermicular graphite cast iron material presents a flake and spherical mixed structure, and has the common advantages of the flake structure and the spherical structure, so that the austenitic vermicular graphite Cast iron materials meet the demands of high-performance engines.

[0024] The cast iron material, by mass fraction, includes the following components: carbon: 2.2-3.0%, silicon: 2.0-3.1%, manganese: 0.5-1.5%, phosphorus: ≤0.08%, sulfur: ≤0.02%, chromium: 0.9 ~1.8%, nickel: 12~...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an austenite vermicular graphite cast iron material. The austenite vermicular graphite cast iron material comprises the following components in percentage by mass: carbon: 2.2-3.0%, silicon: 2.0-3.1%, manganese: 0.5-1.5%, phosphorus: <=0.08%, Sulfur: <= 0.02%, chromium: 0.9-1.8%, nickel: 12-18%, copper: 4.8-8%, cerium: 0.01-0.03%, magnesium: 0.012-0.02%, and the balance iron. The austenitic vermicular graphite cast iron material provided by the invention contains less magnesium elements, so that the wear resistance of the austenitic vermicular graphite cast iron material can be greatly improved. By detecting the performance of the austenite vermicular graphite cast iron material provided by the invention, the vermicular rate, the tensile strength and the elongationrate of the austenite vermicular graphite cast iron material are greatly improved compared with relevant performance parameters in the prior art, and the main reason is that the austenite vermicular graphite cast iron material provided by the invention is a spherical and vermicular mixed body, so that the austenite vermicular graphite cast iron material has the advantages of tensile strength of aspherical cast iron material and high vermicular rate and elongation rate of a vermicular cast iron material.

Description

technical field [0001] The invention relates to the technical field of cast iron, in particular to an austenitic vermicular graphite cast iron material. Background technique [0002] The piston is the "heart" of the automobile engine, which bears alternating mechanical loads and thermal loads, and is one of the key components in the engine with the worst working conditions. One of the main factors affecting the service life of aluminum alloy pistons is the wear of piston ring grooves, especially the first ring groove. [0003] In order to improve the wear resistance of the first ring groove of the aluminum piston, cast iron wear-resistant ring seat (insert ring) is generally used in the industry as an effective solution. This ring-inlaid piston not only maintains the light weight of the aluminum piston, but also Combined with the advantages of wear-resistant cast iron piston ring grooves, the service life of aluminum pistons is greatly improved, and ring-mounted aluminum pi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C37/10C22C37/08C21C1/08C22C33/10
CPCC21C1/08C22C33/10C22C37/08C22C37/10
Inventor 曹红磊王瑞金余嗣瑞李刚王延召刘书彦李金秀
Owner FEILONG AUTO COMPONENTS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products