Fireproof and heat-insulating safe and manufacturing process thereof

A manufacturing process and technology of safes, applied in safes, special surfaces, pre-treated surfaces, etc., can solve the problem that safes do not have fire protection functions

Inactive Publication Date: 2020-10-20
JIANGXI EQUIP INDAL GROUP GREAT INSURANCENT
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Safe is as a kind of utensil for storing cash, bills, confidential documents or other valuables. Generally, safes in the prior art are all made of metal materials,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fireproof and heat-insulating safe and manufacturing process thereof
  • Fireproof and heat-insulating safe and manufacturing process thereof

Examples

Experimental program
Comparison scheme
Effect test

no. 1 example

[0032] A fire-proof and heat-insulating safe, comprising a cabinet body 1, on which there is a fire-proof and heat-insulating cavity 2 and a storage cavity 4, the fire-proof and heat-insulating cavity 2 is provided with a fire-proof and heat-insulating material, and the fire-proof and heat-insulating material Including the following raw materials: matrix material, flame retardant and porous carbon material.

[0033] As a preferred embodiment of the present invention, it also has the following additional technical features:

[0034] The base material is metal foam.

[0035] The flame retardant uses sodium bicarbonate and / or rock powder.

[0036] The mass ratio of the matrix material, flame retardant and porous carbon material is 1:0.05-0.1:0.1-0.3.

[0037] The thickness of the fire-proof and heat-insulating cavity 2 is 0.1-3 cm, preferably 2 cm.

[0038] A number of evenly distributed arched spheres 3 are arranged between the fire-proof and heat-insulating chamber 2 and the...

no. 2 example

[0040] A manufacturing process of a fire-resistant and heat-insulated safe, comprising the following steps:

[0041] Step 1: making a cabinet body with a fire-proof and heat-insulating cavity;

[0042] Step 2: Make fire-proof and heat-insulating materials, and place them in the fire-proof and heat-insulation cavity in step 1. The manufacturing process of fire-proof and heat-insulating materials is as follows:

[0043] First prepare the flame retardant into a solution, then place the porous carbon material in the solution for the first impregnation, continue to add matrix materials into the solution, perform the second impregnation, and dry to obtain the fireproof and heat insulating material.

[0044] Specifically, the base material is iron-nickel foam metal, and the porous carbon material can be activated carbon or coke.

[0045] In the second step, the first impregnation and / or the second impregnation is ultrasonic impregnation.

[0046] In the described step 2, the drying...

Embodiment 201

[0050] A manufacturing process of a fire-resistant and heat-insulated safe, comprising the following steps:

[0051] Step 1: making a cabinet body with a fire-proof and heat-insulating cavity;

[0052] Step 2: Make fire-proof and heat-insulating materials, and place them in the fire-proof and heat-insulation cavity in step 1. The manufacturing process of fire-proof and heat-insulating materials is as follows:

[0053] First prepare the flame retardant into a solution, specifically adding the flame retardant to water, then place the porous carbon material in the solution for the first 3 hours of immersion, continue to add matrix materials to the solution, and perform the second immersion for 5 hours, after drying A fire-proof and heat-insulating material is prepared.

[0054] Described flame retardant adopts sodium bicarbonate.

[0055]The mass ratio of the matrix material, flame retardant and porous carbon material is 1:0.05:0.1.

[0056] Specifically, the base material is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a fireproof and heat-insulating safe, and belongs to the field of safe equipment. The problem that a traditional safe cannot prevent fire and insulate heat is solved. The fireproof and heat-insulating safe comprises a safe body, wherein the safe body is provided with one fireproof and heat-insulating cavity and one storage cavity; and a fireproof and heat-insulating material is arranged in the fireproof and heat-insulating cavity, and the fireproof and heat-insulating material comprises the following raw material of a base material, a flame retardant and a porous carbonmaterial. The safe has excellent fireproof and heat-insulating capacity. The invention further discloses a manufacturing process of the fireproof and heat-insulating safe.

Description

technical field [0001] The invention relates to the field of safe equipment, in particular to a fireproof and heat-insulating safe and a manufacturing process thereof. Background technique [0002] Safe is as a kind of utensil for storing cash, bills, confidential documents or other valuables. Generally, safes in the prior art are all made of metal materials, but metal materials are good conductors of heat, and their thermal conductivity is extremely strong. In the event of a fire, the safe does not have a fireproof function. Contents of the invention [0003] The object of the present invention is to at least solve one of the technical problems in the prior art, and provide a fireproof and heat-insulated safe and its manufacturing process. [0004] Technical solution of the present invention is as follows: [0005] A fire-proof and heat-insulating safe, including a cabinet body, on which there is a fire-proof and heat-insulating cavity and a storage cavity, and a fire-p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): E05G1/02E05G1/06B05D5/00B05D1/18B05D7/24B05D3/04
CPCB05D1/18B05D3/0426B05D5/00B05D7/24E05G1/02E05G1/06
Inventor 徐迪杨陈周静平
Owner JIANGXI EQUIP INDAL GROUP GREAT INSURANCENT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products