Sudoku mountain vein natural ore transmutation glaze and preparation method thereof

A technology of natural ore and kiln-changing glaze, applied in the field of ceramics, can solve the problems of high price, troublesome operation, hazards, etc., achieve the effects of reducing types, improving safety and quality, and simple production process

Pending Publication Date: 2020-11-06
王混正
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the kiln transformation glaze is made of volcanic rock and potassium feldspar as the main material, and then mixed with various chemical raw materials. Most of these chemical raw materials contain heavy metals and toxic chemical solvents (such as: lead oxide, borax, etc.), and people will bring harm to the body and the environment that cannot be ignored during use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Embodiment 1, take by weighing 700g of natural ore raw materials in Jiulongshan Mountains, 100g of potassium feldspar, 40g of calcite, 50g of agate, and 80g of fruit wood ash, put them into a ball mill and grind them for 48 hours, filter with an 80-mesh sieve, and add 600g of purified water , stir evenly.

Embodiment 2

[0016] Embodiment 2, take by weighing 650g of natural ore raw materials in Jiulongshan Mountains, 80g of potassium feldspar, 50g of calcite, 60g of agate, and 110g of fruit ash, put them into a ball mill and grind them for 72 hours, filter with a 120-mesh sieve, and add 650g of purified water , stir evenly.

[0017] After dipping glaze, dipping glaze, spraying glaze, pouring glaze and other methods on the surface of the plain tire and using kiln-changing glaze, it enters the kiln for 10-16 hours and is fired at 1200°C-1300°C. The porcelain fired by the present invention has the characteristics of the Northern Song Dynasty. Ru kiln porcelain features: bright glaze, hard wear-resistant, warm and moist like jade, rich in color, beautiful and generous.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a Sudoku mountain vein natural ore transmutation glaze which is prepared from the following raw materials: 60-70% of natural ore, 5-12% of potassium feldspar, 2-8% of calcite,2-10% of agate, 6-15% of fruit tree ash and 65-70% of purified water. The preparation method comprises the following steps: weighing the raw materials in parts by weight, putting the weighed raw materials into a ball mill, performing milling for 48-72 hours, performing filtration with a 80-120-mesh sieve, adding the purified water, and performing uniform stirring so as to obtain the product. Thenatural ore in the Sudoku Mountain vein contains rich transmutation glaze substances, and mineral substances such as iron and calcium in the natural ore are beneficial to a human body. The raw material variety is reduced, the production process is simple, furnace transmutation can be achieved without changing the formula, and the method is suitable for rapid and effective production.

Description

technical field [0001] The invention relates to the field of ceramics, in particular to a layer of kiln-transformed glaze on the surface of ceramics, a kiln-transformed glaze using natural ore from the Jiulong Mountains as a main raw material and a preparation method thereof. Background technique [0002] Dip glaze, dip glaze, spray glaze, and pour glaze on the surface of the plain tire. After entering the kiln, it will be fired into kiln-shaped porcelain after a certain period of high-temperature oxidation and reduction. Changing the formula of the glaze and the furnace temperature can be fired into kiln-shaped porcelain of different colors. . At present, the kiln-changing glaze is made of volcanic rock and potassium feldspar as the main material, and then various chemical raw materials are added. There are many types of chemical raw materials, and the price is expensive. The formula and ratio must be changed during the kiln transformation, which is troublesome to operate. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/00C04B41/86
CPCC03C8/00C04B41/5022C04B41/86
Inventor 王混正
Owner 王混正