A kind of fluorine-free superhydrophobic surface and preparation method thereof

A super-hydrophobic surface and substrate surface technology, applied to special surfaces, devices for coating liquids on surfaces, coatings, etc., can solve the problems of complex operation and unenvironmental protection, achieve simple operation, improve hydrophobicity, and overcome complex operation. and not environmentally friendly

Active Publication Date: 2021-11-02
SHANGHAI UNIV
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the operation of constructing a fine structure on a solid surface is relatively complicated. For example, Chinese patent CN201810699442.8 obtains a hydrophobic alloy surface by sequentially performing pretreatment, anodic oxidation treatment, hydrogen peroxide treatment and aging treatment on the specimen.
This preparation method has the defects of complex operation and environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of fluorine-free superhydrophobic surface and preparation method thereof
  • A kind of fluorine-free superhydrophobic surface and preparation method thereof
  • A kind of fluorine-free superhydrophobic surface and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] The invention provides a method for preparing a fluorine-free superhydrophobic surface, comprising the following steps:

[0028] (1) mixing the solid particles with a solvent to obtain a dispersion of the solid particles; the concentration of the solid particles in the dispersion is 0.3 to 0.5 g / mL; the particle size distribution of the solid particles in the dispersion is 200 nm to 10 μm; The solid particles include metal particles or inorganic oxide particles;

[0029] (2) Coating the dispersion in the step (1) on the surface of the substrate and drying to obtain a surface containing solid particles; the distribution density of the solid particles in the surface containing solid particles is 10000 to 20000 / mm 2 ;

[0030] (3) Coating the fluorine-free block copolymer solution on the surface containing solid particles obtained in the step (2), and then annealing to obtain a fluorine-free super-hydrophobic surface.

[0031] The invention mixes solid particles with a s...

Embodiment 1

[0071] (1) Use the MQW series jet mill (setting speed: 10000r / min, crushing time: 0.5h) to crush the copper block into copper particles with a particle size of 200nm-20μm, then put 5g of copper particles and 1000mL of deionized water into the Mixer, adjust the speed of the mixer to 1000r / min, stir for 0.5h, then stand still for 5s, take the upper suspension and add deionized water, and then repeat the above operation several times, so that the upper suspension only contains copper particles with a particle size of 200nm to 1μm. Add deionized water to the obtained upper layer suspension containing copper particles to adjust the concentration to 0.3 g / mL to obtain an aqueous dispersion of copper particles.

[0072] (2) Spin-coat the aqueous dispersion of copper particles obtained in step (1) onto the surface of the glass substrate (the rotating speed of the spin-coating is set to be 2000r / min, and the time of the spin-coating is 30s), then process at 150°C for 2h and dry, Form a...

Embodiment 2

[0080] (1) Mix 3g of 200nm-10um aluminum particles with 100mL of deionized water, put them into a mixer, adjust the speed of the mixer to 1000r / min, and stir for 0.5h to obtain an aqueous dispersion of aluminum particles with a concentration of 0.3g / mL.

[0081] (2) Spin-coat the aqueous dispersion of aluminum particles obtained in step (1) onto the surface of the glass substrate (set the spin-coating speed to be 2000r / min, and the spin-coating time to be 30s), then treat and dry at 150°C for 2h, Form the surface containing aluminum particles, wherein the distribution density of aluminum particles on the surface containing aluminum particles is 11000-16000 / mm 2 .

[0082] (3) The surface of the aluminum-containing particles obtained in step (2) is spin-coated with MH-b-PS with a thickness of 40 μm (the speed of spin coating is 1500r / min, and the time of spin coating is 30s), and then using tetrahydrofuran at 25°C , annealed in solvent for 10h to obtain a superhydrophobic surf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
concentrationaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of superhydrophobic materials, and provides a method for preparing a fluorine-free superhydrophobic surface, comprising the following steps: mixing solid particles with a solvent to obtain a dispersion of solid particles, and coating the dispersion on the surface of a substrate After drying, a surface containing solid particles is obtained, and a fluorine-free block copolymer solution is coated on the obtained surface containing solid particles, followed by annealing to obtain a fluorine-free super-hydrophobic surface. The present invention controls the distribution density of the solid particles on the surface of the substrate by controlling the concentration of the water dispersion of the solid particles, thereby controlling the roughness of the substrate; by controlling the particle diameter of the solid particles in the dispersion of the solid particles, microscopic The nanostructure can not only improve the roughness of the substrate surface, but also ensure the self-assembly of the fluorine-free block copolymer on the surface to form smaller micro-nanostructures, improve the hydrophobicity of the surface, and achieve the effect of superhydrophobicity.

Description

technical field [0001] The invention relates to the technical field of superhydrophobic materials, in particular to a fluorine-free superhydrophobic surface and a preparation method thereof. Background technique [0002] Hydrophobic materials generally refer to materials with a water contact angle of greater than 150° and a rolling angle of less than 10°. For example, the "lotus leaf effect" on the surface of the lotus leaf is a remarkable performance of hydrophobic materials in nature. In production and life, superhydrophobic surfaces have a wide range of application prospects, such as anti-biofouling coatings for ships, surface cleaning of satellite antennas, self-cleaning of automotive windshields, antifouling textiles, antifouling architectural coatings, fluid drag reduction Wait. Therefore, related research is receiving more and more attention. [0003] At present, two methods are generally used to prepare superhydrophobic surfaces: one is to directly build microstru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B05D5/08C09D153/00
CPCB05D5/08C09D153/00
Inventor 胡腾达陈旻彧朱志强龚春柳廖英杰陈果兰伟霞魏斌
Owner SHANGHAI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com