Novel heat-resistant PVC profile and preparation method thereof

A technology of PVC resin powder and profiles, which is applied in the field of new heat-resistant PVC profiles and its preparation, can solve problems such as poor heat resistance, and achieve improved heat resistance, little change in impact strength and tensile strength, and excellent overall performance Effect

Pending Publication Date: 2020-12-18
亿利生态科技有限责任公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention provides a new type of heat-resistant PVC profile and its preparation me

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0018] Example 1:

[0019] 100 parts of PVC resin, 5 parts of heat-resistant modifier, 3.8 parts of stabilizer, calcium carbonate (CaCO 3 ) 18 parts, 9 parts of toughening agent, 0.5 part of processing modifier, 5 parts of titanium dioxide, and 0.7 part of lubricant; mix and discharge the above ingredients; add the pre-mixed dry powder in the above steps into the extruder Production of profiles; high-speed stirring, when the temperature reaches 110 °C, stir for 4 minutes, enter the cold mixer to 45 °C and discharge; the temperature settings of each zone of the extruder: 150 °C in the conveying section, 170 °C in the compression section, 180 °C in the melting section, Head 175°C.

Example Embodiment

[0020] Example 2:

[0021] 100 parts of PVC resin, 10 parts of heat-resistant modifier, 4.3 parts of stabilizer, calcium carbonate (CaCO 3 ) 16 parts, 10 parts of toughening agent, 0.7 part of processing modifier, 6 parts of titanium dioxide, 0.8 part of lubricant; mix and discharge the above various components; add the pre-mixed dry powder in the above steps into the extruder Production of profiles; high-speed stirring, when the temperature reaches 110 °C, stir for 4 minutes, enter the cold mixer to 45 °C and discharge; the temperature settings of each zone of the extruder: 150 °C in the conveying section, 170 °C in the compression section, 180 °C in the melting section, Head 175°C.

Example Embodiment

[0022] Example 3:

[0023] 100 parts of PVC resin, 15 parts of heat-resistant modifier, 4.9 parts of stabilizer, calcium carbonate (CaCO 3 ) 13 parts, 10 parts of toughening agent, 0.9 part of processing modifier, 7 parts of titanium dioxide, 0.1.1 part of lubricant; mix and discharge the above-mentioned various components; add the pre-mixed dry powder in the above steps into extrusion Profiles are produced in the machine; high-speed stirring, when the temperature reaches 110 °C, stir for 4 minutes, then enter the cold mixer to 45 °C for discharge; the temperature settings of each zone of the extruder: 150 °C in the conveying section, 170 °C in the compression section, and 180 °C in the melting section ℃, head 175℃.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a novel heat-resistant PVC profile and a preparation method thereof.The novel heat-resistant PVC profile is composed of PVC resin powder and auxiliaries, the auxiliaries are composed of a heat-resistant modifier, a stabilizer, calcium carbonate, a flexibilizer, a processing modifier, titanium dioxide and a lubricant, and the heat-resistant agent is a styrene-butenoic acid-acrylonitrile copolymer; the PVC profile has the advantages that the Vicat softening point can be obviously improved by adding the heat-resistant agent styrene butenoic acid-acrylonitrile copolymer, and on the basis of obviously improving the heat resistance of the PVC profile, the impact strength and the tensile strength can be kept slightly changed, and the overall performance is excellent.

Description

Technical field: [0001] The invention relates to the technical field of new PVC materials, in particular to a novel heat-resistant PVC profile and a preparation method thereof. Background technique: [0002] PVC is one of the five synthetic thermoplastics, its output is second only to polyethylene, and PVC is mainly hard products; PVC profiles are widely used in furniture and decoration industries, and develop at a relatively fast speed, but PVC profiles are not heat resistant. It cannot meet the demand for long-term use under high temperature conditions, which limits its application range. Therefore, improving the heat resistance of PVC profiles is one of the keys to the development and application of PVC profiles, which will promote its application and development in more industries. Invention content: [0003] In order to overcome the common problem of poor heat resistance of PVC materials in the prior art), the present invention provides a novel heat-resistant PVC prof...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L25/12C08L23/28C08K3/26C08K3/22C08K5/09C08K13/02
CPCC08L27/06C08K2003/265C08K2003/2241C08L2205/035C08L2201/08C08L25/12C08L23/286C08K3/26C08K3/22C08K5/09C08K13/02
Inventor 石建文王文凤张家鹤魏得虎史占权邬智勇任超
Owner 亿利生态科技有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap