A kind of functional masterbatch for improving the appearance flow mark defect of spray-free material and preparation method thereof

A functional masterbatch and spray-free technology, which is applied in the field of polymers, can solve the problems of easy flow marks on the surface and affect the batch use of spray-free plastics, and achieve the effects of improving dispersion, improving flow direction stability, and strong product adaptability

Active Publication Date: 2022-08-02
会通新材料(上海)有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for the existing surface-sprayed plastics, injection molding manufacturers are affected by the structure of parts and rib positions during injection molding. When using spray-free plastic products, surface defects such as flow marks are prone to appear on the surface, which affects the batch use of spray-free plastics.
In recent years, some people have proposed to use bimodal polypropylene to improve the appearance of flow marks, but after the verification of actual projects, bimodal polypropylene metal silver cannot solve the problem of flow marks very well

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of functional masterbatch for improving the appearance flow mark defect of spray-free material and preparation method thereof
  • A kind of functional masterbatch for improving the appearance flow mark defect of spray-free material and preparation method thereof
  • A kind of functional masterbatch for improving the appearance flow mark defect of spray-free material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The technical solutions in the embodiments of the present invention will be described clearly and completely below. Obviously, the described embodiments are only a part of the embodiments of the present invention, rather than all the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by those of ordinary skill in the art without creative efforts shall fall within the protection scope of the present invention.

[0033] A functional masterbatch for improving the appearance flow mark defect of spray-free materials, comprising the following raw materials in parts by weight:

[0034] 15-40 parts of polypropylene;

[0035] 30-50 parts of modified nano-silica;

[0036] 20-35 parts of surface-modified metallic pigments;

[0037] 1-5 parts of compatibilizer;

[0038] 3-6 copies of other additives.

[0039] Specifically, as shown in Table 1,

[0040] The composition of preparation raw material in the specific embodiment of table 1 ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a functional master batch for improving the appearance flow mark defects of spray-free materials and a preparation method thereof, and relates to the technical field of polymers. The metal silver polypropylene functional master batch includes 15-40 parts of polypropylene, 15-40 parts by weight of modified nano-di 30-50 parts of silicon oxide, 20-35 parts of surface-modified metal pigments, 1-5 parts of compatibilizer, and 3-6 parts of other auxiliary agents; the present invention prepares a fluid-like material having a core-shell structure by an acid-base neutralization method Silica nanoionic material. The modified nano-silica fluid is coated on the surface of the metal pigment to form a protective layer, and the strong polar amino group is introduced into the main chain of the non-polar molecule, which greatly improves the performance of the metal pigment in polypropylene. It can effectively improve the stability of the flow direction of the metal pigment in the molten polypropylene plastic in the mold cavity, greatly reduce the change of the arrangement direction of the flake metal pigment in the melt, and maintain the original parallel arrangement. Improves the symptoms of flow marks or water traps on the product surface.

Description

technical field [0001] The invention relates to the technical field of polymers, in particular to a functional masterbatch for improving the appearance flow mark defects of spray-free materials and a preparation method. Background technique [0002] In recent years, with the continuous improvement of living standards and the continuous improvement of the country's environmental protection requirements, the spray painting process has disadvantages such as large environmental pollution, easy to fall off paint, difficult to repair after falling paint, complicated process process, and unrecyclable production of defective products. more and more people's attention. With the development of materials and mold technology, spray-free materials that replace spraying technology have become a new trend in the application of plastic products. [0003] Spray-free plastics refer to products that add metallic pigments, pearlescent pigments and other pigments with special color effects to r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08J3/22C08L23/14C08L51/06C08K13/06C08K9/04C08K3/36C08K9/02C08K9/06C08K9/10C08K3/08
CPCC08J3/226C08J2423/14C08J2451/06C08K13/06C08K9/08C08K9/04C08K3/36C08K9/02C08K9/06C08K9/10C08K2003/0812C08K2003/0806C08K2003/0831C08K2003/0893C08K2003/085C08K2201/011
Inventor 王刚吴仲涛蒋文远周海
Owner 会通新材料(上海)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com