Penetrating ultrasonic testing method of vertical honeycomb splicing interface with water spray

An ultrasonic testing and penetrating technology, which is applied to the analysis of solids using sound waves/ultrasonic waves/infrasonic waves, material analysis using sound waves/ultrasonic waves/infrasonic waves, and measuring devices. It can solve the high risk of scrapping parts with multi-layer honeycomb sandwich structures. Unable to solve problems such as whether the honeycomb splicing interface is debonded, unable to perform water spray penetration C-scan, etc., to reduce the risk of scrapping, less difficult to detect, and less attenuation

Active Publication Date: 2021-12-07
COMAC +1
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Since the multi-layer honeycomb sandwich structure after one curing has no surface skin, the upper and lower honeycombs are directly exposed, and water spray penetration C-scanning cannot be performed. In the prior art, only the vertically spliced ​​multi-layer honeycomb after two curings is completed. Sandwich structure parts are inspected by water spray penetrating ultrasonic C-scan, and once defects are detected in multi-layer honeycomb sandwich structure parts, the parts can only be scrapped. The scrap rate of parts is high, which affects production costs
Therefore, the existing vertical honeycomb splicing interface water spray penetrating ultrasonic testing method cannot detect and monitor whether the honeycomb splicing interface after a solidification is debonded in advance, which makes the scrapping risk of multi-layer honeycomb sandwich structure parts high and affects production costs. technical issues

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Penetrating ultrasonic testing method of vertical honeycomb splicing interface with water spray

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] The technical solutions of the present invention will be further described below in conjunction with the accompanying drawings and through specific implementation methods.

[0025] In describing the present invention, it is to be understood that the terms "upper", "lower", "front", "rear", "left", "right", "vertical", "horizontal", "top", The orientation or positional relationship indicated by "bottom", "inner", "outer", etc. is based on the orientation or positional relationship shown in the drawings, and is only for the convenience of describing the present invention and simplifying the description, rather than indicating or implying the referred device Or elements must have a certain orientation, be constructed and operate in a certain orientation, and thus should not be construed as limiting the invention.

[0026] see figure 1 , the vertical honeycomb splicing interface water jet penetrating ultrasonic detection method of an embodiment comprises the following step...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A vertical honeycomb splicing interface water spray penetrating ultrasonic detection method, comprising the following steps: vertically splicing multilayer honeycomb structures; paving a layer of peelable skin on the upper and lower surfaces of the obtained multilayer honeycomb structure; The multi-layer honeycomb structure that has been peeled off the skin is cured for the first time; the multi-layer honeycomb structure after the first curing is subjected to a water spray penetrating ultrasonic C-scan test to detect whether all the honeycomb splicing interfaces are debonded; if all the honeycomb splicing interfaces are If there is no debonding defect, the detachable skin on the upper and lower surfaces of the multi-layer honeycomb structure is torn off; the surface skin is pasted on the upper and lower surfaces of the multi-layer honeycomb structure, and the multi-layer honeycomb structure pasted with the surface skin is subjected to secondary curing , to obtain vertically spliced ​​multilayer honeycomb structure parts. The above-mentioned ultrasonic testing method of vertical honeycomb splicing interface water spray penetrating can ensure the quality of the vertically spliced ​​multilayer honeycomb sandwich structure parts, reduce the risk of scrapping the multilayer honeycomb sandwich structure parts, and help save production costs.

Description

technical field [0001] The invention relates to the technical field of non-destructive testing, in particular to a water-spraying penetrating ultrasonic testing method for a vertical honeycomb splicing interface. Background technique [0002] In recent years, due to the needs of the development of aerospace technology, composite materials have developed rapidly, and various advanced composite materials and complex structural forms are replacing traditional airframe structural materials. Ultrasonic testing is the most effective and convenient non-destructive testing method for composite material structural parts, especially for ultrasonic testing of composite honeycomb sandwich structures. Due to the particularity of the honeycomb structure, the testing method is mainly based on water spray Ultrasound C-scan detection mainly. [0003] Traditional composite honeycomb sandwich structures are mostly single-layer honeycomb sandwich structures. With the continuous emergence of ne...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): G01N29/04G01N29/22
CPCG01N29/04G01N29/22G01N2291/0231
Inventor 王旭刘奎南方刘佳肖鹏张继敏周晖于光
Owner COMAC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products