Quick-drying single-component plastic primer and preparation method thereof

A single-component, fast-drying technology, applied in primers, polyurea/polyurethane coatings, coatings, etc., can solve the problems of improving resistance, long drying and solidification time, and poor solidification of spray topcoats. Good water resistance, excellent coagulation performance, and short coagulation time

Inactive Publication Date: 2021-02-09
GUANGDONG YATU CHEM
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The patent publication number is CN110591478A, which is named as a high-weather-resistant acrylic transformer topcoat and its preparation method. It discloses a high-weather-resistant acrylic transformer topcoat, but the solidification property of the high-weather-resistant acrylic transformer topcoat is Poor, it takes a long time to dry and solidify, and the resistance needs to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Quick-drying single-component plastic primer and preparation method thereof
  • Quick-drying single-component plastic primer and preparation method thereof
  • Quick-drying single-component plastic primer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] As a kind of quick-drying type one-component plastic primer of the embodiment of the present invention, described quick-drying type one-component plastic primer comprises the following components by weight, 35 parts of polyurethane modified acrylic resins, 20 parts of butyl acetates , 0.7 parts of wetting and dispersing agent, 20 parts of nano-barium sulfate, 25 parts of titanium dioxide, 0.8 parts of hydrophobically modified fumed silica, 0.8 parts of carbon black and 0.5 parts of anti-settling wax. The wetting and dispersing agent is modified poly ester, and the hydrophobically modified fumed silica is fumed silica R972.

Embodiment 2

[0022] As a kind of quick-drying type one-component plastic primer of the embodiment of the present invention, described quick-drying type one-component plastic primer comprises the following components by weight, 40 parts of polyurethane modified acrylic resins, 15 parts of butyl acetates , 0.7 parts of wetting and dispersing agent, 19.5 parts of nano barium sulfate, 25 parts of titanium dioxide, 0.8 parts of hydrophobically modified fumed silica, 0.8 parts of carbon black and 1 part of anti-settling wax. The wetting and dispersing agent is modified poly ester, and the hydrophobically modified fumed silica is fumed silica R972.

Embodiment 3

[0024] As a kind of quick-drying type one-component plastic primer of the embodiment of the present invention, described quick-drying type one-component plastic primer comprises the following components by weight, 45 parts of polyurethane modified acrylic resins, 15 parts of butyl acetates , 0.7 parts of wetting and dispersing agent, 19.5 parts of nano barium sulfate, 20 parts of titanium dioxide, 0.8 parts of hydrophobically modified fumed silica, 0.8 parts of carbon black and 1 part of anti-settling wax. The wetting and dispersing agent is modified poly ester, and the hydrophobically modified fumed silica is fumed silica R972.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides a quick-drying single-component plastic primer. The quick-drying single-component plastic primer comprises the following components in parts by weight: 30-50 parts of polyurethane modified acrylic resin, 10-20 parts of butyl acetate, 0.5-1 part of a wetting dispersant, 15-20 parts of nano barium sulfate, 18-25 parts of titanium dioxide, 0.1-1 part of hydrophobic modified fumed silica, 0.2-1 part of carbon black and 0.1-1 part of anti-settling wax. The quick-drying single-component plastic primer disclosed by the invention is easy to construct, good in appearance and leveling property, a formed paint film is flat and smooth in appearance, quick to dry, surface-dried in 5-10 minutes, excellent in adhesion to PP, ABS, nylon+glass fiber and other materials, and excellentin adhesion to upper-layer finish paint, and the paint adhesion testing adhesion is level 0-1; and hot water resistance (40 DEG C) lasts for 10 days or above. After the water resistance test, the paint adhesion testing adhesion is level 0-1. The quick-drying single-component plastic primer disclosed by the invention is good in flexibility and good in impact resistance; the plastic primer has goodadhesion on different materials, and applies the nano barium sulfate to have good water resistance.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a quick-drying one-component plastic primer and a preparation method thereof. Background technique [0002] The patent publication number is CN110591478A, which is named as a high-weather-resistant acrylic transformer topcoat and its preparation method. It discloses a high-weather-resistant acrylic transformer topcoat, but the solidification property of the high-weather-resistant acrylic transformer topcoat is Poor, it takes a long time to dry and solidify, and the tolerance needs to be improved. Contents of the invention [0003] The purpose of the present invention is to overcome the shortcomings of the prior art and provide a quick-drying one-component plastic primer and a preparation method. [0004] In order to achieve the above object, the technical solution adopted by the present invention is: a quick-drying one-component plastic primer, the quick-drying one-component ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D7/61C09D7/62C09D7/65
CPCC09D175/14C09D5/002C09D7/61C09D7/62C09D7/65C08K2201/011C08K2003/3045C08K2003/2241C08L2201/08C08L2205/03C08L91/06C08L67/00C08K13/06C08K7/26C08K3/30C08K3/22C08K3/04
Inventor 冯兆均罗国庆陈容爱李守康李锦源冯嘉伟
Owner GUANGDONG YATU CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com