A high-strength and high-toughness large martensitic stainless steel ring forging and its manufacturing method

A martensitic stainless steel, manufacturing method technology, applied in the direction of manufacturing tools, furnace types, engine components, etc., can solve the problems of unstable impact energy, cracking, etc., to shorten the production cycle and manufacturing costs, improve stability, and optimize chemistry The effect of ingredients

Active Publication Date: 2022-04-22
AVIC EXCELLENCE FORGING WUXI
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above problems, the present invention provides a high-strength and high-toughness large-scale martensitic stainless steel ring forging and its manufacturing method, which can solve the problem of cracking after forging and impact energy due to the large-scale ring forging produced by martensitic stainless steel X17CrNi16-2. unstable problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-strength and high-toughness large martensitic stainless steel ring forging and its manufacturing method
  • A high-strength and high-toughness large martensitic stainless steel ring forging and its manufacturing method
  • A high-strength and high-toughness large martensitic stainless steel ring forging and its manufacturing method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] A high-strength and high-toughness large-scale martensitic stainless steel ring forging, in terms of weight percentage, the chemical composition of the martensitic stainless steel includes C: 0.22%, Mn: 0.975%, P: 0.015%, S: 0.020%, Si: 0.001%, Cr: 15%, Mo: 0.10%, Ni: 2.5%, Cu: 0.10%, V: 0.005%, Nb: 0.025%, Ti: 0.020%, and the balance is Fe; at the same time, the gas composition meets : H: 1.5ppm, O: 40ppm, N: 200ppm.

[0052] The preparation method of the high-strength and high-toughness large-scale martensitic stainless steel ring forging is: it includes the following process steps,

[0053] Step 1, using the process of EAF+AOD to make the raw materials in the above parts by weight into steel ingots;

[0054] Step 2, forging the steel ingot to obtain a ring-shaped blank forging;

[0055] Step 3, then performing pre-forging heat treatment on the ring-shaped blank forging;

[0056] Step 4, performing mechanical rough machining and flaw detection on the ring forging t...

Embodiment 2

[0071] A high-strength and high-toughness large-scale martensitic stainless steel ring forging, in terms of weight percentage, the chemical composition of the martensitic stainless steel includes C: 0.14%, Mn: 1.5%, P: 0.030%, S: 0.010%, Si: 0.60%, Cr: 15.25%, Mo: 0.0020%, Ni: 2.25%, Cu: 0.001%, V: 0.05%, Nb: 0.010%, Ti: 0.0020%, and the balance is Fe; at the same time, the gas composition meets : H: 0.03ppm, O: 20ppm, N: 300ppm.

[0072] The preparation method of the high-strength and high-toughness large-scale martensitic stainless steel ring forging is: it includes the following process steps,

[0073] Step 1, using the process of EAF+AOD to make the raw materials in the above parts by weight into steel ingots;

[0074] Step 2, forging the steel ingot to obtain a ring-shaped blank forging;

[0075] Step 3, then performing pre-forging heat treatment on the ring-shaped blank forging;

[0076] Step 4, performing mechanical rough machining and flaw detection on the ring forg...

Embodiment 3

[0094] A high-strength and high-toughness large-scale martensitic stainless steel ring forging, in terms of weight percentage, the chemical composition of the martensitic stainless steel includes C: 0.18%, Mn: 0.45%, P: 0.002%, S: 0.003%, Si: 0.030%, Cr: 15.5%, Mo: 0.20%, Ni: 2.0%, Cu: 0.20%, V: 0.10%, Nb: 0.050%, Ti: 0.010%, and the balance is Fe; at the same time, the gas composition meets : H: 3ppm, O: 5ppm, N: 400ppm.

[0095] The preparation method of the high-strength and high-toughness large-scale martensitic stainless steel ring forging is: it includes the following process steps,

[0096] Step 1, using the process of EAF+AOD to make the raw materials in the above parts by weight into steel ingots;

[0097] Step 2, forging the steel ingot to obtain a ring-shaped blank forging;

[0098] Step 3, then performing pre-forging heat treatment on the ring-shaped blank forging;

[0099] Step 4, performing mechanical rough machining and flaw detection on the ring forging that...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a high-strength and high-toughness large-scale martensitic stainless steel ring forging. In terms of weight percentage, the martensitic stainless steel includes C: 0.14-0.22%, Mn: 0.45-1.5%, and P: ≤0.030% , S: ≤0.020%, Si: ≤0.60%, Cr: 15~15.5%, Mo: ≤0.20%, Ni: 2.0~2.5%, Cu: ≤0.20%, V: ≤0.10%, Nb: ≤0.050% , Ti: ≤0.020%, and the balance is Fe; at the same time, the gas composition meets: H: ≤3ppm, O: ≤40ppm, N: 200-400ppm; the corresponding manufacturing method, the steel ingot is passed through the cold saw nozzle, the riser, the heat Cut the riser, then perform three upsetting and two pulling, horse frame reaming, ring rolling, preliminary heat treatment, rough turning, quenching and tempering, body sampling, physical and chemical testing, and processing according to the drawing. The invention can solve the problems that large-scale ring forgings produced by adopting the martensitic stainless steel X17CrNi16-2 are prone to cracking after forging and unstable impact energy.

Description

technical field [0001] The invention relates to the field of manufacturing martensitic stainless steel forgings, in particular to a high-strength and high-toughness large martensitic stainless steel ring forging and a manufacturing method thereof. Background technique [0002] Martensitic stainless steel X17CrNi16-2 is the material in the European standard EN10250-4, its QT800 mechanical properties meet the tensile strength: 800 ~ 950Mpa, yield strength: ≥600Mpa, elongation: ≥10%, impact energy (Akv) ≥20J , Widely used in aviation, hydropower, ships, petroleum, valves and machinery and other industrial fields. [0003] The X17CrNi16-2 material is a hard-to-deform steel, because its microstructure not only contains martensite, but also a small amount of ferrite, and if the initial forging temperature of this material is too high during thermal processing, it is not only prone to overheating, but also prone to deformation. Excessive delta ferrite is produced, which further re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C38/02C22C38/04C22C38/42C22C38/44C22C38/46C22C38/48C22C38/50C21D1/26C21D6/00C21D8/00C21D9/40B21K1/76
CPCC22C38/04C22C38/02C22C38/002C22C38/44C22C38/42C22C38/46C22C38/48C22C38/50C22C38/001C21D9/40C21D6/004C21D6/005C21D6/008C21D1/26C21D8/005B21K1/761
Inventor 郭亮沈志远李少雨李松强邓伟吕洪良
Owner AVIC EXCELLENCE FORGING WUXI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com