Metal product surface sludge ferrous chloride recovery treatment process
A technology for ferrous chloride and metal products, applied in water/sludge/sewage treatment, dehydration/drying/concentrated sludge treatment, metallurgical wastewater treatment, etc. Low-level problems, to achieve the effect of high crystal purity and simple processing technology
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025]Example 1:
[0026]The surface sludge of the metal article adopted in this example is ferrous recovery process, including the following steps:
[0027]Step 1: Collect the surface sludge of the metal article, and the mixture of sludge and waste acid after pickling and pickling after pickling.
[0028]Step 2: Connect the mixture of the sludge and waste acid to the evaporative tank, 0.35 MPa of the evaporation tank, the temperature is set to 40 ° C, the rotational speed is set to 40R / min, when the chloride concentration does not change The evaporation tank is 0.5 MPa, the temperature is increased to 55 ° C, and the rotational speed is set to 55 r / min until the chloride concentration is unchanged, the evaporation can be pressured, and the internal chloride is naturally cooled, and there is appeared A small amount of crystallization;
[0029]Step 3: Press the evaporation tank with a negative pressure of 0.65 MPa, and the temperature is set to 70 ° C until the chloride concentration is unch...
Example Embodiment
[0033]Example 2:
[0034]The surface sludge of the metal article adopted in this example is ferrous recovery process, including the following steps:
[0035]Step 1: Collect the surface sludge of the metal article, and the mixture of sludge and waste acid after pickling and pickling after pickling.
[0036]Step 2: The mixture of the sludge and the waste acid liquid is accessed into the evaporative tank, and the evaporation tank is 0.35 MPa, the temperature is set to 50 ° C, the rotational speed is set to 45R / min, when the chloride concentration is unchanged The evaporation tank is 0.5 MPa, the temperature is increased to 60 ° C, and the rotational speed is set to 65R / min until the chloride concentration is unchanged, the evaporation tank is pressed, and the internal chloride is naturally cooled, and there is appeared A small amount of crystallization;
[0037]Step 3: The evapozzo tank is 0.65 MPa, and the temperature is set to 75 ° C until the chloride concentration is unchanged, and the eva...
Example Embodiment
[0041]Example 3:
[0042]The surface sludge of the metal article adopted in this example is ferrous recovery process, including the following steps:
[0043]Step 1: Collect the surface sludge of the metal article, and the mixture of sludge and waste acid after pickling and pickling after pickling.
[0044]Step 2: Access the mixture of the sludge and waste acid to the evaporative tank, 0.35 MPa of the evaporation tank, the temperature is set to 40-50 ° C, the rotational speed is set to 45R / min, when the ferride concentration is not After the change, the evaporation tank was 0.5 MPa, the temperature was increased to 55 ° C, and the rotational speed was set to 65 r / min until the chloride concentration was unchanged, and the evaporation tank was pressed, and the internal chloride was naturally cooled. There is a small amount of crystallization;
[0045]Step 3: Press the evaporation tank with a negative pressure of 0.65 MPa, and the temperature is set to 70 ° C until the chloride concentration i...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap