A low thermal expansion coefficient and glass fiber technology, which is applied in the field of glass fiber, can solve the problems of difficult production, mechanical properties such as elastic modulus cannot meet the requirements at the same time, and the expansion coefficient of glass fiber is not low enough, so as to achieve the effect of low crystallization rate

Active Publication Date: 2022-04-05
TAISHAN FIBERGLASS INC
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to make up for the deficiencies of the existing technology and solve the problems in the prior art that the expansion coefficient of glass fiber is not low enough, the production difficulty is large, and the mechanical properties such as elastic modulus cannot meet the requirements at the same time, the present invention provides a glass fiber with a low thermal expansion coefficient

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of low thermal expansion coefficient glass fiber
  • A kind of low thermal expansion coefficient glass fiber
  • A kind of low thermal expansion coefficient glass fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0043] The technical solutions in the embodiments of the present invention will be clearly and completely described below, and the described embodiments are only part of the embodiments of the present invention, not all of the embodiments. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0044] The production technology of glass fiber with low coefficient of thermal expansion comprises the following steps:

[0045] (1) Calculate the quality of each raw material required according to the implementation formula, mix and homogenize each raw material according to the formula requirements, and transport the batch material that meets the requirements of the particle size distribution to the kiln head silo, and then use the feeder to feed the compound at a constant speed. The material is put into the all-electric melting f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
crystallization temperatureaaaaaaaaaa
elastic modulusaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to view more

Abstract

The invention discloses a glass fiber with low thermal expansion coefficient, which belongs to the technical field of glass fiber. The glass fibers of the present invention consist of the following components: SiO 2 55.0~63.0%, Al 2 o 3 17.5~25.0%, MgO 9.0~16.5%, B 2 o 3 2.0~9.0%, ZnO 0.1~4.5%, TiO 2 0.1~4.0%, ZrO 2 0.1~3.0%,H f o 2 0.1~2.0%, Li 2 O 0.1~2.0%; of which TiO 2 , ZrO 2 、H f o 2 The sum of the contents is 1.0-5.0%. The low expansion coefficient glass fiber of the present invention does not add CaO, K 2 O, Na 2 O component, add B at the same time 2 o 3 , ZnO, TiO 2 , ZrO 2 、H f o 2 And optimizing the ratio of each element significantly reduces the expansion coefficient of the glass fiber of the present invention; the expansion coefficient of the glass fiber of the present invention is as low as 2.77×10 ‑6 / °C. While ensuring a low expansion coefficient, the glass fiber of the present invention has an elastic modulus as high as 93GPa or more, and is suitable for the requirements of high-precision components.

Description

technical field [0001] The invention relates to the technical field of glass fibers, in particular to a glass fiber with a low thermal expansion coefficient. Background technique [0002] The application of glass fiber has more and more extensive prospects, but due to the high thermal expansion coefficient of most glass series at present, the demand in such as electronic printed circuit board (PCB) and high-precision parts of the automotive industry is limited. The coefficient of thermal expansion is an important thermal property of glass fiber, which largely depends on the chemical composition of glass fiber. [0003] In the common glass fiber series, the expansion coefficient of S series glass is about 4.0×10 -6 / ℃, D glass expansion coefficient is about 3.5×10 -6 / °C. S series glass and D glass have large expansion coefficients, which cannot meet the requirements of high-precision components. [0004] The expansion coefficient of T glass is low, but SiO in T glass 2 ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C13/00C03B37/022
CPCC03C13/00C03B37/022C03C3/093C03B37/00C03C2213/00
Inventor 唐志尧李永艳
Owner TAISHAN FIBERGLASS INC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap