Glue for sand sculpture as well as preparation and use method thereof

A technology of sand sculpture and glue, which is applied in the field of glue for sand sculpture, can solve problems such as difficult mixing of sand particles, uneven density of sand sculpture, difficult to fine sculpture, etc., and achieve the effect of low cost, not easy to weather, and not easy to crack

Active Publication Date: 2021-04-16
SHANGHAI INST OF TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the non-toxic adhesive is in a solidified state, and it is not easy to mix evenly with sand grains, and it is not easy to be plasticized, so it is difficult to carry out fine sculpture; moreover, the non-toxic adhesive has good performance in preventing water seepage, so a small amount of water should be sprayed during the sand sculpture process. To set the shape, because the non-toxic adhesive prevents water seepage, water is difficult to penetrate, making the internal density of the sand sculpture uneven, the sand particles in different parts are easy to slide, and it is difficult to shape, so it is not suitable for the production of sand sculptures

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A kind of glue for sand sculpture, its preparation and use method are as follows:

[0034] (1) Prepare the glue mixed with sodium carbonate, refined konjac flour and water, the mass ratio of sodium carbonate, refined konjac flour and water is 1:5:100.

[0035] (2) Stir the sand sculpture glue and sand obtained in step (1) evenly, and the mass ratio of sand sculpture glue to sand is 1:20.

[0036] It can be cured at room temperature, and sand sculptures with good shape can be obtained, and no cracks will appear in the outdoor environment for 1 month.

Embodiment 2

[0038] A kind of glue for sand sculpture, its preparation and use method are as follows:

[0039] (1) Prepare the glue that sodium carbonate, refined konjac flour and water mix, and the mass ratio of sodium carbonate, refined konjac flour and water is 1:10:100.

[0040] (2) Stir the sand sculpture glue and sand obtained in step (1) evenly, and the mass ratio of sand sculpture glue to sand is 1:20.

[0041] It can be cured at room temperature, and sand sculptures with good shape can be obtained, and no cracks will appear in the outdoor environment for 1 month.

Embodiment 3

[0043] A kind of glue for sand sculpture, its preparation and use method are as follows:

[0044] (1) Prepare the glue that sodium carbonate, refined konjac flour and water mix, and the mass ratio of sodium carbonate, refined konjac flour and water is 2:5:100.

[0045] (2) Stir the sand sculpture glue and sand obtained in step (1) evenly, and the mass ratio of sand sculpture glue to sand is 1:20.

[0046] It can be cured at room temperature, and sand sculptures with good shape can be obtained, and no cracks will appear in the outdoor environment for 1 month.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a glue for sand sculpture as well as a preparation method and a use method thereof. The glue for sand sculpture comprises the following components in parts by weight: 1-2 parts of sodium carbonate, 5-10 parts of konjaku flour and 100-200 parts of water. Compared with the prior art, the glue has the advantages of being safe to use, non-toxic, convenient to clean, capable of being cured at normal temperature, and good in adhesive force to sand, and does not pollute an adhered object.

Description

technical field [0001] The invention relates to the technical field of sand sculpture production, in particular to a glue for sand sculpture and its preparation and use method. Background technique [0002] Sand sculpture is a kind of sculpture made of sand. It is mainly made of sand and water. It is molded by stacking, engraving, carving, digging, etc., and then reinforced by spraying specific glue on the surface. Due to the poor adhesion of sand, it is easy to disperse and it is not easy to make complex shapes. When making sand sculptures, it is often necessary to add glue for bonding. The main characteristics of sand sculptures are large size, heavy weight, easy to disperse, and difficult to store and move. After the work is completed, it is reinforced by spraying specific glue on the surface. In the production of existing sand sculpture artworks, after the work is completed, it is reinforced by spraying special glue on the surface, or adding a binder during the producti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J105/02C09J11/02B44C3/06
Inventor 王根礼
Owner SHANGHAI INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com